- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 239 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 239 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PP HGX500707 Polypropylene, Multifiller Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 3.20 mm |
239 °F @Thickness 0.126 in |
ASTM D648 |
| Covestro Bayblend® 2753 Polycarbonate + ABS Blend, Automotive
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| LG Chemical LUMAX HF-5306F High Flow PBT, 30% Polymer Alloy, Weather Resistant, Flame Retardant LUMAX resins are a family of thermoplastic blends of polybutyleneterephthalate(PBT) and styrenic resins that combine the most desirable properties of both resins and fillers. They offer high heat r.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 3.20 mm |
239 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOL EI5002 PP Description: Injection Molding, PP, General PurposeApplication: Automotive Interior PartsCAS: 9003-07-0, 9010-79-1 and 9002-88-4Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 6.40 mm |
239 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOL TE5109 PP+Rubber+MF, High Impact Description: Injection Molding, PP+Rubber+MF, High Impact, Good WeatherabilityApplication: Automotive Exterior (Bumper Fascia, Rear Bumper Step)Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 3.20 mm |
239 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL WCV065 PPE+Polyolefin Flexible, non-halogenated FR, PPE+Polyolefin resin designed for evaluation in Automotive ISO6722 Class A-C applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 3.20 mm |
239 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP ML004 PP LNP* LUBRICOMP* ML004 is a product based on Polypropylene containing 20% PTFE. Added features of this grade include: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 3.20 mm |
239 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP NL001 PC+ABS LNP LUBRICOMP* NL001 is a compound b ased on PC+ABS resin containing 5% PTFE. Added features include: Wear Resistant, Suitable for Thin Wall Applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP WI001 PBT (Europe-Africa-Middle East) LNP* LUBRICOMP* WI001 is a compound based on Polybutylene Terephalate resin containing Silicone. Added features include; Inernally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| SCG Chemicals EL-Proâ„¢ P702J Polypropylene Injection Molding Key Characteristics:High clarityHigh stiffnessGood processabilityMicrowavable for cooking applicationsOdorlessSafe for food contactRecommended Applications:General purpose injection parts that requi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene DescriptionPolyfort® FXP 2779U is a 20% talc-filled, UV stabilized copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-2 |
| Borealis HG385MO Polypropylene HG385MO is a polypropylene homopolymer intended for injection molding. This grade combines unique Borstar® reactor design with Borstar® nucleation technology to produce highly-crystalline polyprop.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-2 |
| Borealis ME266U Polypropylene Compound, Mineral Filled ME266U is a 20% mineral filled polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and gives a good surface quality. .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1182 Talc Fortified Impact Resistant Polypropylene DescriptionPolyfort® FPP 1182 is a 20% talc fortified impact resistant polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 115 °C | >= 239 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 2121UV-M-31 Black Filled Polypropylene Homopolymer DescriptionPolyfort® FPP 2121UV-M-31 is a 30% black filled polypropylene homopolymer. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® 2D 25 W 20 X black PA612-I Product Description: Grilamid 2D 25 W 20 X black 9992 is a semi-flexible high viscosity, plasticized, high impact, heat and UV resistant extrusion grade based on polyamide 612 (PA612). Unique proper.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® GTR 45 PA6I/6T Product description: Grivory GTR 45 is a transparent engineering thermoplastic based on amorphous, partially aromatic copolyamide for injection molding. Compared to other semi crystalline polyamides.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® L 25H FWA nat PA12 Product Description: Grilamid L 25 H FWA natural is a highviscosity, unreinforced and heat stabilized Polyamide 12 (PA12). Grilamid L 25 H FWA natural is designed for technical injection moulded com.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® XE 3817 black 9992 PA12 Product description: Grilamid XE 3817 black 9992 is a medium viscosity, heat and UV-stabilized Polyamid 12. Grilamid XE 3817 black 9992 is especially suitable for the coating of metal tubes and offe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® FG6130 NC010 Polybutylene Terephthalate (PBT)
(Unverified Data**)< Unreinforced High Viscosity Polybutylene Terephthalate Developed for Food Contact Applications and Extrusion and Injection Molding Crastin FG6130 NC010 is an unreinforced medium high viscosity polyb.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® L 20H FWA nat PA12 Product Description: Grilamid L 20 H FWA natural is a medium viscosity, unreinforced and heat stabilized Polyamide 12 (PA12). Grilamid L 20 H FWA natural is used for technical injection molded parts.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0336W20L1 Wollastonite Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0339C30L Calcium Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | |
| BASF Procom® D 1188 Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| Aaron Industries AAROPRENE® TFIPP 2020 High Impact Talc Filled Polypropylene AAROPRENE® TFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH TS3020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | |
| BASF Procom® D 1026 Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL PX2355 PPE+HIPS (Europe-Africa-Middle East) NORYL PX2355 is an unfilled, medium heat, low odour and low emission material with excellent heat aging performance. It has been developed for automotive interior applications, such as instrument pa.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| Aclo Accutech TPO TPO030T9V Paintable Grade Approved to Suzuki Spec Black B14257 |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene DescriptionPolyfort® FXP 2779U is a 20% talc-filled, UV stabilized copolymer polypropylene.Information provided by A. Schulman. |
|||