- Polymer Property : Specific Heat Capacity = 0.109 BTU/lb-°F
Polymer Property : Specific Heat Capacity = 0.109 BTU/lb-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Specific Heat Capacity | 0.456 J/g-°C | 0.109 BTU/lb-°F | |
| Special Metals Nickel 201 Commercially pure (99.6%) wrought nickel essentially the same as Nickel 200 but with a lower carbon content to prevent embrittlement by intergranular carbon at temperatures over 600°F (315°C)... |
|||
| Specific Heat Capacity | 0.456 J/g-°C | 0.109 BTU/lb-°F | |
| Special Metals Nickel 205 Wrought nickel similar to Nickel 200 but with compositional adjustments to enhance performance in electrical and electronic applications. Ferromagnetic. Used for the anodes and grids of electronic.. |
|||
| Specific Heat Capacity | 0.456 J/g-°C @Temperature 20.0 °C |
0.109 BTU/lb-°F @Temperature 68.0 °F |
|
| California Fine Wire Nickel A 200 Nickel Alloy All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
| Specific Heat Capacity | 0.456 J/g-°C | 0.109 BTU/lb-°F | |
| ATI Allegheny Ludlum AL 200™ Nickel Alloy, UNS N02200 Ferromagnetic. Allegheny Ludlum AL 200 alloy is wrought commercially pure nickel. This alloy provides highly ductile mechanical properties across a wide temperature range. Either alloy provides c.. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Specific Heat Capacity | 0.455 J/g-°C @Temperature 200 °C |
0.109 BTU/lb-°F @Temperature 392 °F |
|
| Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Specific Heat Capacity | 0.454 J/g-°C | 0.109 BTU/lb-°F | |
| Special Metals INCOLOY® 27-7MO Super-Austenitic Stainless Steel INCOLOY® alloy 27-7MO (UNS S31277; EP 1,263,999 B1) is an advanced 7% molybdenum super-austenitic stainless steel offering corrosion resistance in most environments superior to 6% molybdenum super-.. |
|||