- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 52.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 52.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | |
| Plastcom SLOVALEN PC 63 T 15 PP reinforced with 15% mineral filler Features: Modified PP for injection moulding with the content of 15% mineral filling. Increased rigidity, strength and thermal. Decreased shrinkage. Application in all automotive interior industry.D.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75 |
| Phillips Sumika Marlex® CHP-275 Thermoplastic Polyolefin
(discontinued **) Engineered Thermoplastic Polyolefin.Applications: Automotive Head and Side Impact TrimConditioning after Molding: 48 hr at 23°C, 48 hr at 90°CNominal Shrinkage: 0.7-0.9%, 0.8-1.1%Drying conditions.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 - 104 °C | 126 - 219 °F | Average value: 64.8 °C Grade Count:18 |
| Overview of materials for Polypropylene, Fiber Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Fiber Grade". Each property range of values reported is minimum and maximum values of app.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 2-9000 Polypropylene Block-Copolymer INNOPOL® CS 2-9000 is a polypropylene block-copolymer based compound. This grade is available in nature and custom colored form.INNOPOL® CS 2-9000 is developed for producing injection molded a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON MX10301C PP LNP* STAT-KON* MX10301C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Thermocomp MX01767C PP LNP* Stat-Kon* MX01767C is a compound based on Polypropylene containing Proprietary Fillers. Charactiers of this grade are Statically Conductive, Clean Compound System.This data was supplied by SAB.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | Unannealed; ISO 75-2/Af |
| Styron DGF080.00 ESU Polypropylene Overview: 10% glass filled polypropyleneNaturalMedium flowHeat ResistantInformation provided by Styron |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® V3004 PBT (Asia Pacific) Unfilled PBT modified with elastomer. Targeted for flexible hinge, automotive connectors, film applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75 B |
| Borealis Borsoft™ SF203CF Soft Polypropylene Copolymer for Extrusion Coating Borsoft SF203CF is a new statistic-heterophasic propylene-ethylene copolymer suitable for coating applications. Its polymer structure permits perfect adhesion to certain products. According to the.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75-2 |
| Borealis Daplen™ HJ060UB Polypropylene Compound for Direct Left Manufactured Applications Daplen FJ060UB is a special low viscosity compound for direct LFT manufacturing process. It interacts perfectly with glass fibers to create excellent stiffness and impact resistance. Daplen HJ060U.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1498HU is a high flow UV stabilized medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1498HU is a high flow UV stabilized medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1498HU is a high flow UV stabilized medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C per hour; ISO 75-2 |
| Total PPH 10099 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 1099 is a controlled-rheology homopolymer having a very narrow molecular weight distribution. PPH 10099 is characterized by high fluidity for high speed spinning on spunla.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C per hour; ISO 75-2 |
| Total PPH 9082 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 9082 is a controlled-rheology and antistatic homopolymer. PPH 9081 is characterized by a narrow molecular weight distribution and excellent flow properties, providing impr.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C per hour; ISO 75-2 |
| Total PPH 9099 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 9099 is a very narrow molecular weight distribution homopolymer polypropylene, with anti gas-fading stabilization. ApplicationATOFINA Polypropylene PPH 9099 is intended for.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C per hour; ISO 75-2 |
| Total PPC 3640 Polypropylene, Heterophasic Copolymer ATOFINA Polypropylene PPC 3640 is a nucleated heterophasic copolymer. PPC 3640 is characterized by improved stiffness, creep resistance and high impact resistance.ApplicationPPC 3640 has been devel.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75-2/AF |
| Addiplast Addilene J 310 Polypropylene Copolymer UnreinforcedInformation provided by Addiplast. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
| Ashley Polymers Ashlene® D926 Nylon 12 A flexible Nylon 12 with exceptional toughness, excellent abrasion and chemical resistance, outstanding low temperature performance, dimensional stability and low moisture absorption. Also availabl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
| Ashley Polymers Ashlene® D930H Nylon 12 A plasticized Nylon 12 offering improved flexibility with superior moisture and chemical resistance. Also UV and heat stabilized, available in natural and precolored. Any color other than natural .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
| Ashley Polymers Ashlene® L930 Nylon 12 A plasticized Nylon 12 offering improved flexibility with superior moisture and chemical resistance. The natural color is slightly darker.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
| Ashley Polymers Ashlene® D925 Nylon 12 A flexible Nylon 12 with exceptional toughness, excellent abrasion and chemical resistance, outstanding low temperature performance, dimensional stability and low moisture absorption. Also availabl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | |
| 3M Dyneon™ PVDF 11010/0000 Polyvinylidene Fluoride 3M™ Dyneon™ PVDF 11010/0000 is a copolymer of VF2 and HFP (hexafluoropropylene). Recommended for flared tubing, it combines excellent chemical resistance, and dimensional stability with a moderate.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C per hour; ISO 752 |
| Total PPC 3120 MU5 Polypropylene, Heterophasic Copolymer, Automotive Polypropylene PPC 3120 MU5 is a heterophasic copolymer with a Melt Flow index of 15 g/10 min. Polypropylene PPC 3120 MU5 is a high impact copolymer formulated to give good UV resistance.Polypropyle.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOTUF W1000I PBT (Europe-Africa-Middle East) LNP* THERMOTUF* W1000I is a compound based on Polybutylene Terephalate resin. Added features include: High Impact |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 1498HU UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1498HU is a high flow UV stabilized medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Stat-kon MD000IU PP (Asia Pacific) LNP* Stat-kon* MD000IU is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact, UV Stabilized.This data wa.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON MS000IL PP LNP* STAT-KON* MS000IL is a compound based on Polypropylene resin containing Stainless Steel. Added features of this material include: High Impact, Low Extractible, Electrically Conductive, food c.. |
|||