Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ASTM D648 |
Mytex Polymers AS14KW-02 Polypropylene, Talc filled, Compounded Description: Talc filled compounded polypropylene produced for automotive interior applications using Mytex® Technology.Key Applications: General purpose interiorInformation provided by Mytex Polym.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYfill PP CCP20020 UV Polypropylene, Mineral Reinforced, UV stabilized Information provided by Polykemi AB |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | 120°C/h; ISO 75/1 |
Polykemi AB POLYfill PPH GK8020D Polypropylene Homopolymer, Glass Reinforced, Detergent Resistant Information provided by Polykemi AB |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | Unannealed; ASTM D648 |
LNP Stat-Kon® PDX-S-90398 Polyamide 12, Stainless Steel Fiber
(discontinued **) Features: Electrically ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ASTM D648 |
Ineos H02C-01 Polypropylene Homopolymer This is a low flow rate, high clarity homopolymer designed for extrusion, thermoforming, blow molding, and rigid packaging. Applications that require good see-through clarity combined with good hea.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C @Thickness 6.40 mm |
237 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
LG Chemical XR409HJ ABS, Heat Resistance, Curl Fit Feature: Injection Molding, Heat Resistance, Curl FitApplication: Automotives Interior & Exterior Housing (P/W Switch Housing Etc)CAS No. 25120-20-1, 9003-56-9 and 25747-74-7Information provided by .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ASTM D648-97 |
Ipiranga Petrochem PH 0242 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ISO 75-1,-2 |
Ineos ABS Lustran® Ultra 4115 ABS Pellets (a-methylstyrene-SAN / PC-modified), Very High Heat Grade Lustran® Ultra 4115 is very high heat grade with high impact resistance and is PC-modified. It is used for the production of molded plastic articles. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP LUBRICOMP NL001 PC+ABS LNP LUBRICOMP* NL001 is a compound b ased on PC+ABS resin containing 5% PTFE. Added features include: Wear Resistant, Suitable for Thin Wall Applications. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | 80*10*4mm, Cut; ISO 75-1&2 |
SABIC Innovative Plastics SABIC PPCOMPOUND 7727 PP SABIC® PPcompound 7727 is a mineral filled, impact modified polypropylene TPO. This material combines impact resistance, heat stability, and is used in injection molded applications. The IMDS ID.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP STAT-KON FX98501 PE LNP* STAT-KON* FX98501 is a compound based on Polyethylene resin containing Proprietary Fillers. Added feature of this material is: Electrically Conductive. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics Xenoy® X3515 PC+POLYESTER (Asia Pacific) Flame Retardant, Impact Modified, Opaque, Designed for outdoor telecommunication enclosure applications.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics Xenoy® X3515 PC+POLYESTER (Europe-Africa-Middle East) Flame Retardant, Impact Modified, Opaque, Designed for outdoor telecommunication enclosure applications.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
SABIC Innovative Plastics NORYL PPX PPX7115 PPE+PP (Europe-Africa-Middle East) High modulus/impact/heat PPE+PP. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
SABIC Innovative Plastics LNP STAT-KON 9X02785 PC LNP STAT-KON* 9X02785 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3052UX Impact Resistant Copolymer DescriptionPolyfort® PP 3052UX is a UV stabilized extra high flow impact resistant copolymer with a relatively high stiffness.Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3052UX Impact Resistant Copolymer DescriptionPolyfort® PP 3052UX is a UV stabilized extra high flow impact resistant copolymer with a relatively high stiffness.Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3052UX Impact Resistant Copolymer DescriptionPolyfort® PP 3052UX is a UV stabilized extra high flow impact resistant copolymer with a relatively high stiffness.Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | 120°C per hour; ISO 752 |
Total PPC 10641 Polypropylene, Heterophasic Copolymer, Injection Molding Polypropylene PPC 10641 is a nucleated antistatic heterophasic copolymer with high Melt Flow index of 44 g/10 min.Polypropylene PPC 10641 is characterized by high fluidity with good mechanical prope.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | 120°C per hour; ISO 752 |
Total PPC 10642 Polypropylene, Heterophasic Copolymer, Injection Molding Polypropylene PPC 10642 is a nucleated antistatic heterophasic copolymer with high Melt Flow index of 44 g/10 min.Polypropylene PPC 10642 is characterized by high fluidity with good mechanical prope.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ASTM D648 |
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3052UX Impact Resistant Copolymer DescriptionPolyfort® PP 3052UX is a UV stabilized extra high flow impact resistant copolymer with a relatively high stiffness.Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | Unannealed; ASTM D648 |
ExxonMobil AP3N Polypropylene Impact Copolymer Product Description: A medium impact copolymer resin designed for appliance applications requiring good stiffness and fast cycle time.Availability: Asia Pacific Features:Fast Molding CycleHigh Glos.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ASTM D648 |
Aclo Accutech Polypropylene Homopolymer HP0339W20L Wollastonite Reinforced |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | 90 Minute UV Cure + Thermal; ASTM D648 |
3D Systems Accura® SI 40 Plastic for the SLA® 500 System Accura 40 "Ar" or "Hc" type materials - for the SLA 500 system. Mimics Nylon 6:6ApplicationsHigh temperature testing:Under hood bolt-on testingWind tunnel testingHVAC testingPrototyping and testing .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ASTM D648 |
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ISO 75-2 |
Borealis Xmod™ MC55T1 Polypropylene Compound 10% Mineral Filled Xmod MC55t1 is a 10% mineral filled grade based on HCPP intended for injection molding. Xmod has been developed especially for the car industry, to be used in interior parts. XMod offers very good .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C @Thickness 6.40 mm |
237 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
LG Chemical LUPOY NS5000C PC/ABS, High Impact Description: Injection Molding, PC/ABS, Heat Resistance, High Flow, High ImpactApplication: Automotive (Interior)CAS: 103598-77-2 and 9003-56-9Information provided by LG Chemical |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ASTM D648 |
A. Schulman POLYFLAM™ E-15086-1B Mineral Impact Modified, Low Warp Polypropylene Black DescriptionPolyfort® E-15086-1B is a mineral impact modified low warp polypropylene black.Information provided by A. Schulman. |