- Polymer Property : CTE, linear = 13.2 µm/m-°C
Polymer Property : CTE, linear = 13.2 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.2 µm/m-°C @Temperature 0.000 - 700 °C |
7.33 µin/in-°F @Temperature 32.0 - 1290 °F |
|
| Kennametal Stellite Stellite® STAR with P/M Processing Applications: Vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw cutter inserts, wear pads, pins, balls, hardfa.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 500 °C |
7.33 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Alloy 625/ Alloy 718 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Multimet alloy 12.7 mm plate weldment Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Type 304 Stainless steel 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 500 °C |
7.33 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Type 304 Stainless steel 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Haynes Hastelloy® W alloy, gas metal arc welds, as-welded Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Haynes Hastelloy® W alloy, gas tungsten arc welds, aged 1000 hours at 650°C (1200°F) Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Haynes Hastelloy® W alloy, shielded metal arc welds, aged 1000 hours at 650°C (1200°F) Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 500 °C |
7.33 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Haynes Hastelloy® W alloy, shielded metal arc welds, as-welded Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 300 °C |
7.33 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes Excellent high temperature strength and very good resistance to oxidizing environments up to 1095°C for prolonged exposure, and excellent resistance to sulfate deposit hot corrosion. Readily fabr.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 500 °C |
7.33 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Haynes Hastelloy® alloy 188 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Haynes Hastelloy® alloy 718 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Haynes Hastelloy® alloy X 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 500 °C |
7.33 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Haynes Hastelloy® alloy X 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.33 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 25.0 - 500 °C |
7.33 µin/in-°F @Temperature 77.0 - 932 °F |
|
| Haynes Hastelloy® C-2000® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 21.0 - 300 °C |
7.33 µin/in-°F @Temperature 69.8 - 572 °F |
|
| Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2075°F (1135°C) Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 23.9 - 427 °C |
7.33 µin/in-°F @Temperature 75.0 - 800 °F |
|
| HP Alloys Alloy C-276, 10% Cold Worked 10% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes Internati.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 400 °C |
7.33 µin/in-°F @Temperature 752 °F |
|
| Bohler-Uddeholm BÖHLER M261 Extra Plastic Lens Mold Steel VACUUM ARC REMELTED HARDENED AND TEMPERED PLASTIC LENS MOLD STEELBOHLER M261 follow current trends in tool and die-making:Excellent machinability coupled with higher hardnessGood dimensional stabili.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 700 °C |
7.33 µin/in-°F @Temperature 68.0 - 1290 °F |
|
| Bohler-Uddeholm BÖHLER W302 SUPERIOR® Premium H13 Tool Steel A premium grade H13 hot work tool steel featuring:Very good toughness properties meeting the requirements of NADCA 207-97, and the superior quality levels of NADCA 207-2003Very good heat checking re.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 700 °C |
7.33 µin/in-°F @Temperature 68.0 - 1290 °F |
|
| Bohler-Uddeholm BÖHLER W403 VMR® Hot Work Tool Steel W403 VMR is a modified hot work alloy with an excellent combination of hot tensile properties and toughness. The balanced properties of this grade are not only due to chemistry modification, but to .. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Assab Steels HOTVAR Hot Work Steel HOTVAR is a high performance molybdenum-vanadium alloyed hot-work tool steel which is characterized by:High hot wear resistanceVery good high temperature propertiesHigh resistance to thermal fatigue.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| Bohler-Uddeholm BÖHLER W360 ISOBLOC® Hot Work Tool Steel BÖHLER W360 ISOBLOC was developed as a tool steel for dies and punches in warm and hot forging. The steel can be used for a variety of applications where hardness and toughness are required. Prope.. |
|||
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 500 °C |
7.33 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Haynes Hastelloy® alloy 625 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||