- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 253 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 253 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.18 mm |
253 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Stat-Tech™ PC-CB2/000 CR Polycarbonate (PC) Stat-Tech™ PC-CB2/000 CR XP100827Information provided by PolyOne |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| Network Polymers NPP 30-0200 TF20 Description: 20% Talc Filled Homopolymer PolypropyleneInformation provided by Network Polymers Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP CIP15015 UV Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® MC8002 PC+ABS AUTOMOTIVE. Low viscosity, high impact and ductility. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® MC8100 PC+ABS Extrusion blowmolding grade. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® MC8100 PC+ABS (Asia Pacific) Extrusion blowmolding grade. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPHC T20050 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD1212 PC Copolymer 18 MFR LEXAN High Flow Ductile Copolymer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD1212 PC Copolymer (Europe-Africa-Middle East) 18 MFR LEXAN High Flow Ductile Copolymer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD1232 PC Copolymer (Europe-Africa-Middle East) 18 MFR LEXAN High Flow Ductile Copolymer UV-stabilized, available in transparent colors only |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD1262 PC Copolymer (Asia Pacific) 19 MFR LEXAN High Flow Ductile Copolymerwith 400 nm cut off, available in transparent colors only |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP CIP6015F VTUV Polypropylene, Mineral Reinforced, Heat and UV Stabilized Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD1212 PC Copolymer (Asia Pacific) 18 MFR LEXAN High Flow Ductile Copolymer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® HFD1262 PC Copolymer 19 MFR LEXAN High Flow Ductile Copolymerwith 400 nm cut off, available in transparent colors only |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | Unannealed; ASTM D648 |
| Global PP-1142-R Polypropylene Homopolymer Description-transparency, high stiffness, high heat resistantApplications-disposable drinkware, thin-walled parts, medical applicationsInformation provided by Global Polymers Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 2-4120 20% Talc-Filled Polypropylene Block-Copolymer INNOPOL® CS 2-4120 is a 20% talc-filled compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form as well.INNOPOL® CS 2-4120 is developed for p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Lubricomp ZP003 PPE+PS (Europe-Africa-Middle East) LNP* LUBRICOMP* ZP003 is a compound based on PPE + PS Blend resin containing PTFE, Silicone. Added features include Internally Lubricated.This data was supplied by SABIC-IP for the Europe-Africa-Mid.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 6.40 mm |
253 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Xenoy® X3515 PC+POLYESTER (Europe-Africa-Middle East) Flame Retardant, Impact Modified, Opaque, Designed for outdoor telecommunication enclosure applications.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ISO 75 |
| Teijin Multilon T-3011 Standard PC/ABS Polymer Alloy General grade of PC/ABS polymer alloy, having improved impact strength and heat resistance compared with a heat resistant ABS and flame retardant m-PPE and also having higher fluidity compared with .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON KD000EI Acetal Copolymer (Europe-Africa-Middle East) LNP* Stat-Kon* KD000EI is a compound based on Acetal Copolymer resin containing Carbon Powder. Added features include: Electrically Conductive, Impact Modified. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| A. Schulman POLYFLAM™ FLP 3714 20% Glass Filled HDPE DescriptionPolyfort® FLP 3714 is a 20% glass filled HDPE product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | Annealed; ASTM D648 |
| ExxonMobil AP3N Polypropylene Impact Copolymer Product Description: A medium impact copolymer resin designed for appliance applications requiring good stiffness and fast cycle time.Availability: Asia Pacific Features:Fast Molding CycleHigh Glos.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| ExxonMobil PP1222F Mineral-filled Homopolymer Medium melt flow rate homopolymer, 20% filled. Particularly suitable for consumer products and appliance applications requiring long term heat aging resistance. UL continuous service rating of 95°.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| ExxonMobil PP7815E1 Polypropylene Homopolymer Product Description: A high crystallinity, low impact strength copolymer resin designed for compounding base or injection molding applications requiring high melt flow rate.Availability: North Amer.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0336M20CL Mica Reinforced Coupled |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0336M40L Mica Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | |
| BASF Luranyl® KR 2420 Polyphenylene Ether + Styrene-Butadiene Blend Grade with high resistance to heat deformation and outstanding impact strength. For auto parts such as air vents or the instrument panel; also used for door-mirror housings.Data was collected by IS.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C | 253 °F | ASTM D648 |
| Aclo Accutech Polypropylene Copolymer CP0436M40L Mica Reinforced |
|||