3M AC-250 B-1/6 Aerospace Sealant

Category	Polymer , Thermoset
Manufacturer	3M
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M AC-250 B-1/6 Aerospace Sealant.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M Aerospace Sealant AC-250 B-1/6 is a two-part, polysulfide, quick repair sealant for integral fuel tank and fuselage sealing applications. The mixed compound is a thixotropic paste and can be readily applied with a spatula or extrusion gun. It will cure to a fuel-resistant rubber at temperatures above -6.7°C. It exhibits excellent tooling properties.Information provided by 3M

Physical Properties	Metric	English	Comments
Density	1.62 g/cc	0.0585 lb/in³	AMS-S83318
Volatiles	5.0 %	5.0 %
Brookfield Viscosity	900000 - 1.30e+6 cP	900000 - 1.30e+6 cP	Base, RVF #6 sp @ 2 rpm

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	40	40	Hydrolytic Stability; AMS-S83318
	55	55	AMS-S83318
Tensile Strength at Break	1.38 MPa @Temperature 60.0 °C, Time 1.21e+6 sec	200 psi @Temperature 140 °F, Time 336 hour	JRF; AMS-S83318
	3.38 MPa @Temperature 121 °C, Time 605000 sec	490 psi @Temperature 250 °F, Time 168 hour	JRF; AMS-S83318
	2.76 MPa @Time 1.21e+6 sec	400 psi @Time 336 hour	Standard Cure; AMS-S83318
Elongation at Break	280 % @Temperature 121 °C, Time 605000 sec	280 % @Temperature 250 °F, Time 168 hour	JRF; AMS-S83318
	380 % @Temperature 60.0 °C, Time 1.21e+6 sec	380 % @Temperature 140 °F, Time 336 hour	JRF; AMS-S83318
	340 % @Time 1.21e+6 sec	340 % @Time 336 hour	Standard Cure; AMS-S83318
Peel Strength	9.12 kN/m @Temperature 60.0 °C, Time 605000 sec	52.0 pli @Temperature 140 °F, Time 168 hour	JRF, Alclad; AMS-S83318
	9.29 kN/m @Temperature 60.0 °C, Time 605000 sec	53.0 pli @Temperature 140 °F, Time 168 hour	JRF/SW, MIL-C-27725; AMS-S83318
	9.29 kN/m @Temperature 60.0 °C, Time 605000 sec	53.0 pli @Temperature 140 °F, Time 168 hour	JRF/SW, Alodine; AMS-S83318
	9.64 kN/m @Temperature 60.0 °C, Time 605000 sec	55.0 pli @Temperature 140 °F, Time 168 hour	JRF, MIL-C-27725; AMS-S83318
	9.64 kN/m @Temperature 60.0 °C, Time 605000 sec	55.0 pli @Temperature 140 °F, Time 168 hour	JRF/SW, Stainless Steel; AMS-S83318
	10.2 kN/m @Temperature 60.0 °C, Time 605000 sec	58.0 pli @Temperature 140 °F, Time 168 hour	JRF/SW, Alclad; AMS-S83318
	10.5 kN/m @Temperature 60.0 °C, Time 605000 sec	60.0 pli @Temperature 140 °F, Time 168 hour	JRF, Stainless Steel; AMS-S83318
	10.5 kN/m @Temperature 60.0 °C, Time 605000 sec	60.0 pli @Temperature 140 °F, Time 168 hour	JRF/SW, Titanium; AMS-S83318
	11.0 kN/m @Temperature 60.0 °C, Time 605000 sec	63.0 pli @Temperature 140 °F, Time 168 hour	JRF, Alodine; AMS-S83318
	11.4 kN/m @Temperature 60.0 °C, Time 605000 sec	65.0 pli @Temperature 140 °F, Time 168 hour	JRF, Titanium; AMS-S83318

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	121 °C	250 °F	AMS-S83318
Minimum Service Temperature, Air	-54.0 °C	-65.2 °F	AMS-S83318

Processing Properties	Metric	English	Comments
Cure Time	60.0 min @Temperature 25.0 °C	1.00 hour @Temperature 77.0 °F	Tack-Free Time
	120 min @Temperature 4.40 °C	2.00 hour @Temperature 39.9 °F	Tack-Free Time
	300 min @Temperature -6.70 °C	5.00 hour @Temperature 19.9 °F	Tack-Free Time
	480 min @Temperature 25.0 °C	8.00 hour @Temperature 77.0 °F
	600 min @Temperature 4.40 °C	10.0 hour @Temperature 39.9 °F
	840 min @Temperature -6.70 °C	14.0 hour @Temperature 19.9 °F
Shelf Life	6.00 Month @Temperature <=26.7 °C	6.00 Month @Temperature <=80.1 °F

Descriptive Properties	Value	Comments
Appearance	Dark Brown	Accelerator
	Gray
	White	Base