- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 248 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 248 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
| Mytex Polymers AS65KWLGUS Polypropylene, Talc filled, Compounded Description: Talc filled compounded polypropylene with high stiffness, superior impact balance, surface hardness and extremely low gloss.Key Applications: Non-painted instrument panelInformation pro.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYblend 50LG PC/ABS-Blend, Low Gloss Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYblend 65CI PC/ABS-Blend Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH GF1020 Polypropylene Homopolymer, Glass Fibre-Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH T3022D Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
| Reliance Industries Repol H200MK Polypropylene REPOL Polypropylene H200MK is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
| ICO Polymers ICORENEâ„¢ 440-1312 PP Rotational Molding Resin Description: ICORENE 440-1312 is a polypropylene copolymer developed for rotational molding applications. The resin is fully UV protected. Key Characteristics: very high rigidity, good creep resist.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOL GP1000FC Flame Retardant PP Description: Injection Molding, FR PP, General Purpose, Flame RetardantApplication: Electrical & Electronic, Automotive PartsCAS: 9003-07-0 and 1309-64-4Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 2-9120 20% Talc-Filled Polypropylene Block-Copolymer INNOPOL® CS 2-9120 is a 20% talc-filled compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 2-9120 is developed for producing.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75-1/-2 |
| Lanxess Pocan® S 1517 000000 PBT PBT, non-reinforced, injection molding, extrusion, impact modified |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
| Lavergne VYTEEN PC/ABS 8515 Polycarbonate - Acrylonitrile Butadiene Styrene Alloy Vyteen PC/ABS 8515 is an enhanced PC/ABS alloy with balanced impact/stiffness properties designed for injection molding applications.Features: -High resilience -Excellent processability -High def.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 359 PBT (Europe-Africa-Middle East) VALOX 359 is an unreinforced, flame retarded, low warpage PBT injection moulding resin. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Valox® VX5005 PBT (Europe-Africa-Middle East) VALOX VX5005 is a 5% glass fibre reinforced, impact modified PBT+PC blend with low warpage characteristics.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
| SPS Guang Zhou SAMATâ„¢ 5000C Flame-retarded Polypropylene Characteristic: Good flame retardance, non-halogen, high flow properties, high impact, high heat resistance, meets the requirements of RoHs and PaHsApplications: E/E applianceInformation Provided by.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL PX1112 PPE+HIPS (Europe-Africa-Middle East) NORYL PX1112 is an unfilled medium heat resistant material. This grade offers improved impact resistance to meet the ECE-dashboard standard. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® V3004 PBT (Asia Pacific) Unfilled PBT modified with elastomer. Targeted for flexible hinge, automotive connectors, film applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Xenoy® X5600WX PC+POLYESTER (Europe-Africa-Middle East) Unreinforced, opaque Polyester+PC alloy. Chemical resistance, dimensional stability and mechanical performance. UV Stabilized. Mold ReleaseThis data was supplied by SABIC-IP for the Europe-Africa-Mi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL PX0844 PPE+PS PPE+PS blend. Unfilled. UL94 HB rated. Low water absorption. Hydrolytic stability. Dimensional stability. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 120 °C | >= 248 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 2122UV-M-31 is a black 40% talc filled polypropylene. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
| A. Schulman PP 3482-01 Polypropylene Nucleated Homopolymer Polypropylene DescriptionPP 3482 is a nucleated homopolymer polypropylene with excellent heat resistance and stiffness properties.ApplicationThis product is for injection molded applications and is in compliance .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 120 °C | >= 248 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 2122UV-M-31 is a black 40% talc filled polypropylene. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
| A. Schulman PP 3369-01 Polypropylene Medium-Flow Homopolymer Polypropylene DescriptionPolypropylene PP 3369-01 is a medium-flow homopolymer polypropylene nucleated and anti-static designed for the molding of thin walled, and large parts.ApplicationTypical applications of P.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | |
| Covestro Bayblend® KU 2-1474 Polycarbonate/ABS Blend Easier flowing than BAYBLEND T 64.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® XE 4188 black 9992 PA612 Product description: Grilamid XE 4188 black 9992 is a high viscosity, unreinforced, impact resistant polyamide 612 (PA612) extrusion grade. Unique features of Grilamid XE 4188 black 9992 are: High v.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® LC6601 NC010 Nylon 612 Plasticized Toughened Polyamide 612 Developed for Extrusion Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0334T30L Talc Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ASTM D648 |
| Cheng Yu Plastic C1300 PC/ABS |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75 |
| Polyram RamLloy A001 Nylon 66/Polyethylene Alloy for Injection Molding, Impact Modified Nylon 66/PE Alloy, reduction of water absorption, impact modified, for injection molding applications.Information provided by Polyram. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75 |
| Polyram RamOfin PPC350M6 Polypropylene, 30% Mineral Filled 30% Mineral filled, heat stabilized polypropylene for injection molding applications.Information provided by Polyram. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRILOY Z20001 PPO LNP* Lubriloy* Z20001 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Flame Retardant. |
|||