Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 600 °C |
7.83 µin/in-°F @Temperature 32.0 - 1110 °F |
|
Kennametal Stellite Stellite® 12 PM with P/M Processing Applications: include vane plugs, fuel metering pins, spacer bushings, ball blanks (bearings), race blanks (bearings), diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wea.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 20.0 - 315 °C |
7.83 µin/in-°F @Temperature 68.0 - 599 °F |
|
Kennametal Stellite Stellite® 21 Excellent high temperature strength, high toughness. Solution treat at 1191-1204°C, rapid air cool, age between 538-871°C to increase hardness and strength at the expense of impact and ducti.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6 PM with P/M Processing Adhesive wear test data: 0.49 P/M, 0.48 Cast; Typical applications include: (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) die.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 1.6 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 20.0 - 1000 °C |
7.83 µin/in-°F @Temperature 68.0 - 1830 °F |
|
Kennametal Stellite Stellite® 98M2 with P/M Processing Adhesive wear test data P/M 0.58 Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy sheet Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 10% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 20% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 20% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 40% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 40% cold reduction, 925°C for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 50% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 50% cold reduction, 980°C (1800°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, sheet, 100 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 760°C (1400°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 870°C (1600°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, sheet, 1000 hours exposure at 980°C (1800°F) Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 3.2 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 10% cold reduction, 1095°C (2000°F) for 5 minutes Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 25.0 - 400 °C |
7.83 µin/in-°F @Temperature 77.0 - 752 °F |
|
Haynes 214® alloy, 30% cold reduction Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 21.0 - 316 °C |
7.83 µin/in-°F @Temperature 69.8 - 601 °F |
|
Kennametal Stellite Stellite® 31 PM after P/M processing, aged 8 hours at 802°C air cooled Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 21.0 - 316 °C |
7.83 µin/in-°F @Temperature 69.8 - 601 °F |
|
Kennametal Stellite Stellite® 31 PM cast aged 8 hours at 802°C air cooled Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous we.. |
|||
CTE, linear | 14.1 µm/m-°C @Temperature 0.000 - 200 °C |
7.83 µin/in-°F @Temperature 32.0 - 392 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |