Polyram Polytron P40N11 Polypropylene, 40% Long Glass Fibers
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler |
| Manufacturer | Polyram |
| Trade Name | Polytron |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram Polytron P40N11 Polypropylene, 40% Long Glass Fibers.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A chemically coupled 40% long glass fiber reinforced natural polypropylene, heat stabilized, for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0012 cm/cm | 0.0012 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 120 MPa | 17400 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 6.70 GPa | 972 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 168 °C | 334 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Flame Spread | 22 mm/min | 0.87 in/min | FMVSS302 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C6600 PC+ABS
- SABIC Innovative Plastics Geloy XP4034 ASA (Europe-Africa-Middle East)
- SABIC Innovative Plastics Lexan® DMX1132 PC Copolymer (Asia Pacific)
- Fainplast Compounds RH 207/OP Rigid PVC, Antishock Extrusion
- Lubrizol Advanced Materials Pearlthane® MB-9005 Thermoplastic Polyurethane Elastomer
- Teknor Apex Beetle® 66GS6 Nylon 66, 30% Glass Bead Reinforced
- Eurostar Staramide B28H PA6, Heat Stabilized, Injection Molded
- BASF Neopolen® P 9230 K 0.04 g/cc Core density; Expanded Polypropylene (Europe)
- Polyram PlusTek RA502 Nylon 6.6, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved