PSM Industries Ferro-TiC® C Medium Alloy Tool Steel

Category	Ceramic , Carbide , Metal , Ferrous Metal , Alloy Steel , Medium Alloy Steel , Tool Steel
Manufacturer	PSM Industries
Trade Name	Ferro-TiC®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PSM Industries Ferro-TiC® C Medium Alloy Tool Steel.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ferro-TiC® Steel alloy bonded titanium carbide (TiC) materials are made by advanced powder metallurgy technologies. Unlike tungsten carbide, Ferro-TiC® is bonded by hardenable alloy matrices.Excellent vibration dampening in the annealed condition, excellent cryogenic properties. Replaces A-2 tool steel. Highly Magnetic.Ferro-TiC® Unique CharacteristicsProvides the lightweight, size, stability, and hardnessVirtually porosity free - significantly better than the A1 ASTM B-276-79 StandardLow specific mass. Ferro-Tic® is 10-20% lighter than its steel counterpart and about 50% lighter than tungsten carbide10 times the wear resistance of tool steelsEconomical fabrication (conventionally machinable in the annealed stage by milling and turning, conventionally heat treatable to achieve high hardness)50-90% less linear size change in heat treat than tool steelsInformation Provided by Ferro-TiC®, a division of PSM Industries

Physical Properties	Metric	English	Comments
Density	6.60 g/cc	0.238 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell C	44	44	Annealed
	70	70	Hardened
Flexural Strength	1490 MPa	216000 psi	Transverse Rupture
Compressive Strength	3590 MPa	520000 psi
Charpy Impact Unnotched	5.653 J/cm²	26.92 ft-lb/in²

Thermal Properties	Metric	English	Comments
CTE, linear	3.53 µm/m-°C @Temperature 21.1 - 191 °C	1.96 µin/in-°F @Temperature 70.0 - 375 °F
Maximum Service Temperature, Air	191 °C	375 °F

Descriptive Properties	Value	Comments
Carbide (Vol. %)	45
Linear Size Change Thru Heat Treat %	0.048
Thermal Shock (No. Cycles)	5