Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 58.9 °C | 138 °F | ASTM D648 |
RheTech Products FT7011-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: Claddings and faciasExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | STN EN ISO 75/A |
Plastcom SLOVAMID 66 HI Polyamide 66, Impact Grade FeaturesModified with thermoplastic reactive elastomer, determined for mouldings with high toughness also at low temperatures. Eligible application for ski-shoes, helmets for sport and other safety.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | |
Plastcom SLOVAMID 66 HI/1 TS PA66, improved strength FeaturesModified with thermoplastic reactive caoutchouc, determined for mouldings with high toughness also at minus temperatures. Eligible application for ski-shoes, helmets for sport and other safe.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | |
Plastcom SLOVAMID 66/6 HI/1 PA66/6, improved strength FeaturesMix of polyamide 66/6 modified with thermoplastic reactive caoutchouc, determined for mouldings with high toughness also at minus temperatures. Eligible application for ski-shoes, helmets fo.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75 |
Solvay Engineered Polymers SEQUEL® 2380 Engineered Polyolefin
(discontinued **) Description: SEQUEL® 2380 engineered polyolefin is designed for large mold-in-color automotive interior applications that require stiffness and dimensional stability over a broad temperature range... |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 58.9 °C | 138 °F | Unannealed; ISO 75A-1, -2 |
LyondellBasell Hostacomâ„¢ CB280F Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ CB280F high melt flow, 1,900 MPa flexural modulus, UV-stabilized, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent balance of processability, .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP LUBRICOMP FL004 PE LNP* Lubricomp* FL004 is a compound based on Polyethylene resin containing 20% PTFE. Added features of this material include: Internally Lubricated. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | 80*10*4mm, Cut; ISO 75-1&2 |
SABIC Innovative Plastics SABIC PPCOMPOUND 9710 PP SABIC® PPcompound 9710 is a mineral filled, impact modified polypropylene TPO. This material combines high impact resistance, scratch resistance, and heat stability with interior automotive UV st.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C @Thickness 3.20 mm |
138 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP LUBRICOMP RP003 PA 66 LNP* LUBRICOMP* RP003 is a compound based on Nylon 66 resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP LUBRICOMP WL003 PBT (Europe-Africa-Middle East) LNP* Lubricomp* WL003 is a compound based on Polybutylene Terephalate resin containing PTFE. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C @Thickness 3.20 mm |
138 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP STAT-KON WS002I PBT LNP* STAT-KON* WS002I is a compound based on PBT resin containing 10% Stainless Steel. Added features of this material include: Electrically Conductive, High Impact. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP STAT-LOY M3000 PP (Europe-Africa-Middle East) LNP* Stat-loy* M3000 is a compound based on Polypropylene resin. Added features of this material include: Antistat, High Impact. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75-1/-2 |
Styrolution Styrolux® 693 D SBC Description: Styrolux® 693 D is a clear styrene-butadiene copolymer (SBC) with a well balanced combination of toughness and clarity. Styrolux® 693 D is mainly used for thermoformed articles, e.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP LUBRICOMP RI001 PA 66 LNP* LUBRICOMP* RI001 is a compound based on Nylon 66 resin containing 2% Silicone. Added feature of this grade is: Wear Resistant. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP STAT-LOY M3000 PP LNP STAT-LOY* M3000 is a compound based on unfilled Polypropylene resin. Added feature of this material is: Antistat. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75 |
A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ASTM D648 |
Formosa Plastics Formolene® 6145O Impact Copolymer Polypropylene Impact Copolymer for Appliance Applications Formolene® 6145O is a medium impact copolymer of polypropylene characterized by its easy mold flow, physical property balance and excellent dimensional s.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75 |
A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75 |
A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | DIN 53461 |
Polyram RamOfin PPC342M6 Polypropylene, 30% Mineral Filled 30% mineral filled, heat resistant polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ASTM D648 |
Diamond Polymers NYLON 6615 HS Natural Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ASTM D648 |
Braskem H 105 Injection Molding Polypropylene Description: H 105 is a high melt flow rate homopolymer with high transparency. Designed for use on thin-walled injection molding parts with high output. This product exhibits excellent processabili.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | |
Arkema Group Rilsan® MB 3750 Nylon 11, Transparent Grade (Dry) Designation ISO 1874-PA11/xx,F,THL,22-020Transparent semi-crystalline PA11 grade.Used for film extrusion and injection molding (low thickness).Very good low temperature impact strength.High chemical.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | |
BASF Procom® D 1165 Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 58.9 °C | 138 °F | |
Aclo Accutech Polypropylene Copolymer CP0436T30L Talc Reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | |
BASF Procom® D 1195 Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75 |
A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | 75/Method Af |
Premix Thermoplastics PRE-ELEC® PA 1411 Conductive Thermoplastic Compound PRE-ELEC® PA 1411 is a conductive thermoplastic compound based on polyamide 6. Conductivity is achieved by using conductive carbon black. PRE-ELEC® PA 1411 has a very low electrical resistivity. P.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75-2 |
Borealis Xmod™ MC55T1 Polypropylene Compound 10% Mineral Filled Xmod MC55t1 is a 10% mineral filled grade based on HCPP intended for injection molding. Xmod has been developed especially for the car industry, to be used in interior parts. XMod offers very good .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75 |
A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman. |