ATI Wah Chang TI-3Al-2.5V
| Category | Metal , Nonferrous Metal , Titanium Alloy |
| Manufacturer | ATI Wah Chang |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ATI Wah Chang TI-3Al-2.5V.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ti-3Al-2.5V has proved to be a sufficiently malleable material for tube manufacture. It can be cold worked by standard tube making processes, is weldable and can be strength-ended by cold working and subsequent heat treatment to a wide range of strengths and ductilities.Information provided by ATI Wah Chang
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.48 g/cc | 0.162 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 490 MPa @Temperature 249 °C |
71000 psi @Temperature 480 °F |
Annealed |
| 565 MPa @Temperature 149 °C |
82000 psi @Temperature 300 °F |
Annealed | |
| 621 MPa @Temperature 23.0 °C |
90000 psi @Temperature 73.4 °F |
||
| 717 MPa @Temperature 249 °C |
104000 psi @Temperature 480 °F |
Cold Worked | |
| 786 MPa @Temperature 149 °C |
114000 psi @Temperature 300 °F |
Cold Worked | |
| 896 MPa @Temperature 23.0 °C |
130000 psi @Temperature 73.4 °F |
||
| Tensile Strength, Yield | 379 MPa @Temperature 249 °C |
55000 psi @Temperature 480 °F |
Annealed |
| 455 MPa @Temperature 149 °C |
66000 psi @Temperature 300 °F |
Annealed | |
| 496 MPa @Temperature 23.0 °C |
72000 psi @Temperature 73.4 °F |
||
| 586 MPa @Temperature 249 °C |
85000 psi @Temperature 480 °F |
Cold Worked | |
| 641 MPa @Temperature 149 °C |
93000 psi @Temperature 300 °F |
Cold Worked | |
| 758 MPa @Temperature 23.0 °C |
110000 psi @Temperature 73.4 °F |
||
| Elongation at Break | 15 % @Temperature 250 °C |
15 % @Temperature 482 °F |
in 50 mm, Cold Worked |
| 17 % @Temperature 150 °C |
17 % @Temperature 302 °F |
in 50 mm, Cold Worked | |
| 19 % @Temperature 23.0 °C |
19 % @Temperature 73.4 °F |
||
| 23 % @Temperature 250 °C |
23 % @Temperature 482 °F |
in 50 mm, Annealed | |
| 25 % @Temperature 150 °C |
25 % @Temperature 302 °F |
in 50 mm, Annealed | |
| 29 % @Temperature 23.0 °C |
29 % @Temperature 73.4 °F |
||
| Modulus of Elasticity | 96.53 GPa @Temperature 788 °C |
14000 ksi @Temperature 1450 °F |
|
| 103.4 GPa @Temperature 23.0 °C |
15000 ksi @Temperature 73.4 °F |
||
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 42.7 - 44.8 GPa | 6200 - 6500 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 9.54 µm/m-°C @Temperature 20.0 °C |
5.30 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 1700 °C | 3090 °F | |
| Beta Transus | 935 °C | 1720 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 3.0 % | 3.0 % | |
| Titanium, Ti | 94.5 % | 94.5 % | |
| Vanadium, V | 2.5 % | 2.5 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000126 ohm-cm | 0.000126 ohm-cm |
Users viewing this material also viewed the following:
- Nye Lubricants PG-3S Grease
- Shuman SP810 Black Polystyrene High Impact
- Samsung Cheil Industries Starex® SD-0150GP High Impact Grade ABS
- Sylvin Technologies 6065 LT GL 85 PVC Wire/Cable Compound
- Borealis FG5199 Linear Low Density Polyethylene
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 60 PHR N220 (ISAF) Filler
- Eurotec® Tecomid® NA40 GR25 NL HS PA6.6, 25% glass fiber reinforced, heat stabilized, natural
- Radici Radilon® A 42 (cond.) Nylon 66
- LATI Latilub 75/4-05T G/30-V0 PBT, 30% Glass Fiber Reinforced, PTFE Filled, Flame Retardant
- Latrobe Lescalloy® HY-TUF VAC-ARC High Strength Alloy Steel
Copyright © lookpolymers.com All Rights Reserved