Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYfill PP HIP15025 HC Polypropylene Information provided by Polykemi AB |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C @Thickness 6.40 mm |
199 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Cycoloy® CX7259 PC (Asia Pacific) Cycoloy resin grade CX7259 is a flame retardant impact modified polycarbonate blend aiming at ultra thin wall designs. It is listed as UL-94 V1 at 0.5mm & V0 at 0.6mm with excellent flow and balance.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | ASTM D-648 |
PlastiComp Complet® LGF40 - TPU Rigid Thermoplastic Polyurethane, 40% Long Glass Fiber Reinforced Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Rigid polyurethane with 40% long glass fiber reinforcementInformation provided by Plas.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | ASTM D648 |
Ineos Nova 1210 High Heat Crystal Polystyrene
(discontinued **) High heat resistance, High molecular weight, optimum performance in extruded foamApplications: Meat and poultry trays, Egg cartons, Food packagingExposure to gamma radiation in the 2.02-6.06 megarad.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C @Thickness 3.20 mm |
199 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics Lexan® FST3403 PC Copolymer (Europe-Africa-Middle East) Lexan* FST3403 resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is EN45545 R6 HL3 compliant and an ideal candidate for train interior .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C @Diameter 4.00 mm |
199 °F @Diameter 0.157 in |
Unannealed; bar; ISO 75-2 |
NOVA Chemicals DYLARK® 250 Impact Grade Engineering Resin Features:High heat resistance Good chemical resistance High impact strength Excellent flow characteristicsApplications:Automotive interior trim applications Automotive consoles Structural HousingsIn.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | |
Ineos ABS TRIAX® 1120 ABS/Nylon Blend, Injection Grade, As Conditioned Injection molding grade with good flow and stress corrosion cracking resistance, good chemical resistance (fuel, cleaning agents), high impact and notched impact strength, good acoustical damping be.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 92.8 °C | 199 °F | Unannealed; ASTM D648 |
Techmer ES HiFill FR® PA6/6,6 GF NAT Availability: North AmericaForms: PelletsFeatures: Flame RetardantAppearance: Natural ColorProcessing Method: Injection MoldingInformation provided by TP Composites, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP THERMOCOMP AF004AH ABS LNP THERMOCOMP* AF004AH is a compound based on ABS resin containing 20% Glass Fiber. Added feature of this material is: Healthcare. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C @Thickness 6.40 mm |
199 °F @Thickness 0.252 in |
ASTM D648 |
Samsung Cheil Industries Infino® GC-1017 PC/ABS, FR Information provided by Samsung Cheil Industries. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | ISO 75-1,-2 |
Styrolution Novodur® P2M-AT ABS Pellets Novodur® P2M-AT has high impact strength, high gloss, and contains antistatic additive. It is used for the production of molded plastic articles. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C @Thickness 6.40 mm |
199 °F @Thickness 0.252 in |
ASTM D648 |
Samsung Cheil Industries Starex® VG-4920F ABS, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C @Thickness 6.40 mm |
199 °F @Thickness 0.252 in |
ASTM D648 |
Samsung Cheil Industries Starex® BM-0320 J ABS, Unreinforced Heat resistantInformation provided by Samsung Cheil Industries. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP Thermocomp WB006 PBT LNP* Thermocomp* WB006 is a compound based on Polybutylene Terephalate resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics Noryl NH3060 PPE+HIPS NH3060 resin is a modified PPE + PS blend with an excellent balance of non-chlorinated non-brominated flame retardance, hydrolytic stability, impact and heat resistance, good flow, and low specific .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C @Thickness 3.20 mm |
199 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics NORYL PVX524 PPE PREVEX* PVX524 resin is a high flow, non FR grade, 100 C HDT |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Unannealed; ISO 75-2/A |
Styron PULSEâ„¢ GX50 PC/ABS Engineering Resin Overview: PULSE GX50 engineering resins give exceptional impact strength even at low temperature and have sufficient heat resistance for the majority of automotive interior components. This resin pr.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 92.8 °C @Thickness 6.35 mm |
199 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
Samsung Cheil Industries Starex® SR-0310 Heat Resistant Grade ABS Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C @Thickness 6.40 mm |
199 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics Noryl PX1701 PPE+PS This data was supplied by SABIC-IP for the Americas region. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Annealed; ASTM D648 |
Lubrizol Isoplast® 101LGF40NAT Engineering Thermoplastic Polyurethane Resin Available in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | ISO 75-1/-2 |
Covestro Makroblend® KU 2-7609 Polycarbonate + PBT, Mineral Filled Impact Grade ISO 7792-1-PC/PBT,MHPR,-030,MD20(PC+PBT)-blendsimpact modifiedInjection molding grade20% mineral filledPreprocessingMax. Water content |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 92.8 °C | 199 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
Diamond Polymers ABS 7502 Description: Injection Molding Grade, Extra High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 92.8 °C | 199 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
Diamond Polymers ABS 7501 Description: Injection Molding Grade, Extra High ImpactInformation provided by Diamond Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | ASTM D648 |
Ashley Polymers Ashlene® 830SMS Nylon 6, MoS2 Filled Basic Nylon 6, medium viscosity, lubricated with Molybdenum Disulfide.Data provided by the manufacturer |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C @Thickness 6.40 mm |
199 °F @Thickness 0.252 in |
Method A; ASTM D648 |
Bhansali Engineering Abstron BL60 Impact modifier for PVC Impact modifier for PVC, White powderInformation provided by Bhansali |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Method A - Annealed; ASTM D-648 |
Bhansali Engineering Abstron IM-17 A EP ABS Electro Plating Applications Electroplating & Hot Stamping GradesInformation provided by Bhansali |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C @Thickness 6.40 mm |
199 °F @Thickness 0.252 in |
Method A; ASTM D648 |
Bhansali Engineering Abstron MIF45EP ABS Injection Molding Grade Electroplating, High FlowInformation provided by Bhansali |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Annealed, 80°C, 4 hours; ISO 175 |
LG Chemical HG-174 ABS, High Gloss, Super High Flow Information Provided by LG Chem |