PTS 30GFR-BK PBT- Flame Retardant, 30% Glass Filled PBT Black Resin

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer Polymer Technology & Services, LLC (PTS)
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PTS 30GFR-BK PBT- Flame Retardant, 30% Glass Filled PBT Black Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 117 MPa

@Thickness 3.17 mm
 17000 psi

@Thickness 0.125 in
 ASTM D638
Elongation at Break 3.0 %

@Thickness 3.17 mm
 3.0 %

@Thickness 0.125 in
 ASTM D638
Flexural Strength 172 MPa

@Thickness 3.17 mm
 25000 psi

@Thickness 0.125 in
 ASTM D790
Flexural Modulus 6.21 GPa

@Thickness 3.17 mm
 900 ksi

@Thickness 0.125 in
 ASTM D790
Izod Impact, Notched 0.587 J/cm
1.10 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 216 °C
421 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 202 °C
395 °F
ASTM D648
UL RTI, Electrical 75.0 °C
167 °F
UL RTI, Mechanical with Impact 75.0 °C
167 °F
UL RTI, Mechanical without Impact 75.0 °C
167 °F
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
5VA

@Thickness 2.50 mm
 5VA

@Thickness 0.0984 in