Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 149 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	93.3 - 149 °C	200 - 300 °F	Average value: 110 °C Grade Count:8
Overview of materials for Polyphenylene Ether, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Impact Grade". Each property range of values reported is minimum and maximum values..
Deflection Temperature at 1.8 MPa (264 psi)	93.3 - 149 °C	200 - 300 °F	Average value: 127 °C Grade Count:6
Overview of materials for PPE/PPO + Carbon Fiber This property data is a summary of similar materials in the MatWeb database for the category "PPE/PPO + Carbon Fiber". Each property range of values reported is minimum and maximum values of appropr..
Deflection Temperature at 1.8 MPa (264 psi)	90.6 - 149 °C	195 - 300 °F	Average value: 142 °C Grade Count:83
Overview of materials for Polycarbonate, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 30% Glass Filled". Specific grades with glass content between 25% and 34% are included. E..
Deflection Temperature at 1.8 MPa (264 psi)	132 - 149 °C	270 - 300 °F	Average value: 142 °C Grade Count:49
Overview of materials for Polycarbonate, Carbon + PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Carbon + PTFE Filled". Each property range of values reported is minimum and maximum valu..
Deflection Temperature at 1.8 MPa (264 psi)	121 - 149 °C	250 - 300 °F	Average value: 136 °C Grade Count:14
Overview of materials for Polycarbonate, Conductive This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Conductive". Each property range of values reported is minimum and maximum values of appr..
Deflection Temperature at 1.8 MPa (264 psi)	129 - 149 °C	265 - 300 °F	Average value: 139 °C Grade Count:10
Overview of materials for Polycarbonate, NCG Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, NCG Filled". Each property range of values reported is minimum and maximum values of appr..
Deflection Temperature at 1.8 MPa (264 psi)	91.1 - 149 °C	196 - 300 °F	Average value: 143 °C Grade Count:33
Overview of materials for Polycarbonate, 40% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 40% Glass Filled". Specific grades with glass content between 35% and 44% are included. E..
Deflection Temperature at 1.8 MPa (264 psi)	107 - 149 °C	225 - 300 °F	Average value: 132 °C Grade Count:6
Overview of materials for Polycarbonate, Glass Fiber & Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Glass Fiber & Bead Filled". Each property range of values reported is minimum and maximum..
Deflection Temperature at 1.8 MPa (264 psi)	82.0 - 149 °C	180 - 300 °F	Average value: 100 °C Grade Count:5
Overview of materials for Acrylic, Impact Modified Sheet This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Impact Modified Sheet". Each property range of values reported is minimum and maximum values of..
Deflection Temperature at 1.8 MPa (264 psi)	104 - 149 °C	220 - 300 °F	Average value: 130 °C Grade Count:11
Overview of materials for Polypropylene, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Carbon Fiber 10%". Each property range of values reported is minimum and maximum values o..