- ATI Allvac® Nickelvac® X-750 Nickel Superalloy, Heat Treatment: 982°C (1800°F) + Age
ATI Allvac® Nickelvac® X-750 Nickel Superalloy, Heat Treatment: 982°C (1800°F) + Age
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | ATI Allvac |
| Trade Name | Nickelvac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ATI Allvac® Nickelvac® X-750 Nickel Superalloy, Heat Treatment: 982°C (1800°F) + Age.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Allvac.Applications: Turbine, engine components. Blades, vanes, fasteners, springs, bellows. Extrusion dies, nuclear, heat treating, forming tools.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.30 g/cc | 0.300 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 326 | 326 | Estimated from Rockwell C value for Brinell test with 3000 kg load/10 mm diameter ball |
| Hardness, Knoop | 354 | 354 | Estimated from Rockwell C value. |
| Hardness, Rockwell C | 35 | 35 | |
| Hardness, Vickers | 341 | 341 | Estimated from Rockwell C value. |
| Tensile Strength, Ultimate | 1207 MPa | 175100 psi | |
| Tensile Strength, Yield | 793 MPa @Strain 0.200 % |
115000 psi @Strain 0.200 % |
|
| Elongation at Break | 20 % | 20 % | |
| Reduction of Area | 20 % | 20 % |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 0.70 % | 0.70 % | |
| Carbon, C | 0.040 % | 0.040 % | |
| Chromium, Cr | 15.5 % | 15.5 % | |
| Iron, Fe | 7.0 % | 7.0 % | |
| Nickel, Ni | >= 70 % | >= 70 % | as balance |
| Niobium, Nb (Columbium, Cb) | 0.95 % | 0.95 % | |
| Titanium, Ti | 2.5 % | 2.5 % |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 51 HF UVT General Purpose Acrylic Resin
- ND Industries StudGrade® 146 Permanent StudGrade HD Threadlocker
- Hong Kun Group Zinc Borate Flame Retardant
- Spartech Royalite R722 PVC Alloy Aircraft Grade Sheet
- SABIC Innovative Plastics LNP Stat-kon NX03602 PC+ABS (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP RF0059 PA 66
- SPHERE ONE EXTENDOSPHERESâ„¢ PM 6550 Hollow Plastic Spheres
- SABIC Innovative Plastics LNP THERMOTUF VF1001S Super Tough Nylon
- Hexcel® HexWeb® CR-PAA™ 1/4-5052-0.001 Phosphoric Acid Anodized Aluminum Honeycomb
Copyright © lookpolymers.com All Rights Reserved