Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 15.0 min | 0.250 hour | Skin over time |
P & P Technology MS-N Nickel Graphite Conductive Adhesive P & P Technology conductive nickel/graphite adhesive is a one part electrically conductive room temperature curing elastomer. It is supplied as a readily extrudable paste that cures rapidly when exp.. |
|||
Cure Time | 15.0 min @Temperature 113 °C |
0.250 hour @Temperature 235 °F |
|
Parker Chomerics CHO-BOND® 584-29 SYRINGE-PAK™ Silver Filled Conductive Epoxy and Hardener Description: Chomerics CHO-BOND 584-29 is a two-component, highly conductive adhesive system that combines the strong adhesive characteristics of epoxy with the superior conductivity of pure silver... |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 518581R018 0.018" (0.457 mm) Uncured Silicone Rubber with Fiberglass Substrate
(discontinued **)&l Design/Construction:Side 1: Uncured Silicone RubberSide 2: Uncured Silicone RubberAppearance: Red silicone gum on fiberglass clothThis data Represents typical values for the production material. The.. |
|||
Cure Time | 15.0 min @Temperature 166 °C |
0.250 hour @Temperature 330 °F |
|
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 330ºF Cure Temperature MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Cure Time | 15.0 min @Temperature 160 °C |
0.250 hour @Temperature 320 °F |
|
TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 2.0 PHR Di-Cup 40C Peroxide Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and m.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 23234R025 0.025" (0.635 mm) Semi-Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Semi-Cured Silicone Rubber This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications... |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 49581B010 0.0105" (0.267 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Uncured Silicone RubberSide 2: Uncured Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in place .. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 51586R035 0.035" (0.889 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSide 2: Uncured Silicone RubberAppearance: Red silicone gum and rubber on fiberglass clothThis data Represents typical values for the production mate.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 51601W015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Uncured Silicone RubberSide 2: Uncured Silicone RubberProduct Use: Flexible heater insulationAppearance: White silicone gum on fiberglass with polymer release linersThis .. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 55586XC028 0.0295" Cured/Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSubstrate: Style 162 FiberglassSide 2: Uncured Silicone RubberInterleave: 3 mil PEThis data represents typical values for the production material .. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 99570R010 0.010" Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier Design/Construction:Liner: 0.001" FEP FilmSide 1: Uncured Silicone RubberCarrier: 0.003" PTFE coated FiberglassThis data represents typical values for the production material and should not be us.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon R34066X015 0.015" (0.381 mm) Cured Silicone with Fiberglass Substrate Design/Construction:Side 1: Platinum Cured SiliconeSide 2: Peroxide Catalyzed Silicone Appearance: Gray silicone gum on fiberglass clothThis data Represents typical values for the production materia.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
Arlon R35551X015 0.015" Uncured Silicone Rubber with Woven Fabric Substrate Design/Construction:Interleave: 0.003" PolyethyleneSide 1: Uncured Silicone RubberSubstrate: Primed 3M Nextel 312 Woven Fabric AF-10, HCSide 2: Uncured Silicone RubberThis data represents typica.. |
|||
Cure Time | 15.0 min @Pressure 0.0689 - 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 10.0 - 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
Arlon Thermabond® 48991A010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate Description: Generation IIa Thermabond® NP electrically insulating electronic adhesive. Bonds without primer.Design/Construction: Liner: PolyethyleneSide 1: Uncured Silicone RubberSubstrate: Style .. |
|||
Cure Time | 15.0 min @Temperature 141 °C |
0.250 hour @Temperature 285 °F |
Recommended Cure Cycle |
Arlon Thermabond® T-20 NP (99770W015) 0.015" (0.381 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier Description: 15 mil Primerless Thermabond®. T-20 NP. Thermally conductive, electrically insulating electronic adhesive. Bonds with primer.Design/Construction:Liner: FEPProduct: Uncured Silicone Rub.. |
|||
Cure Time | 15.0 min @Temperature 138 °C |
0.250 hour @Temperature 280 °F |
Recommended Cure Cycle |
Arlon Thermabond®-II 99760N015 0.015" (0.381 mm) Unsupported/Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Unsupported/Uncured RubberAppearance: White/grey gumThis data Represents typical values for the production material. The data should not be used to write, or in place of,.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 41600R025 0.025" Uncured, Unsupported Silicone Rubber on Release Carrier Design/Construction:Interleave: 0.003" PolyethyleneSide 1: Uncured, Unsupported Silicone RubberSubstrate: Holland Cloth CarrierThis data represents typical values for the production material and .. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
|
Arlon 51141R020 Silicone Rubber/Fiberglass Laminate Interleave 1: 3 mil PE; Side 1: uncured silicone rubber; Substrate: 7628 fiberglass; Side 2: uncured silicone rubber; Interleave 2: 3 mil PE |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
|
Arlon 51228R020 Silicone Rubber/Fiberglass Laminate Interleave: 1.5 mil PE; Side 1, layer 2: uncured silicone rubber; Side 1, layer 1: Cured silicone rubber; Substrate: 7628 fiberglass; Side 2: cured silicone rubber |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
|
Arlon 51276R020 Silicone Rubber/Fiberglass Laminate Side 1: cured silicone rubber; Substrate: 7628 fiberglass; Side 2: uncured silicone rubber; Interleave: 3 mil polyethylene |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 51581R020 0.020" Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave: 3 mil PolyethyleneSide 1: Uncured Silicone RubberSubstrate: Prime Coated 7628 FiberglassSide 2: Uncured Silicone RubberThis data represents typical values for the.. |
|||
Cure Time | 15.0 min @Temperature 154 °C |
0.250 hour @Temperature 309 °F |
|
TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Carbon Black, N-220 (ISAF) Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and m.. |
|||
Cure Time | 15.0 min @Temperature 149 °C |
0.250 hour @Temperature 300 °F |
|
TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 30A, Black Sulfur Cure Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and m.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
Arlon 44580R020 0.020" Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave: 2.5 mil PolyethyleneSide 1: Uncured Silicone RubberSubstrate: Style 1165 Fiberglass (Flexible Heater Substrate)This data represents typical values for the producti.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 44686W013 0.013" (0.330 mm) Cured/Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSide 2: Uncured Silicone Rubber UL Recognition: 220°C per UL Card E54153Appearance: White silicone gum on fiberglassThis data represents typical val.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
|
Arlon R37879X034 Silicone Rubber/Fiberglass Laminate Interleave: 3 mil PE; Layer 2: uncured silicone rubber; Layer 1: Cured silicone rubber; Substrate: 162 fiberglass |
|||
Cure Time | 15.0 min @Temperature 160 °C |
0.250 hour @Temperature 320 °F |
|
TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 60A, Black Peroxide Cure Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and m.. |