- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 399 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 399 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 3.20 mm |
399 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem 1100EF PEI Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, U.S. FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 3.20 mm |
399 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM 2312EPR PEI 30% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 399 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics ULTEM 2312EPR PEI (Asia Pacific) 30% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 3.20 mm |
399 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM 2312EPR PEI (Asia Pacific) 30% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 6.40 mm |
399 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem ATX202R PEI+PCE 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 6.40 mm |
399 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem ATX202R PEI+PCE (Asia Pacific) 20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 3.20 mm |
399 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem ATX203R PEI+PCE 30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 3.20 mm |
399 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Ultem ATX203R PEI+PCE (Europe-Africa-Middle East) 30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regio.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 6.40 mm |
399 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 553 PBT+PC 30% GR PBT+PC, UL94 V-0. Reduced warpage characteristics.Applications; appliance handles, spotlights, electric motors, pump housings, etc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 6.40 mm |
399 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 553 PBT+PC (Asia Pacific) 30% GR PBT+PC, UL94 V-0. Reduced warpage characteristics.Applications; appliance handles, spotlights, electric motors, pump housings, etc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 6.40 mm |
399 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 553U PBT+PC 30% GR PBT+PC, UL94 V-0. Reduced warpage characteristics.Applications; appliance handles, spotlights, electric motors, pump housings, etc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 6.40 mm |
399 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 855 PBT 15% GR PBTP, UL94 V-0 rated. Improved surface appearance. For external housings: steam irons, appliance housings and lighting parts. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 3.20 mm |
399 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Valox® PDR4910 PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 6.40 mm |
399 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Xenoy® 6370 PBT+PC 30% glass-reinforced, impact modified thermoplastic alloy. Improved toughness and ductility. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 399 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Thermocomp EB004 PEI LNP* Thermocomp* EB004 is a compound based on Polyetherimide resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 3.20 mm |
399 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp KB004 Acetal Copolymer LNP THERMOCOMP* KB004 is a compound based on Acetal Copolymer resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 3.20 mm |
399 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Noryl GTX GTX965 PPE+PA66 NORYL GTX965 is a mineral reinforced PPE/PA blend. It offers excellent surface appearance, processability and dimensional stability at elevated temperatures. The best molding condition for good appe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 6.40 mm |
399 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics ULTEM LTX300A PEI Copolymer (Asia Pacific) High flow Polyetherimide blend with low toxicity, smoke and flame evolution. ECO Compliant, UL94 V0 listing in recognized colors. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 399 °F | |
| Arkema Group Orgalloy® LE 6010 HV Nylon Alloy, 10% Glass Fiber Reinforced (Conditioned) LE series, flexible polyamide alloys: processability on PE screw, low moisture absorption, chemical resistance (no known solvents). 10% glass fiber reinforced. Suited to blow molding of technical pa.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 399 °F | ASTM D648 |
| Adell BJ-14 Nylon 6, 20% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 399 °F | ASTM D648 |
| Adell BJ-34 Nylon 6, 20% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 - 221 °C | 399 - 430 °F | ASTM D648 |
| Cast Nylons Nycast® 6MPB Plasticized Nylon 6 A plasticized Type 6 material, NYCAST® 6MPB is formulated for use as pile driver caps or cushion pads. Data provided by the manufacturer, Cast Nylons Limited.The data below are average values prese.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 - 221 °C | 399 - 430 °F | ASTM D648 |
| Cast Nylons Nycast® Nyloil®-FG Lubricated Nylon, Food Grade NYCAST® NYLOIL® was developed to extend the wear-resistant properties of unlubricated or dry lubricated materials such as MoS2 filled nylons. NYCAST® NYLOIL® will last 5 to 7 times longer than .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 399 °F | ASTM D648 |
| Ashley Polymers Ashlene® P126 PBT Polyester, 30% Glass Reinforced PBT polyester with 30% glass reinforcement.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 - 221 °C | 399 - 430 °F | ASTM D648 |
| Cast Nylons Nycast® Nyloil® Lubricated Nylon NYCAST® NYLOIL® was developed to extend the wear-resistant properties of unlubricated or dry lubricated materials such as MoS2 filled nylons. NYCAST® NYLOIL® will last 5 to 7 times longer than .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 - 221 °C | 399 - 430 °F | ASTM D648 |
| Cast Nylons Nycast® XHA Heat Stabilized Nylon 6 Heat stabilized Cast Nylon 6 adds up to 20 degrees F higher continuous operation temperature for those applications that require additional temperature resistance beyond the standard resistance. Dat.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 399 °F | ASTM Test |
| BASF Ultramid® B3ZG3 15% Glass Filled PA6 (Dry) Ultramid B3ZG3 is an impact-modified, 15% glass fiber reinforced injection molding PA6 grade. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 6.40 mm |
399 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL GTX GTX909 PPE+PS+PA 400F (205C) HDT. 3.3 Notched Izod. Excellent chemical resistance |
|||