- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 115 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 115 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 3.20 mm |
239 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® C1000HF PC+ABS (Asia Pacific) High flow PC+ABS. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYblend 65V PC/ABS-Blend, Flame Retardant Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 3.20 mm |
239 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CX1440 PC+ABS CYCOLOY CX1440 is a general purpose PC+ABS blend specially developped for thin wall applications requiring weld line strength and high flow with a good balance of properties |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| PolyMirae Moplen EP540S Injection Molding Grade Polypropylene Moplen EP540S is the polypropylene block copolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen EP540S is a block copolymer particularly suitable for injection.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP FARADEX NS003 PC+ABS (Europe-Africa-Middle East) LNP* Faradex* NS003 is a compound based on PC+ABS Blend resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® 6134 NC010 PBT
(Unverified Data**) Crastin® 6134 NC010 is an unreinforced, medium viscosity polybutylene terephthalate resin for extrusion and injection molding.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® S600F40 NC010 PBT
(Unverified Data**) Crastin® S600F40 NC010 is an unreinforced, lubricated, low viscosity polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | unannealed; ASTM D648 |
| Dow INSPIRE™ TF2300 Thermoplastic Polyolefin
(discontinued **) Information provided by DowThe Inspire brand was spun off from Dow Chemical to Styron in 2010, although this grade had previously been removed from Dow's standard product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| Ineos H53N-00 Polypropylene Homopolymer This is a high flow rate nucleated and lightly lubricated homopolymer polypropylene designed for high-speed injection molding of thin-walled parts requiring good stiffness and fast cycle times. Thi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 2-1000 Polypropylene Block-Copolymer INNOPOL® CS 2-1000 is a polypropylene block-copolymer compound. This grade is available in natural and custom colored form.INNOPOL® CS 2-1000 is developed for producing injection molded automo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 - 120 °C | 239 - 248 °F | ASTM D1525, HDT Method B |
| Loxim 841 02T HB Polypropylene Compound, 40% Talc Filled, Flame Retardant Information provided by Loxim Industries |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL SE0 PPE+HIPS (Europe-Africa-Middle East) NORYL SE0 is an unfilled, flame retardant material with a Vicat B/120 of 130C according ISO 306. NORYL SE0 is V0 at 1.6 mm according UL94 and halogen free according VDE/DIN 472 part 815. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75 |
| Teijin Multilon T-3713 Standard PC/ABS Polymer Alloy General grade of PC/ABS polymer alloy, having improved impact strength and heat resistance compared with a heat resistant ABS and flame retardant m-PPE and also having higher flowability compared wi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene DescriptionPolyfort® FXP 2779U is a 20% talc-filled, UV stabilized copolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 115 °C | >= 239 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 2121UV-M-31 Black Filled Polypropylene Homopolymer DescriptionPolyfort® FPP 2121UV-M-31 is a 30% black filled polypropylene homopolymer. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| Formosa Plastics Formolene® 2306N Impact Copolymer Polypropylene Impact Copolymer for Compression and Injection Molded Caps and Closures Formolene® 2306N is a polypropylene copolymer formulated for compression and injection molded cap applications. It was create.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | GB1634 |
| Zhejiang Juner JEPP2007 PP For Automotive Parts Applications: Inner Decorate PartsInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 115 °C | >= 239 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 2121UV-M-31 Black Filled Polypropylene Homopolymer DescriptionPolyfort® FPP 2121UV-M-31 is a 30% black filled polypropylene homopolymer. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | pressure unspecified; ASTM D648 |
| Total PPC 4481WZ Polypropylene, Impact Copolymer TOTAL Petrochemicals Polypropylene 4481WZ is a nucleated impact copolymer with a Melt Flow index of 4.0 g/10 min.TOTAL Polypropylene 4481WZ is characterized by a good stiffness/impact balance couple.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 115 °C | >= 239 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 2121UV-M-31 Black Filled Polypropylene Homopolymer DescriptionPolyfort® FPP 2121UV-M-31 is a 30% black filled polypropylene homopolymer. It is weather and urethane contact resistant and contains a mold release. Information provided by A. Schulman... |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® 2D 25 W 20 X black PA612-I Product Description: Grilamid 2D 25 W 20 X black 9992 is a semi-flexible high viscosity, plasticized, high impact, heat and UV resistant extrusion grade based on polyamide 612 (PA612). Unique proper.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-2/B |
| ExxonMobil Exxtral™ LNU 012 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin with good heat resistance and good surface finish designed for fast injection molding of large electrical appliance parts.Availability.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| DuPont Performance Polymers Crastin® FGS600F10 NC010 Polybutylene Terephthalate (PBT)
(Unverified Data**) Unreinforced Polybutylene Terephthalate Developed for Food Contact ApplicationsInformation provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | LAB036 |
| ExxonMobil Mytex™ AS65KW-LGDC Talc filled compounded polypropylene produced for automotive interior applicationsInformation provided by ExxonMobil Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| Diamond Polymers NPP25-0604 Impact Copolymer Polypropylene Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | Unannealed; ASTM Data |
| Dow C700-35N Polypropylene Impact Copolymer Dow Polypropylene Impact Copolymer Resins are semi-crystalline thermoplastic materials that can provide a combination of desirable properties and affordability: low density; excellent chemical resis.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0339C30L Calcium Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0339C40L Calcium Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | |
| Asahi Kasei Xyron® AT610 Modified Polyphenylene Ether Applications: Information provided by Asahi Kasei |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C @Thickness 3.20 mm |
239 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CX1440 PC+ABS (Asia Pacific) CYCOLOY CX1440 is a general purpose PC+ABS blend specially developped for thin wall applications requiring weld line strength and high flow with a good balance of properties |
|||