- Polymer Property : CTE, linear = 14.0 µm/m-°C
Polymer Property : CTE, linear = 14.0 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.0 µm/m-°C @Temperature -55.0 - 288 °C |
7.78 µin/in-°F @Temperature -67.0 - 550 °F |
Y-Direction; IPC-TM-650 2.4.41 |
| Rogers Corporation RO4003C Glass-Reinforced Hydrocarbon and Ceramic Laminate with Thin Film Resistor Foil RO4000® Series High Frequency Circuit Materials are glass-reinforced hydrocarbon and ceramic (not PTFE) laminates with TICER™ TCR® Thin Film Resistor Foils. These laminates are designed for perf.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 300 °C |
7.78 µin/in-°F @Temperature 68.0 - 572 °F |
|
| Industeel URANUS® 35N 23.04 Duplex Stainless Steel with PREN = 24 Description: URANUS® 35N (UR 35N) is a 23% Cr, 4% Nickel, Mo free duplex stainless steel (23.04). The alloy UR 35N has similar corrosion resistance properties similar to 316L. Furthermore, its me.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 500 °C |
7.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 230® alloy, 20% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 21.0 - 649 °C |
7.78 µin/in-°F @Temperature 69.8 - 1200 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 21.0 - 649 °C |
7.78 µin/in-°F @Temperature 69.8 - 1200 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 21.0 - 649 °C |
7.78 µin/in-°F @Temperature 69.8 - 1200 °F |
|
| Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 315 °C |
7.78 µin/in-°F @Temperature 77.0 - 599 °F |
|
| Haynes HR-160® alloy, plate, aged 4000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 26.0 - 316 °C |
7.78 µin/in-°F @Temperature 78.8 - 601 °F |
|
| Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 26.0 - 316 °C |
7.78 µin/in-°F @Temperature 78.8 - 601 °F |
|
| Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 500 °C |
7.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 230® alloy, plate, 8000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 800 °C |
7.78 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 800 °C |
7.78 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 40% cold work, aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 315 °C |
7.78 µin/in-°F @Temperature 77.0 - 599 °F |
|
| Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 21.0 - 300 °C |
7.78 µin/in-°F @Temperature 69.8 - 572 °F |
Mean; aged |
| Special Metals DURANICKEL® 301 (UNS N03301) Spring Wire Tensile strength (ultimate) and elongation values reported here are typical for Spring Wire specifically. Other property values are typical of annealed DURANICKEL® alloy 301 or the alloy in gener.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 21.0 - 300 °C |
7.78 µin/in-°F @Temperature 69.8 - 572 °F |
Mean |
| Special Metals DURANICKEL® 301 (UNS N03301) Spring Wire, Aged Tensile strength (ultimate) and elongation values reported here are typical for Spring Wire, Aged specifically. Other property values are typical of aged DURANICKEL® alloy 301 or the alloy in gen.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 540 °C |
7.78 µin/in-°F @Temperature 68.0 - 1000 °F |
|
| Crucible Steel AIRKOOL® (AISI A2) Tool Steel Airkool (AISI A2) is an air-hardening medium alloy tool steel which is heat treatable to HRC 60-62. It has wear resistance intermediate between the oil hardening tool steels (O1) and the high carbon.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 500 °C |
7.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Aged 732°C (1350°F)/4hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 500 °C |
7.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Aged 732°C (1350°F)/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 500 °C |
7.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Double Aged 718°C (1325°F)/8hr/AC to 621°C (1150°F)/8hr/AC Data provided by Carpenter Technology Corporation.Custom Age 625 PLUS® alloy is a precipitation hardenable, nickel-base alloy which, in many environments, displays corrosion resistance similar to t.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 500 °C |
7.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 25.0 - 500 °C |
7.78 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 21.0 - 649 °C |
7.78 µin/in-°F @Temperature 69.8 - 1200 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 14.0 µm/m-°C @Temperature 20.0 - 500 °C |
7.78 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Kennametal Stellite Stellite® 4 Cobalt Chromium Alloy The higher tungsten content of Stellite alloy 4 gives improved high temperature properties and an increase in abrasive wear resistance over Stellite alloy 6, but not as good as Stellite alloy 12 or .. |
|||