Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 17.2 MPa @Temperature -55.0 °C |
2490 psi @Temperature -67.0 °F |
ASTM D1002-64 |
3M Scotch-Weld™ 3532 B/A Brown Two-Part Urethane Adhesive 3532 B/A Brown
(discontinued **) Two-part urethane adhesives cure at room temperature or with heat to provide tough, impact resistant bonds with high peel strength. Features include fast cure adhesive, 20-30 minutes handling stren.. |
|||
Shear Strength | 17.2 MPa @Temperature -55.0 °C |
2490 psi @Temperature -67.0 °F |
ASTM D1002-64 |
3M Scotch-Weld™ 3535 B/A Off-white Two-Part Urethane Adhesive 3535 B/A Off-white
(discontinued **) Two-part urethane adhesives cure at room temperature or with heat to provide tough, impact resistant bonds with high peel strength. Features include fast cure adhesive, 15-20 minutes handling stren.. |
|||
Shear Strength | 17.2 MPa @Temperature -55.0 °C |
2490 psi @Temperature -67.0 °F |
ASTM D1002-64 |
3M Scotch-Weld™ 3549 B/A Brown Two-Part Urethane Adhesive 3549 B/A Brown
(discontinued **) Two-part urethane adhesives cure at room temperature or with heat to provide tough, impact resistant bonds with high peel strength. Features include long worklife adhesive, 2-4 hours handling stren.. |
|||
Shear Strength | 17.2 MPa @Temperature 25.0 °C |
2500 psi @Temperature 77.0 °F |
Tensile lap |
Resin Technology Group TIGA 110-EXDP Low Viscosity, Optically Clear Glass Bonder Mix ratio 100/50 by volume.TIGA 110EX-DP is a transparent, low viscosity epoxy resin formulation recommended for industrial adhesive, small potting and laminating applications where sparkling clarit.. |
|||
Shear Strength | 17.2 MPa @Temperature 93.3 °C |
2500 psi @Temperature 200 °F |
ASTM D732 |
Greene Tweed Avalon® 89 PTFE Products made from Avalon® thermoplastics are constructed from proprietary high-performance reinforced PTFE material. Greene, Tweeds Avalon thermoplastics, available in grades ranging from virgin.. |
|||
Shear Strength | 17.2 MPa @Temperature 98.9 °C |
2500 psi @Temperature 210 °F |
Lap Shear |
Hexcel® Redux® 312L Modified epoxy film adhesive Redux® 312 is a high-strength 250°F curing film adhesive, suitable for metal to metal bonding and sandwich constructions, where operating temperatures of up to 210°F may be experienced. A support.. |
|||
Shear Strength | 17.2 MPa @Temperature 93.3 °C |
2500 psi @Temperature 200 °F |
Lap Shear |
Hexcel® Redux® 335U Adhesive film for bonding metallic and composite components (0.03 psf) Redux 335 is a film adhesive curing at 250F. It is available in a range of standard areal weights from 0.015 to 0.06 psf. It is available either unsupported or with knitted and/or matt carrier for a.. |
|||
Shear Strength | 17.2 MPa @Temperature -55.0 °C |
2500 psi @Temperature -67.0 °F |
Tensile Lap Shear; Aluminum No Primer; ASTM D1002 |
Hexcel® Redux® HP655 Toughened BMI film Adhesive Redux® HP655 is a toughened BMI structural adhesive designed for metal to metal, composite to composite, and honeycomb sandwich bonding for both co-cured and precured composite skins. Redux® HP655.. |
|||
Shear Strength | 17.2 MPa @Temperature 24.0 °C |
2500 psi @Temperature 75.2 °F |
Overlap |
3M Scotch-Weld™ 1838L B/A Two-Part Structural Adhesive Multi-purpose and Rigid bondsInformation provided by 3M |
|||
Shear Strength | 17.2 MPa @Temperature 121 °C |
2500 psi @Temperature 250 °F |
Aluminum Overlap |
3M Scotch-Weld™ 2214 Hi-Temp Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids, 3M™ Sc.. |
|||
Shear Strength | 17.2 MPa @Temperature 149 °C |
2500 psi @Temperature 300 °F |
Aluminum Overlap |
3M Scotch-Weld™ 2214 Hi-Temp Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids, 3M™ Sc.. |
|||
Shear Strength | 17.2 MPa @Temperature 121 °C |
2500 psi @Temperature 250 °F |
Aluminum Overlap |
3M Scotch-Weld™ 2214 Hi-Temp New Formula Epoxy Adhesive 3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp Formula is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids,.. |
|||
Shear Strength | 17.2 MPa @Temperature 25.0 °C, Time 86400 sec |
2500 psi @Temperature 77.0 °F, Time 24.0 hour |
Lap, Alum to Alum |
Atom Adhesives AA-BOND F112 Epoxy Adhesive AA-BOND F112 is an impact resistant, fiber-optic adhesive. AA-BOND F112 is two-part, low viscosity epoxy has the distinct advantage of remaining below 3000 cps for a minimum of 40 minutes. AA-BOND F.. |
|||
Shear Strength | 17.2 MPa @Temperature 121 °C |
2500 psi @Temperature 250 °F |
Overlap |
3M Scotch-Weld™ 1386 One-Part Epoxy Adhesives and Metal Primer High Temperature strength and Impact resistanceInformation provided by 3M |
|||
Shear Strength | 17.2 MPa @Temperature -40.0 °C |
2500 psi @Temperature -40.0 °F |
Overlap, Etched Aluminum |
3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 17.2 MPa @Temperature -55.0 °C |
2500 psi @Temperature -67.0 °F |
Overlap |
3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 17.2 MPa @Temperature -40.0 °C |
2500 psi @Temperature -40.0 °F |
Overlap, Etched Aluminum |
3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 17.2 MPa @Temperature -55.0 °C |
2500 psi @Temperature -67.0 °F |
Overlap |
3M Scotch-Weld™ 3535 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 17.2 MPa @Temperature -40.0 °C |
2500 psi @Temperature -40.0 °F |
Overlap, Etched Aluminum |
3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 17.2 MPa @Temperature -55.0 °C |
2500 psi @Temperature -67.0 °F |
Overlap |
3M Scotch-Weld™ 3549 B/A Two-Part Structural Adhesive 3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion propertie.. |
|||
Shear Strength | 17.2 MPa @Temperature 24.0 °C |
2500 psi @Temperature 75.2 °F |
Overlap |
3M Scotch-Weld™ DP270 Black Structural Adhesive Rigid potting compound, Non-corrosiveInformation provided by 3M |
|||
Shear Strength | 17.2 MPa @Temperature 24.0 °C |
2500 psi @Temperature 75.2 °F |
Overlap |
3M Scotch-Weld™ DP270 Clear Structural Adhesive Rigid potting compound, Non-corrosiveInformation provided by 3M |