Bhansali Engineering Abstron BL60 Impact modifier for PVC

Category Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded
Manufacturer Bhansali Engineering
Trade Name Abstron
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bhansali Engineering Abstron BL60 Impact modifier for PVC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Impact modifier for PVC, White powderInformation provided by Bhansali
Physical Properties Metric English Comments
Specific Gravity 1.045 g/cc
1.045 g/cc
ASTM D792
Linear Mold Shrinkage 0.00400 - 0.00600 cm/cm
0.00400 - 0.00600 in/in
ASTM D955
Melt Flow 8.00 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 8.00 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 106
106
ASTM D785
Tensile Strength, Yield 34.3 MPa

@Thickness 3.20 mm
 4980 psi

@Thickness 0.126 in
 Type I, 5 mm/min; ASTM D638
38.2 MPa

@Thickness 3.20 mm
 5550 psi

@Thickness 0.126 in
 Type I, 50 mm/min; ASTM D638
Flexural Yield Strength 53.0 MPa

@Thickness 6.40 mm
 7680 psi

@Thickness 0.252 in
 5 mm/min; ASTM D790
Flexural Modulus 1.86 GPa

@Thickness 6.40 mm
 270 ksi

@Thickness 0.252 in
 5 mm/min; ASTM D790
Izod Impact, Notched 3.92 J/cm

@Thickness 6.40 mm
 7.35 ft-lb/in

@Thickness 0.252 in
 ASTM D256
5.69 J/cm

@Thickness 3.20 mm
 10.7 ft-lb/in

@Thickness 0.126 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C

@Thickness 6.40 mm
 199 °F

@Thickness 0.252 in
 Method A; ASTM D648
Flammability, UL94 HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
Users viewing this material also viewed the following: