ATI Wah Chang Zircadyne® Alloy Zr 705

Category Metal , Nonferrous Metal , Zirconium Alloy
Manufacturer ATI Wah Chang
Trade Name Zircadyne®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ATI Wah Chang Zircadyne® Alloy Zr 705.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zircadyne 705 is zirconium alloyed with niobium to increase its strength and improve its formability. Alloy exhibits good ductility even at cryogenic temperatures and strength comparable with other common engineering alloys.Information provided by ATI Wah Chang
Physical Properties Metric English Comments
Density 6.64 g/cc
0.240 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 281 MPa

@Temperature 371 °C
 40800 psi

@Temperature 700 °F
300 MPa

@Temperature 316 °C
 43500 psi

@Temperature 601 °F
326 MPa

@Temperature 260 °C
 47300 psi

@Temperature 500 °F
370 MPa

@Temperature 204 °C
 53600 psi

@Temperature 399 °F
389 MPa

@Temperature 149 °C
 56400 psi

@Temperature 300 °F
495 MPa

@Temperature 93.0 °C
 71800 psi

@Temperature 199 °F
615 MPa

@Temperature 23.0 °C
 89200 psi

@Temperature 73.4 °F
Tensile Strength, Yield 173 MPa

@Temperature 371 °C
 25100 psi

@Temperature 700 °F
190 MPa

@Temperature 316 °C
 27600 psi

@Temperature 601 °F
196 MPa

@Temperature 260 °C
 28400 psi

@Temperature 500 °F
262 MPa

@Temperature 204 °C
 38000 psi

@Temperature 399 °F
272 MPa

@Temperature 149 °C
 39500 psi

@Temperature 300 °F
391 MPa

@Temperature 93.0 °C
 56700 psi

@Temperature 199 °F
506 MPa

@Temperature 23.0 °C
 73400 psi

@Temperature 73.4 °F
Elongation at Break 18.8 %

@Temperature 23.0 °C
 18.8 %

@Temperature 73.4 °F
27.8 %

@Temperature 371 °C
 27.8 %

@Temperature 700 °F
28.9 %

@Temperature 260 °C
 28.9 %

@Temperature 500 °F
29 %

@Temperature 316 °C
 29 %

@Temperature 601 °F
30.5 %

@Temperature 93.0 °C
 30.5 %

@Temperature 199 °F
31.7 %

@Temperature 149 °C
 31.7 %

@Temperature 300 °F
33 %

@Temperature 204 °C
 33 %

@Temperature 399 °F
Modulus of Elasticity 74.6 GPa

@Temperature 371 °C
 10800 ksi

@Temperature 700 °F
77.8 GPa

@Temperature 316 °C
 11300 ksi

@Temperature 601 °F
81.0 GPa

@Temperature 260 °C
 11700 ksi

@Temperature 500 °F
84.2 GPa

@Temperature 204 °C
 12200 ksi

@Temperature 399 °F
87.3 GPa

@Temperature 149 °C
 12700 ksi

@Temperature 300 °F
90.5 GPa

@Temperature 93.0 °C
 13100 ksi

@Temperature 199 °F
93.8 GPa

@Temperature 38.0 °C
 13600 ksi

@Temperature 100 °F
94.7 GPa

@Temperature 23.0 °C
 13700 ksi

@Temperature 73.4 °F
Poissons Ratio 0.33
0.33
Fatigue Strength 55.2 MPa
8000 psi
notched
290 MPa

@# of Cycles 1.00e+7
42000 psi

@# of Cycles 1.00e+7
Unnotched
Shear Modulus 34.5 GPa

@Temperature 23.0 °C
 5000 ksi

@Temperature 73.4 °F
Thermal Properties Metric English Comments
CTE, linear 4.86 µm/m-°C

@Temperature 149 °C
 2.70 µin/in-°F

@Temperature 300 °F
5.58 µm/m-°C

@Temperature 260 °C
 3.10 µin/in-°F

@Temperature 500 °F
5.94 µm/m-°C

@Temperature 371 °C
 3.30 µin/in-°F

@Temperature 700 °F
Melting Point 1840 °C
3340 °F
Component Elements Properties Metric English Comments
Fe + Cr <= 0.20 %
<= 0.20 %
Hafnium, Hf <= 4.5 %
<= 4.5 %
Niobium, Nb (Columbium, Cb) 2.0 - 3.0 %
2.0 - 3.0 %
Zirconium, Zr >= 91 %
>= 91 %