Kennametal Stellite Stellite® 31 PM after P/M processing, aged 8 hours at 802°C air cooled

Category	Metal , Nonferrous Metal , Cobalt Alloy , Superalloy
Manufacturer	Kennametal Stellite
Trade Name	Stellite®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Kennametal Stellite Stellite® 31 PM after P/M processing, aged 8 hours at 802°C air cooled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, miscellaneous wear parts. Data provided by the manufacturer, Deloro Stellite Inc.Product of former Deloro Stellite Inc.

Physical Properties	Metric	English	Comments
Density	8.45 g/cc	0.305 lb/in³	P/M (98%)
	8.61 g/cc	0.311 lb/in³	Theoretical

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1035 MPa	150100 psi
Tensile Strength, Yield	725 MPa @Strain 0.200 %	105000 psi @Strain 0.200 %
Elongation at Break	1.5 %	1.5 %	in 25.4 mm

Thermal Properties	Metric	English
CTE, linear	14.1 µm/m-°C @Temperature 21.0 - 316 °C	7.83 µin/in-°F @Temperature 69.8 - 601 °F
	14.5 µm/m-°C @Temperature 21.0 - 427 °C	8.06 µin/in-°F @Temperature 69.8 - 801 °F
	15.1 µm/m-°C @Temperature 21.0 - 538 °C	8.39 µin/in-°F @Temperature 69.8 - 1000 °F
	15.7 µm/m-°C @Temperature 21.1 - 649 °C	8.72 µin/in-°F @Temperature 70.0 - 1200 °F
	16.5 µm/m-°C @Temperature 21.1 - 816 °C	9.17 µin/in-°F @Temperature 70.0 - 1500 °F
	16.6 µm/m-°C @Temperature 21.1 - 871 °C	9.22 µin/in-°F @Temperature 70.0 - 1600 °F

Component Elements Properties	Metric	English	Comments
Carbon, C	0.50 %	0.50 %
Chromium, Cr	25.5 %	25.5 %
Cobalt, Co	50 %	50 %	As remainder
Iron, Fe	<= 2.0 %	<= 2.0 %
Manganese, Mn	<= 1.0 %	<= 1.0 %
Nickel, Ni	10.5 %	10.5 %
Other	<= 2.0 %	<= 2.0 %
Phosphorous, P	<= 0.040 %	<= 0.040 %
Silicon, Si	<= 1.0 %	<= 1.0 %
Sulfur, S	<= 0.040 %	<= 0.040 %
Tungsten, W	7.5 %	7.5 %