A. Schulman ComAlloy Hiloy® 422 Heavy Mineral Reinforced, PBT Alloy
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Mineral Filled |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 422 Heavy Mineral Reinforced, PBT Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.40% Heavy Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.81 g/cc | 0.0654 lb/in³ | |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Ultimate | 49.0 MPa | 7110 psi | ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| Flexural Modulus | 4.40 GPa | 638 ksi | ASTM D790 |
| Izod Impact, Notched | 0.210 J/cm | 0.393 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.74 J/cm | 21.99 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 210 - 225 °C | 410 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 235 - 249 °C | 455 - 480 °F |
Users viewing this material also viewed the following:
- JPJ Technologies 6100M HDPE Extrusion
- Lehmann & Voss LUVOCOM® 1/CF/10/GF/20/BK Polyamide 66, with carbon fiber and glass fiber, heat stabilized
- Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes
- UBE UBEPOL BR360L Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- Zeon Chemicals Nipol® 1052 Nitrile Elastomer
- A. Schulman POLYFORT™ FPP 4529 Mineral Filled Copolymer Polypropylene
- ExxonMobil Vistamaxx™ 6202FL Propylene-based Elastomer - Performance Film
- Eagle Brass 304 Austenitic Stainless Steel, Full Hardened
- Aremco Quartz-Coat™ 850 High Temperature Specialty Coatings Inorganic, Glass-Ceramic Filled
Copyright © lookpolymers.com All Rights Reserved