- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 152 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 152 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | STN EN ISO 75/A |
| Plastcom SLOVALEN PC 69 GF 35 FRT 4 Polypropylene Copolymer, 35% Glass Fiber, Halogen Free and Phosphor Free Flame Retardant FeaturesModified copolymer PP for injection moulding, chemically reinforced with 35% glass fiber, contains the modifier of mechanical properties and non halogen and free phosphor flame retardant. I.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 305 °F | ASTM D648 |
| RheTech Products GC40P100-00 40% Glass Fiber Reinforced Polypropylene, Chemically Coupled, Natural Applications: Consumer goodsBracketsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | Unannealed; ISO 75-2/A |
| PolyOne OnForce™ LFT PP-50LGF/001 Natural Polypropylene Homopolymer (PP Homopolymer) PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | ASTM D-648 |
| PlastiComp Complet® LGF40 - PP Homopolymer Polypropylene, 40% Long Glass Fiber Reinforced Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Polypropylene with 40% long glass fiber reinforcementInformation provided by PlastiCom.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® XHT3141 PC Copolymer XHT3141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® XHT3143 PC Copolymer XHT3143 is a high flow, UV stabilized, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® XHT3143 PC Copolymer (Asia Pacific) XHT3143 is a high flow, UV stabilized, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® EXRL0627 PC Copolymer EXRL0627 is a high flow, UV stabilized, high heat polycarbonate copolymer. It is available in a range of opaque and transparent colors.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 305 °F | Unannealed; ASTM D648 |
| PolyOne Stat-Tech™ NJ-10SS/000 Nylon 12 - 10% Stainless Steel Reinforced
(discontinued **) Data provided by PolyOne. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | |
| Lehmann & Voss LUVOCOM® 50/CF/10/GF/10/TF/10/BK Polycarbonate, with carbon fiber, glass fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 305 °F | ASTM D648 |
| Fiberfil® J-60/30/E/M Polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 305 °F | ASTM D648 |
| Fiberfil® J-60/30/E8 Polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 305 °F | ASTM D648 |
| Fiberfil® J-60/30/F Polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 305 °F | ASTM D648 |
| Fiberfil® J-60/40/E8 Polypropylene Homopolymer, 40% Glass Reinforced, Chemically coupled Information provided by FIBERFIL Engineered Plastics |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | |
| Lehmann & Voss LUVOCOM® 1105/WT106 PEEK, unreinforced Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistan.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | |
| Lehmann & Voss LUVOCOM® PC-50/GF/30/TF/15/ BK Polycarbonate, with glass fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 305 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6 0301 Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/ReinforFeatures: High DensityProcessing Method: Injection MoldingInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 305 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PP GF20 CC HS 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightAdditive: Heat StabilizerFeatures: Heat Stabilized and Chemically CoupledInformation pro.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C @Thickness 3.20 mm |
306 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP KFB11 Acetal Copoly LNP* THERMOCOMP* KFB11 is a compound based on Acetal Copolymer resin containing 5% Glass Fiber, 5% Glass Bead. Added features of this material include: Low Warpage, Chemically Coupled. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics ULTEM 9085 PEI Blend (Asia Pacific) High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | ASTM-D648 |
| Polyram Polytron P40B11 Homopolymer Polypropylene, Chemically Coupled 40% LGF A chemically coupled 40% LGF reinforced black PP, heat stabilized for injection molding applications.Information provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | ASTM-D648 |
| Polyram Polytron P40N01 Homopolymer Polypropylene, Chemically Coupled 40% Long Glass Fiber A CHEMICALLY COUPLED 40% LONG GLASS FIBER REINFORCED NATURAL POLYPROPYLENE HEAT STABILIZED FOR INJECTION MOLDING APPLICATION.Information provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | ISO 75 |
| Polyram Polytron P40N11 Polypropylene, 40% Long Glass Fibers A chemically coupled 40% long glass fiber reinforced natural polypropylene, heat stabilized, for injection molding applications.Information provided by Polyram. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 305 °F | |
| BCC Products BC 7136 Epoxy Casting BC7136 is a gray, low toxicity, aluminum filled, epoxy casting resin. This heat resistant system may be used at room temperature without post-curing. May be cast to a thickness of ¾ inch in non-con.. |
|||