Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 19.8 min @Temperature 100 °C |
0.330 hour @Temperature 212 °F |
|
Parker Chomerics CHO-FORM® 5518 Robotically Dispensed Gasketing Description: CHO-FORM® 5518 Two-component, thermal cure silicone system with Ag/Cu particle filler. Minimum cure temperature is only 85°C (185°F). Formulated for painted, plated or metalized plas.. |
|||
Cure Time | 19.8 - 30.0 min @Temperature 43.3 °C |
0.330 - 0.500 hour @Temperature 110 °F |
De-mold Time |
Northstar Polymers MPS-F04A Hand-Mixable Flexible Foam This foam formulation is designed to make molded flexible foam parts/sheets/dies/blocks by hand-mixing or by the meter dispensing equipment. The components are stable liquid at room temperature and.. |
|||
Cure Time | 19.8 - 40.2 min @Temperature 43.3 °C |
0.330 - 0.670 hour @Temperature 110 °F |
De-mold Time |
Northstar Polymers MPS-F08A Hand-Mixable Flexible Foam This foam formulation is designed to make molded flexible foam parts/sheets/dies/blocks by hand-mixing or machine casting by the meter dispensing equipment. The components are stable and liquid at .. |
|||
Cure Time | 19.8 min @Temperature 23.0 °C |
0.330 hour @Temperature 73.4 °F |
M10 steel, handling strength |
Permabond LH197 Anaerobic Gasketmaker Permabond® LH197 is an anaerobic material designed for making “formed in situ” gaskets between metal surfaces. It is highly flexible, making it ideal for dissimilar surfaces where differential th.. |
|||
Cure Time | 19.8 - 30.0 min @Temperature 110 °C |
0.330 - 0.500 hour @Temperature 230 °F |
|
Master Bond Supreme 10HTF Fast Curing Toughened One Component Epoxy Adhesive Master Bond Polymer System Supreme 10HTF is a one part, no-mix system featuring a unique combination of properties including high shear and peel strength, exceptionally wide service temperature rang.. |
|||
Cure Time | 19.8 - 30.0 min @Temperature 121 °C |
0.330 - 0.500 hour @Temperature 250 °F |
|
Master Bond Supreme 3HT High Bond Strength One Component Epoxy Adhesive System Master Bond Polymer System Supreme3HT is a storage stable one component, heat curing epoxy adhesive featuring a hither to unattainable balance of performance properties including both high shear and.. |
|||
Cure Time | 19.8 - 30.0 min @Temperature 121 °C |
0.330 - 0.500 hour @Temperature 250 °F |
|
Master Bond Supreme 3HTND-1SM Fast Curing, One Component, Surface Mount Adhesive Master Bond Polymer System Supreme 3HTND-1SM is a one component, exceptionally fast curing surface mount adhesive system with exceptional toughness and durability. It has high shear and peel strengt.. |
|||
Cure Time | 19.8 - 30.0 min @Temperature 121 °C |
0.330 - 0.500 hour @Temperature 250 °F |
|
Master Bond Supreme 3HTND-2GT One Part, Toughened, Fast Curing Glob Top Adhesive Master Bond Polymer System Supreme 3HTND-2GT is a fast curing, toughened one component high performance epoxy adhesive/sealant which meets the growing need for precise positioning and bonding of mic.. |
|||
Cure Time | 19.8 min @Temperature 65.0 °C |
0.330 hour @Temperature 149 °F |
|
Trelleborg Emerson & Cuming Eccobond® 26 Two-Component General Purpose Epoxy Adhesive Emerson & Cuming 26 Eccobond® Two-Component General Purpose Epoxy AdhesiveFilled, room temperature curing, general purpose, epoxy adhesive. Recommended for varied uses including repair and manufact.. |
|||
Cure Time | 19.8 - 30.0 min @Temperature 121 °C |
0.330 - 0.500 hour @Temperature 250 °F |
|
Master Bond EP3HT Fast Curing One Component Epoxy System Master Bond Polymer System EP3HT is a one component system featuring high shear strength and good temperature resistance along with a fast cure schedule. Master Bond Polymer System EP3HT produces du.. |
|||
Cure Time | 19.8 - 30.0 min @Temperature 121 °C |
0.330 - 0.500 hour @Temperature 250 °F |
|
Master Bond EP3HTMED One Component, Biocompatible Epoxy System Master Bond Polymer System EP3HTMed combines the ease of a one part, no mix, fast curing adhesive with high shear strength. This special formulation fully meets USP Class VI requirements. EP3HTMed p.. |
|||
Cure Time | 19.8 min @Temperature 16.0 °C |
0.330 hour @Temperature 60.8 °F |
Tack Free |
Chesterton ARC 5 Paste grade Rapid Cure Abrasion Control Description: ARC 5 is an advanced composite formulated for emergency repair and patching of metal components subject to light abrasive and corrosive conditions. It can be used to seal leaks and patc.. |
|||
Cure Time | 19.8 min @Temperature 25.0 °C |
0.330 hour @Temperature 77.0 °F |
Light Load |
Chesterton ARC 5 Paste grade Rapid Cure Abrasion Control Description: ARC 5 is an advanced composite formulated for emergency repair and patching of metal components subject to light abrasive and corrosive conditions. It can be used to seal leaks and patc.. |
|||
Cure Time | 19.8 min @Temperature 43.0 °C |
0.330 hour @Temperature 109 °F |
Tack Free |
Chesterton ARC 897 Fine Grade Sliding Wear Compound Description: ARC 897 is an advanced ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a t.. |
|||
Cure Time | 19.8 min @Temperature 43.0 °C |
0.330 hour @Temperature 109 °F |
Tack Free |
Chesterton ARC BX2 Contractor Grade Fine Sliding Wear Compound Description: ARC BX2 is an advanced contractor grade ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It .. |
|||
Cure Time | 19.8 min @Temperature 43.0 °C |
0.330 hour @Temperature 109 °F |
Tack Free |
Chesterton ARC MX2 High Wear Fine Particle Wear Compound Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion and chemical attack. It is applied at a thickness of 3 mm (1/8”.. |
|||
Cure Time | 19.8 min @Temperature 32.0 °C |
0.330 hour @Temperature 89.6 °F |
Light Load |
Chesterton ARC MX5 Rapid Curing Fine Particle Wear Compound Description: An advanced ceramic reinforced composite for the emergency repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a th.. |
|||
Cure Time | 19.8 min @Temperature 16.0 °C |
0.330 hour @Temperature 60.8 °F |
Tack Free |
Chesterton MRS 5 Metal Rebuilding System MRS 5 is an advanced composite formulated for emergency repair and patching of metal components subject to light abrasive and corrosive conditions. It can be used to seal leaks and patch holes as we.. |
|||
Cure Time | 19.8 min @Temperature 25.0 °C |
0.330 hour @Temperature 77.0 °F |
Light Load |
Chesterton MRS 5 Metal Rebuilding System MRS 5 is an advanced composite formulated for emergency repair and patching of metal components subject to light abrasive and corrosive conditions. It can be used to seal leaks and patch holes as we.. |
|||
Cure Time | 19.8 min @Temperature 75.0 °C |
0.330 hour @Temperature 167 °F |
Dust Free, at 50% humidity |
Blue River Coatings High Performance Acrylic Sanding Sealer BLUE RIVER COATINGS HIGH PERFORMANCE ACRYLIC SANDING SEALER is a waterbased wood sealer to fill the grain. The product is designed to be a sandable self-sealing topcoat for wood. HIGH PERFORMANCE AC.. |
|||
Cure Time | 19.8 min @Temperature 75.0 °C |
0.330 hour @Temperature 167 °F |
Dust Free, at 50% humidity |
Blue River Coatings High Performance Acrylic Topcoat BLUE RIVER COATINGS HIGH PERFORMANCE ACRYLIC TOPCOAT is a water dispersible acrylic enamel. HIGH PERFORMANCE ACRYLIC TOPCOAT is designed to be a low VOC and EPA compliant coating with excellent cove.. |
|||
Cure Time | 19.8 min @Temperature 75.0 °C |
0.330 hour @Temperature 167 °F |
Dust Free, at 50% humidity |
Blue River Coatings Hyfro-Flex Polyurethane Top Coat BLUE RIVER COATINGS HYDRO-FLEX POLYURETHANE TOPCOAT is a water dispersible polyurethane. When the customer receives HYDRO-FLEX, it is already formed in the container, where as the solvent base type,.. |
|||
Cure Time | 19.8 min @Temperature 75.0 °C |
0.330 hour @Temperature 167 °F |
Recoat, at 50% humidity |
Blue River Coatings Undercoat Primer BLUE RIVER COATINGS UNDERCOAT PRIMER is a high quality, single component primer, not requiring any catalyzing agent. Performance obtained is equal or superior to that of two-component, catalyzed epo.. |
|||
Cure Time | 19.8 min @Temperature 75.0 °C |
0.330 hour @Temperature 167 °F |
Dust Free, at 50% humidity |
Blue River Coatings Low VOC Primer Sealer BLUE RIVER COATINGS LOW VOC PRIMER SEALER is a high quality, single component primer. Performance obtained is equal or superior to that of single component solvent primers. LOW VOC PRIMER SEALER off.. |
|||
Cure Time | 19.8 min @Temperature 75.0 °C |
0.330 hour @Temperature 167 °F |
Recoat, at 50% humidity |
Blue River Coatings Primer Sealer-PSWP BLUE RIVER COATINGS PRIMER SEALER-PSWP is a high quality, single component primer formulated specifically for priming wood, vinyl, and most plastic substrates. Performance obtained is equal or super.. |
|||
Cure Time | 19.8 min @Temperature 75.0 °C |
0.330 hour @Temperature 167 °F |
Recoat, at 50% humidity |
Blue River Coatings Wood Primer BLUE RIVER COATINGGS WOOD PRIMER is a high quality, single component primer, not requiring any catalyzing agent. WOOD PRIMER offers good coverage, excellent durability, and ease of application, as w.. |