Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 160 - 180 °C | 320 - 356 °F | ISO 75-A |
Raschig Group DECAL® 2061 Phenolic Wood flour reinforced phenolic molding compound. Good electrical properties, chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals and PCAs and .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 160 - 180 °C | 320 - 356 °F | ISO 75-A |
Raschig Group DECAL® 5431 Phenolic Organically and inorganically filled phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 155 - 180 °C | 311 - 356 °F | ISO 75-A |
Raschig Group MELOPAS® 2010 MF Melamine Organically and inorganically filled Melamine molding compound. Excellent surface hardness, good mechanical strength, good electrical properties. This product meets the allowed upper limits for heav.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 155 - 180 °C | 311 - 356 °F | ISO 75-A |
Raschig Group MELOPAS® 6605 MP Melamine Cellulose reinforced Melamine molding compound. Very good electrical properties, excellent surface hardness, good mechanical strength and heat resistance, good wear and UV-stability, good gliding be.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 155 - 180 °C | 311 - 356 °F | Injection and Compression; ISO 75 |
Raschig Group MELOPLAS® 150 MF Wood flour-reinforced MF molding compound in dark colors. High surface hardness, high mechanical strength, good electrical properties. Self-extinguishing (V-O/1,6 according to UL 94), UL-listed. Fr.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 155 - 180 °C | 311 - 356 °F | Injection and Compression; ISO 75 |
Raschig Group MELOPLAS® 152 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 155 - 180 °C | 311 - 356 °F | Injection and Compression; ISO 75-A |
Raschig Group MELOPLAS® 152.7 MF Cellulose-reinforced MF molding compound in white and colored shades. High surface hardness, very good UV stability, very good resistance to chemicals also to foodstuff ingredients, physiologically.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 155 - 180 °C | 311 - 356 °F | Injection and Compression; ISO 75-A |
Raschig Group MELOPLAS® 181 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. High surface hardness, good electrical properties, good mechanical strength, high UV and heat resistanc.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 155 - 180 °C | 311 - 356 °F | Injection and Compression; ISO 75-A |
Raschig Group MELOPLAS® 181.5 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. Very good electrical properties, high surface hardness, good mechanical strength, high UV and heat resis.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 155 - 180 °C | 311 - 356 °F | Injection and Compression; ISO 75-A |
Raschig Group MELOPLAS® 182 MF Wood flour-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in dark colors. Improved dimensional stability and electrical properties as compared with MP 180, high surf.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 155 - 180 °C | 311 - 356 °F | Injection and Compression; ISO 75-A |
Raschig Group MELOPLAS® 183 MF Cellulose-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in white and colored shades. Improved dimensional stability and electrical properties as compared with MP 18.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 160 - 180 °C | 320 - 356 °F | Injection and Compression; ISO 75-A |
Raschig Group MELOPLAS® 3025 MF Cellulose-reinforced and inorganically filled MF molding compound in white and colored shades. High surface hardness, good UV and heat stability, very good resistance to chemicals - also to foodstu.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 91.1 - 180 °C | 196 - 356 °F | Average value: 104 °C Grade Count:39 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled". Specific grades with glass content betwe.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 160 - 180 °C | 320 - 356 °F | ISO 75 Af |
Vyncolit 2530 W Novolac Phenolic Mineral and organic filled phenolic molding compound with excellent thermal properties.USES: Lamp sockets, special lamp holders, pan handles and knobs.Information provided by Vyncolit, a Sumitomo Ba.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 160 - 180 °C | 320 - 356 °F | ISO 75 Af |
Vyncolit 2723 W Novolac Phenolic Mineral and organic filled phenolic molding compound with excellent mechanical, thermal and dielectric properties. I2/FO classified under NF F 16-101 (Fire & Smoke classification).USES: Circuit bre.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 150 - 180 °C | 302 - 356 °F | ISO 75 Af |
Vyncolit 2920 W Novolac Phenolic Mineral and organic filled molding compound with good dimensional stability and heat resistance.USES: Carburettor and intake manifold thermal insulator.Information provided by Vyncolit, a Sumitomo B.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 - 180 °C | 338 - 356 °F | ISO 75 Af |
Vyncolit X682 Novolac Phenolic Glass fiber, glass bead and graphite filled phenolic molding compound with excellent mechanical properties and a low coefficient of friction.USES: Water pump seals and self-lubricating bearings.Info.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 155 - 180 °C | 311 - 356 °F | Injection and Compression; ISO 75-A |
Raschig Group MELOPLAS® 180 MF Wood flour-reinforced, phenol-modified MF molding compound (MPF) in dark colors. High surface hardness, good mechanical strength and electrical properties, good heat resistance. Self-extinguishing .. |