Iran Petrochemical (PCC) 2102TX00 Low Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Iran Petrochemical Commercial Co. (PCC) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Iran Petrochemical (PCC) 2102TX00 Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LDPE 2102TX00 GP filmIt is used in wide range of widths and thicknesses e.g. for punches, bags, liners and lamination film.Information provided by Iran Petrochemical Commercial Co.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ISO 1183 |
| Melt Flow | 1.9 g/10 min | 1.9 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 13.0 MPa | 1890 psi | ISO R527-1 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ISO R527-1 |
| Film Elongation at Break, MD | >= 150 % | >= 150 % | ISO R527-1 |
| Film Elongation at Break, TD | >= 500 % | >= 500 % | ISO R527-1 |
| Modulus of Elasticity | 0.190 GPa | 27.6 ksi | MD; ISO R527-1 |
| 0.200 GPa | 29.0 ksi | TD; ISO R527-1 | |
| Tensile Impact | 260 J/cm | 487 ft-lb/in | ASTM D4272 |
| Coefficient of Friction | 1.0 | 1.0 | ASTM D1894 |
| Tear Strength | 25.0 kN/m | 143 pli | TD; ISO 6383-2 |
| 60.0 kN/m | 342 pli | MD; ISO 6383-2 | |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ISO R527-1 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 11 % | 11 % | ASTM D1003A |
| Gloss | 50 % | 50 % | ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clarity, mV | 29 | Sabtec |
Users viewing this material also viewed the following:
- Radici Radilon® ARV300 (dry) Nylon 66
- Mitsubishi Iupilon® S2000UR 9.5 MFI, UV Stabilized Polycarbonate With Release
- Taiwan Sheen Soon Sheenthane® AS-632H TPU for PU Adhesive
- Shin-Etsu Silicones KE-348 Silicone, RTV
- Total PPH 4060 Polypropylene, Homopolymer
- Goodfellow Iron 55/Nickel 45 Alloy
- Plenco 7476 Phenolic, Granular, Transfer Molded
- Hippe PA 6 Nylon 6
- LyondellBasell DEXFLEX® 711 TPO
- A. Schulman POLYFLAM™ FCB 1236-8555 General Purpose Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved