Thermal Properties | Metric | English | Comments |
---|---|---|---|
Glass Transition Temp, Tg | 20.0 °C | 68.0 °F | |
Mallard Creek Polymers Rovene® 6025 Styrene-Acrylic Emulsion Applications: Rovene® 6025 can be used in multiple coating and paint applications including landscaping coatings and low sheen interior flat wall coatings. It can also be used as a binder for dus.. |
|||
Glass Transition Temp, Tg | 20.0 °C | 68.0 °F | |
Mallard Creek Polymers Rovene® 6102 Resin Supported Emulsion Rovene® 6102 is a hard, film forming vehicle with a moderately low glass transition temperature (Tg) for flexographic and gravure inks and overprint varnishes, that exhibits good water resistance.. |
|||
Glass Transition Temp, Tg | 20.0 °C | 68.0 °F | |
Mallard Creek Polymers Rovene® 6112 Resin Supported Emulsion Rovene® 6112 is a hard, film forming, low glycol ether and VOC vehicle with a moderately low glass transition temperature for flexographic and gravure inks and overprint varnishes. Rovene® 611.. |
|||
Glass Transition Temp, Tg | 20.0 °C | 68.0 °F | |
Mallard Creek Polymers Rovene® 6126 Styrene-Acrylic Emulsion Applications: Rovene® 6126 provides a flexible yet strong cohesive bond for a range of materials and particle surface areas. Rovene® 6126 imparts films with good water resistance properties. F.. |
|||
Glass Transition Temp, Tg | 20.0 °C | 68.0 °F | |
Mallard Creek Polymers Tykote® 6152 Styrene-Acrylic Emulsion Tykote® 6152 is a hard film forming styrene-acrylic emulsion designed for oil and grease resistant barrier coatings. This product also provides excellent water and blocking resistance in barrier .. |
|||
Glass Transition Temp, Tg | 20.0 °C | 68.0 °F | |
Lucite International Elvacite ® 2044 Acrylic Resin Elvacite® 2044 is a high molecular weight n-butyl methacrylate polymer. Elvacite® 2044 is useful in adhesives for smooth plastic films and aluminum, and in silk screen inks. It will plasticize.. |
|||
Glass Transition Temp, Tg | 20.0 °C | 68.0 °F | |
Styron XZ 97212.00 Functionalized SB Performance Features: High stiffness, high mechanical stability, self cross-linking, low HCHO applicationsApplications: Fiber Binding, Glass Fiber Binding and NonwovensEuropeInformation provided by .. |
|||
Glass Transition Temp, Tg | 20.0 °C | 68.0 °F | Ultimate Tg |
Tra-Con Tra-Duct 926H01 Information provided by Tra-Con Inc. |
|||
Glass Transition Temp, Tg | >= 20.0 °C | >= 68.0 °F | Dynamic Cure 20—200°C /ISO 25 Min; Ramp -10—200°C @ 20°C/Min |
Epoxy Technology EPO-TEK® EE165-3 Silver Filled Epoxy A two component, silver-filled, electrically conductive epoxy made for bonding of SMDs, and general solder replacement at the PCB level and circuit assembly. It was designed to be low modulus and f.. |
|||
Glass Transition Temp, Tg | >= 20.0 °C | >= 68.0 °F | Dynamic Cure 20—200°C /ISO 25 Min; Ramp -10—200°C @ 20°C/Min |
Epoxy Technology EPO-TEK® H20F Electrically Conductive, Flexible Epoxy Product Description: EPO-TEK® H20F is a two component, flexible silver epoxy. It was designed for flexible type circuitry, such as switching circuits in a flexible panel system, as well as large di.. |
|||
Glass Transition Temp, Tg | 20.0 °C | 68.0 °F | Mid-Point |
3M Scotch-Weld™ DP190 Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP190 Gray is a 1:1 mix ratio similar to Scotch-Weld™ Epoxy Adhesive 2216 B/A Gray and exhibits good peel, shear and environmental aging properties.Information pro.. |
|||
Glass Transition Temp, Tg | 20.0 °C | 68.0 °F | TM R050-25 |
Resinlab® EP1026R Rubber Modified Epoxy Adhesive Resinlab™ EP1026R is a two part unfilled rubber modified epoxy adhesive designed for high speed bonding of metals, ceramics, and most plastics. It cures to a tough semi-rigid material, and is free .. |
|||
Glass Transition Temp, Tg | 20.0 °C | 68.0 °F | |
Loctite® Durabond® E-00CL Epoxy Adhesive Epoxy AdhesivesLoctite offers a complete line of one-part and two-part epoxy and urethane adhesives for structural bonding, potting and encapsulating. The Loctite® Durabond® line contains 14 appli.. |
|||
Glass Transition Temp, Tg | 20.0 °C | 68.0 °F | |
Loctite® Durabond® E-00NS Epoxy Adhesive Epoxy AdhesivesLoctite offers a complete line of one-part and two-part epoxy and urethane adhesives for structural bonding, potting and encapsulating. The Loctite® Durabond® line contains 14 appli.. |
|||
Glass Transition Temp, Tg | 20.0 °C | 68.0 °F | for homopolymer |
Solvay SIPOMER® PAM-100 Phosphate Esters of Polyethylene Glycol Monomethacrylate Description: Sipomer PAM-100 incorporated into acrylic or styrene acrylic latex systems improves adhesion to metallic substrates and glass. Sipomer PAM-100 also enhances properties such as freeze/th.. |
|||
Glass Transition Temp, Tg | 20.0 - 71.0 °C | 68.0 - 160 °F | Average value: 54.2 °C Grade Count:5 |
Overview of materials for Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified". Each property range of values reported.. |