- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 78.0 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 78.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | ISO 75-1 |
| Mytex Polymers 8224LW Polypropylene, Non-filled, Compounded Description: Mytex® 8224LW is a non-filled compounded polypropylene produced for automotive applications.Key Applications: Automotive exteriorInformation provided by Mytex Polymers |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Network Polymers MS 175 Styrene Methyl Methacrylate Terpolymer Description: Styrene Methyl Methacrylate TerpolymerInformation provided by Network Polymers Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | Method A; ASTM D648 |
| Polymer Industries Densetec HMW Sheet Polymer Industries’ Densetec HMW is the extruded material needed when Densetec HDPE is not enough and Polyslick UHMW™ is not necessary. Densetec HMW has higher impact strength than HDPE and is mor.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | unannealed; ASTM D648 |
| Phillips 66 COPYLENE® CR750CL-02 Polypropylene, Random Copolymer, NX-8000 based COPYLENE™ CR750CL-02 is an easy molding, high melt flow random copolymer that has good see-through and contact clarity in injection molding applications and is formulated with advanced technology. .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | |
| Eastman Eastar DN102 PCTG Copolyester
(discontinued **) ISO data as provided by the manufacturer, Eastman Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | ISO 75 |
| Solvay Engineered Polymers SEQUEL® 2322 Engineered Polyolefin
(discontinued **) SEQUEL® 2322 engineered polyolefin is designed for mold-in-color automotive interior applications that require medium stiffness and good dimensional stability. This material exhibits excellent low.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | ASTM D648 |
| SABIC PP 623B Polypropylene Random Co-polymer for Cast Film Product Description: PP 623B is a PP Random Copolymer grade specially designed for Cast PP (CPP) film extrusion. It contains slip agent and anti-block additives. PP 623B offers good heat weldabil.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | Unannealed; ASTM Data |
| Americas Styrenics Styron® 6010 High Impact Polystyrene
(discontinued **) STYRON® 6010 resin is a high impact polystyrene grade with a proprietary ignition resistance additive package to achieve a UL 94 V-0 rating. It offers high heat resistance, high modulus, good impac.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | ASTM D648 |
| Chevron Phillips HiD® 9402 HDPE Blow Molding Resin
(discontinued **) Resin Type: Linear Homopolymer; Blow Molding, Sheeting and Profile ResinCharacteristics: High Melt Strength - Larger Parts, Wide Range of Processing Conditions, High Stiffness and Impact Resistance,.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | ASTM D648 |
| Chevron Phillips HiD® 99416 with Food Grade Antistat HDPE Blow Molding Resin
(discontinued **) Resin Type: Linear Homopolymer; Blow Molding, Sheeting & Profile Extrusion ResinCharacteristics: High Stiffness, Good Impact Resistance, Very Low Odor & Taste Transfer, Designated for Uniloy Blowmol.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | ASTM D648 |
| LyondellBasell Petrothene® LM600500 High Density Polyethylene ApplicationsPETROTHENE LM 6005-00 resin is especially designed for water, milk, and juice bottles. It exhibits excellent rigidity and good processability.Regulatory StatusLM 6005-00 meets the requi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | ASTM D648 |
| Flint Hills AP7810-HS Polypropylene Ultra High Impact Copolymer Features: Excellent stiffness and low temperature ductility.Applications: Injection Molding: Automotive interior energy management solutionsInformation Provided by Flint Hills Resources |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C @Thickness 3.20 mm |
172 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOL HI5302A PP+MF15%, High Impact Description: Injection Molding, PP+MF15%, High Impact, Good WeatherabilityApplication: Automotive Interior PartsCAS: 9003-07-0, 9010-79-1 and 14807-96-6Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | ISO 75 |
| IPB Bicell® Cellular Polypropylene Sheet Extruded, layered PP sheet, with a cellular core layer. Attributes include:Enhanced strength/thickness ratioOmni-directional flexural stresistanceHigh compression strengthWide variety of finishesRe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | ASTM D648 |
| Lavergne VYSTYRENE PS 3904 High Impact Polystyrene Vystyrene PS 3904 is a black impact modified polystyrene compound with balanced impact/stiffness properties designed for injection molding applicationsFeatures: -High resilience -Excellent process.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | unannealed; ASTM D648 |
| Lendell Parapet GR-00100 PMMA, High Impact |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C @Thickness 3.20 mm |
172 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-LOY A3000LTH ABS LNP* STAT-LOY* A3000LTH is a compound based on ABS resin. Added features of this material include: Transparent, Antistatic, Formulation Locked. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C @Thickness 3.20 mm |
172 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-LOY A3000TXB ABS LNP* STAT-LOY* A3000TXB is a compound based on ABS resin. Added features of this material include: Antistatic, Transparent, Formulated with FDA Food Contact Additives and Bioassessed to ISO 10993... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | ISO 75-2 |
| Borealis BL2571 High Density Polyethylene BL2571 is a high-density polyethylene with high stiffness and high environmental stress crack resistance. This product is intended for blow molding. Applications: household and chemical containers.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | Unannealed; ASTM Data |
| Dow Prevail® 3150 ABS + Polyurethane PREVAIL® 3150 thermoplastic resin offers designers and manufacturers a combination of flexibility and low temperature toughness not previously available in an engineering thermoplastic and is used .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | Unannealed; ISO 75-2/B |
| Dow T702-12N Polypropylene Impact Copolymer Resin Dow Announced Sale of Global Polypropylene Business to Braskem in July 2011. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | |
| BASF Novolen® 2500 MC Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | |
| BASF Novolen® 2600 PC Polypropylene, Injection Molding Grade Injection molded partsData was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | |
| BASF Novolen® 2600 TC Polypropylene, Injection Molding Grade Injection molded partsData was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | |
| BASF Polystyrol® 432 B Impact Grade Polystyrene (Europe) Very easy-flowing, low impact grade for parts with unfavorable flow path/wall-thickness ratios.Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | |
| BASF Polystyrol® 455 F WU Impact Grade Polystyrene (Europe) Very easy-flowing, impact-modified grade.Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | ASTM D648 |
| Cheng Yu Plastic IPS610BK Electric Conducting HIPS, Extrusion |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | Annealed; ISO 75-2A |
| Total Lacqrene® 6630 Impact Polystyrene
(discontinued **) LACQRENE® 6630 and 6631 are easy flowing, high impact polystyrenes for injection molding. With easy processing, good rigidity and ease of coloration. These grades find a wide range of application.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | Annealed; ISO 75-2A |
| Total Lacqrene® 6631 Impact Polystyrene
(discontinued **) LACQRENE® 6630 and 6631 are easy flowing, high impact polystyrenes for injection molding. With easy processing, good rigidity and ease of coloration. These grades find a wide range of application.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 - 98.0 °C | 172 - 208 °F | Average value: 87.8 °C Grade Count:12 |
| Overview of materials for Acrylic, Impact Modified, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Impact Modified, Molded". Each property range of values reported is minimum and maximum values .. |
|||