ATI Allegheny Ludlum Altemp® 263 Nickel-Based alloy
| Category | Metal , Nonferrous Metal , Nickel Alloy |
| Manufacturer | ATI Allegheny Ludlum |
| Trade Name | Altemp® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ATI Allegheny Ludlum Altemp® 263 Nickel-Based alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: high strength up to 1500°F, oxidation resistance up to 2000°FInformation provided by Allegheny Ludlum
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.36 g/cc | 0.302 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell B | 90 | 90 | Solution Annealed, 21°C |
| Hardness, Rockwell C | 28 | 28 | Age Hardened per AMS 5872D, 21°C |
| Tensile Strength, Ultimate | 655 MPa | 95000 psi | |
| 827 MPa | 120000 psi | Solution Annealed | |
| 1034 MPa | 150000 psi | Age Hardened per AMS 5872D, 21°C | |
| Tensile Strength, Yield | 414 MPa | 60000 psi | Solution Annealed |
| 552 MPa | 80100 psi | ||
| 621 MPa | 90100 psi | Age Hardened per AMS 5872D, 21°C | |
| Elongation at Break | 17 % | 17 % | Age Hardened per AMS 5872D, 779°C |
| 35 % | 35 % | Age Hardened per AMS 5872D, 21°C | |
| 50 % | 50 % | Solution Annealed | |
| Creep Strength | 116 MPa @Temperature 779.4 °C, Time 180000 sec |
16800 psi @Temperature 1435 °F, Time 50.0 hour |
|
| Modulus of Elasticity | 220 GPa | 31900 ksi |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 0.30 - 0.60 % | 0.30 - 0.60 % | |
| Carbon, C | 0.040 - 0.080 % | 0.040 - 0.080 % | |
| Chromium, Cr | 19 - 21 % | 19 - 21 % | |
| Cobalt, Co | 19 - 21 % | 19 - 21 % | |
| Copper, Cu | <= 0.20 % | <= 0.20 % | |
| Iron, Fe | <= 0.70 % | <= 0.70 % | As Remainder |
| Manganese, Mn | <= 0.60 % | <= 0.60 % | |
| Molybdenum, Mo | 5.6 - 6.1 % | 5.6 - 6.1 % | |
| Nickel, Ni | >= 46.898 % | >= 46.898 % | |
| Phosphorous, P | <= 0.015 % | <= 0.015 % | |
| Silicon, Si | <= 0.40 % | <= 0.40 % | |
| Sulfur, S | <= 0.0070 % | <= 0.0070 % | |
| Titanium, Ti | 1.9 - 2.4 % | 1.9 - 2.4 % |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 1200H-25 Fiberglass Reinforced Thermoset SMC
- Polimeri Europa EDISTIR N1461 Polystyrene (discontinued **)
- KKPC KOSYN SOL 5001 Solution Styrene Butadiene Rubber (S-SBR)
- LyondellBasell Hifaxâ„¢ EP2015/60 Thermoplastic Polyolefin Elastomer
- Sharadaa Ceramics REFCAST LC60ABR Low Cement Castables
- SABIC Innovative Plastics NORYL LS6010 PPE+HIPS (Europe-Africa-Middle East)
- Lubrizol Estane® S392A Thermoplastic Polyurethane
- TIMET TIMETAL® Code 12 Titanium Alloy (ASTM Grade 12)
- Arkema Group Lucalor® RY 123 CPVC, Plumbing Grade
- Solvay Specialty Polymers AvaSpire® AV-630 Polyaryletherketone (PAEK) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved