Nanocyl NANOCYL™ NC2100 Double-Wall Isolated and Bundled Carbon Nanotubes - Research Grade

Category	Carbon
Manufacturer	Nanocyl
Trade Name	NANOCYL™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Nanocyl NANOCYL™ NC2100 Double-Wall Isolated and Bundled Carbon Nanotubes - Research Grade.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

NANOCYL™ NC2000 series double-wall carbon nanotubes are produced via the catalytic carbon vapor deposition (CCVD) process. Nanotubes which exit the reactor are then purified to greater than 90% carbon to produce the 2100 grade. This grade is then functionalized with COOH to produce the 2101 grade. These products are available in 1 g to 1 kg order quantities.A primary interest is in applications requiring high field emission characteristics, transparency or high surface area.

Physical Properties	Metric	English	Comments
Specific Gravity	1.30 - 2.00 g/cc	1.30 - 2.00 g/cc
Specific Surface Area	>= 500 m²/g	>= 500 m²/g	BET

Mechanical Properties	Metric	English
Tensile Strength	10000 - 60000 MPa	1.45e+6 - 8.70e+6 psi
Elongation at Break	10 %	10 %
Tensile Modulus	1000 GPa	145000 ksi

Thermal Properties	Metric	English	Comments
Thermal Conductivity	>= 3000 W/m-K	>= 20800 BTU-in/hr-ft²-°F

Component Elements Properties	Metric	English	Comments
Carbon, C	>= 90 %	>= 90 %	TGA

Electrical Properties	Metric	English	Comments
Volume Resistivity	0.00001 - 0.0001 ohm-cm	0.00001 - 0.0001 ohm-cm

Descriptive Properties	Value	Comments
Average Diameter	3.5 nanometers	HRTEM
Average Length	1 to 10 microns	TEM/SEM
-COOH Functionalization	<1%	XPS
Metal Oxide	<10%	TGA