Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 14.5 µm/m-°C @Temperature 0.000 - 900 °C |
8.06 µin/in-°F @Temperature 32.0 - 1650 °F |
|
Kennametal Stellite Stellite® 3 PM with P/M Processing Typical applications include (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) diesel engine exhaust, fluid valve seats, saw cutt.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 21.0 - 427 °C |
8.06 µin/in-°F @Temperature 69.8 - 801 °F |
|
Kennametal Stellite Stellite® 31 PM cast Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 0.000 - 300 °C |
8.06 µin/in-°F @Temperature 32.0 - 572 °F |
|
Kennametal Stellite Stellite® 6 PM cast Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) die.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 0.000 - 300 °C |
8.06 µin/in-°F @Temperature 32.0 - 572 °F |
|
Kennametal Stellite Stellite® 6 PM with P/M Processing Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) die.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 0.000 - 300 °C |
8.06 µin/in-°F @Temperature 32.0 - 572 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 12.7 mm (1/2 in.) thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 0.000 - 300 °C |
8.06 µin/in-°F @Temperature 32.0 - 572 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 0.000 - 300 °C |
8.06 µin/in-°F @Temperature 32.0 - 572 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.7 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 0.000 - 300 °C |
8.06 µin/in-°F @Temperature 32.0 - 572 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 4.8 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 0.000 - 300 °C |
8.06 µin/in-°F @Temperature 32.0 - 572 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 0.000 - 800 °C |
8.06 µin/in-°F @Temperature 32.0 - 1470 °F |
|
Kennametal Stellite Stellite® 6K 12.7 or 22.2 mm plate 13.3 mm^3 volume loss--abrasive wear data. Applications include agitators, augers, ball mills, banbury mills, cams, crusher bearings, dryers, dry presses, dump cars, fans, filters, food machinery, g.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 20.0 - 300 °C |
8.06 µin/in-°F @Temperature 68.0 - 572 °F |
|
Industeel URANUS® 52N+ 25 Cr Super Duplex Stainless Steel with PREN = 40 Description: URANUS® 52N+ (UR 52N+) is a super duplex stainless steel with 25% Cr and a PREN value higher than 40. The minimum guaranteed yield strength is 550 MPa which allows the designer to re.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 25.0 - 500 °C |
8.06 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 25.0 - 500 °C |
8.06 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 25.0 - 500 °C |
8.06 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 25.0 - 500 °C |
8.06 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 25.0 - 500 °C |
8.06 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 25.0 - 500 °C |
8.06 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 25.0 - 500 °C |
8.06 µin/in-°F @Temperature 77.0 - 932 °F |
|
Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 25.0 - 900 °C |
8.06 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed, 20% cold work Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 26.0 - 427 °C |
8.06 µin/in-°F @Temperature 78.8 - 801 °F |
|
Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 26.0 - 427 °C |
8.06 µin/in-°F @Temperature 78.8 - 801 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 26.0 - 427 °C |
8.06 µin/in-°F @Temperature 78.8 - 801 °F |
|
Haynes Ultimet® alloy, all-weld metal, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 26.0 - 427 °C |
8.06 µin/in-°F @Temperature 78.8 - 801 °F |
|
Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 26.0 - 427 °C |
8.06 µin/in-°F @Temperature 78.8 - 801 °F |
|
Haynes Ultimet® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 0.000 - 300 °C |
8.06 µin/in-°F @Temperature 32.0 - 572 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 3.2 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 25.0 - 900 °C |
8.06 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 242® alloy Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 25.0 - 900 °C |
8.06 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 242® alloy, after 4000 hours exposure at 650°C (1200°F) Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 25.0 - 900 °C |
8.06 µin/in-°F @Temperature 77.0 - 1650 °F |
|
Haynes 242® alloy, cold reduced sheet, annealed Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
CTE, linear | 14.5 µm/m-°C @Temperature 0.000 - 100 °C |
8.06 µin/in-°F @Temperature 32.0 - 212 °F |
|
Industeel SIRIUS 800 H Heat Resistant Alloy Description: The SIRIUS® 800, H and H+ grades are three variants of a high chromium and nickel austenitic alloy which combines good corrosion and creep resistance. SIRIUS® 800 is employed at tempe.. |