Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 42.0 °C | 108 °F | ASTM D648 |
NOVA Chemicals Sclair® 8107 UV8D Butene LLDPE Rotational Molding Resin Excellent ESCR, Excellent low temperature impact properties, Excellent low shrinkage and warpage properties, Very good processability, UL 94-HB listedApplications: Food and laundry materials handlin.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 42.0 °C | 108 °F | ASTM D648 |
NOVA Chemicals Sclair® 8107G UV8D Butene LLDPE Rotational Molding Resin Excellent ESCR, Excellent low temperature impact properties, Excellent low shrinkage and warpage properties, Very good processability, UL 94-HB listedApplications: Food and laundry materials handlin.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 42.0 °C | 108 °F | ASTM D648 |
LyondellBasell Petrothene® NA940000 Low Density Polyethylene (Blow Molding) ApplicationsPETROTHENE NA 940-000 is a low density homopolymer resin intended for use in blow molding applications. Excellent toughness, good clarity and processability make NA 940-000 an ideal cho.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 42.0 °C @Thickness 3.20 mm |
108 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP LUBRICOMP PDXF89080 PE LNP* LUBRICOMP* PDXF89080 is a compound based on Polyethylene containing Proprietary Fillers. Added feature of this grade is: Wear Resistant. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 42.0 °C | 108 °F | ASTM D648 |
DuPont™ Surlyn® 8660 Ionomer Resin, Sodium Surlyn® 8660 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. The amount of MAA and neu.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 42.0 °C | 108 °F | ASTM D648 |
DuPont™ Surlyn® 9520 Ionomer Resin, Zinc Surlyn® 9520 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 42.0 °C | 108 °F | ASTM D648 |
Arkema Group Pebax® 2533 Polyether Block Amide (PEBA) Information provided by Arkema Group |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 42.0 °C | 108 °F | |
Arkema Group Pebax® 2533 SN 01 Polyether Block Amide (PEBA) (Conditioned) POLYETHER BLOCK AMIDE (PEBA) hardness 25 shore D Non plasticized flexible Polyamide Outstanding mechanical properties at low temperature (-40°C) Applications: molded parts for sport goods (softness.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 42.0 - 57.2 °C | 108 - 135 °F | Average value: 48.9 °C Grade Count:11 |
Overview of materials for Linear Low Density Polyethylene (LLDPE), Injection Molded This property data is a summary of similar materials in the MatWeb database for the category "Linear Low Density Polyethylene (LLDPE), Injection Molded". Each property range of values reported is mi.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 42.0 - 106 °C | 108 - 223 °F | Average value: 72.4 °C Grade Count:25 |
Overview of materials for Polyether Block Amide (PEBA) This property data is a summary of similar materials in the MatWeb database for the category "Polyether Block Amide (PEBA)". Each property range of values reported is minimum and maximum values of a.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 42.0 °C | 108 °F | ASTM D648 |
LATI LATISTAT 48/9900-03 Ethylene Vinyl Acetate (EVA) Base Conductive Plastic
(Unverified Data**) Description: Latistat materials have low specific resistivity. They feature partial electrical conductivity. Selected functional additives give materials with low specific resistivity and reasonable.. |