ATI Allegheny Ludlum AL 200™ Nickel Alloy, UNS N02200

Category	Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer	ATI Allegheny Ludlum
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ATI Allegheny Ludlum AL 200™ Nickel Alloy, UNS N02200.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ferromagnetic. Allegheny Ludlum AL 200 alloy is wrought commercially pure nickel. This alloy provides highly ductile mechanical properties across a wide temperature range. Either alloy provides corrosion resistance in neutral to moderately reducing environments. In the annealed condition, either alloy possesses the approximate strength of mild steel. As-rolled material is sometimes furnished to provide higher strength levels. Uses include containers and piping in caustic soda and food processing plants.This nickel alloy is readily fabricated by standard fabricating practices. The material are covered by a variety of specification and are assigned maximum allowable stresses in the ASME Boiler and Pressure Vessel Code. This alloy provides high thermal and electrical conductivity in comparison to nickel base alloys, stainless and low alloy steels. AL 200 Alloy is ferromagnetic.Information provided by Allegheny Ludlum

Physical Properties	Metric	English	Comments
Density	8.90 g/cc	0.322 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell B	45	45	Typical Annealed
Tensile Strength, Ultimate	462 MPa	67000 psi	Typical Annealed
Tensile Strength, Yield	148 MPa @Strain 0.200 %	21500 psi @Strain 0.200 %	Typical; Annealed
Elongation at Break	47 %	47 %	typical in 2"; Annealed
Modulus of Elasticity	207 GPa	30000 ksi
Poissons Ratio	0.31	0.31
Shear Modulus	81.0 GPa	11700 ksi

Thermal Properties	Metric	English	Comments
CTE, linear	13.3 µm/m-°C @Temperature 27.0 - 93.0 °C	7.39 µin/in-°F @Temperature 80.6 - 199 °F
	14.4 µm/m-°C @Temperature 27.0 - 316 °C	8.00 µin/in-°F @Temperature 80.6 - 601 °F
Specific Heat Capacity	0.456 J/g-°C	0.109 BTU/lb-°F
Thermal Conductivity	67.1 W/m-K @Temperature 100 °C	466 BTU-in/hr-ft²-°F @Temperature 212 °F
Maximum Service Temperature, Air	316 °C	601 °F	Ductility loss due to carbon phase precipitation above this temp.

Component Elements Properties	Metric	English	Comments
Carbon, C	<= 0.15 %	<= 0.15 %
Copper, Cu	0.020 %	0.020 %
Iron, Fe	0.050 %	0.050 %
Manganese, Mn	0.020 %	0.020 %
Nickel, Ni	99.8 %	99.8 %	as balance; includes Co
Silicon, Si	0.050 %	0.050 %
Sulfur, S	0.0020 %	0.0020 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.00000850 ohm-cm	0.00000850 ohm-cm

Users viewing this material also viewed the following: