3M Scotch-Weld™ 3535 B/A Off-white Two-Part Urethane Adhesive 3535 B/A Off-white  (discontinued **)

Category	Polymer , Adhesive , Thermoset , Polyurethane, TS , Thermoset Polyurethane, Adhesive
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	3M Scotch-Weld™ 3535 B/A Off-white Two-Part Urethane Adhesive 3535 B/A Off-white  (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Two-part urethane adhesives cure at room temperature or with heat to provide tough, impact resistant bonds with high peel strength. Features include fast cure adhesive, 15-20 minutes handling strength, semi-rigid urethane, and faster setting version of 3532 B/A Adhesive. Mix ratio by volume 1:1. Average T-Peel at 75°F (24°C) is 25 PIW; 180° peel tested on 0.030 inch aluminum per ASTM D 1876-61T.Information provided by 3M Adhesives Division.

Physical Properties	Metric	English	Comments
Brookfield Viscosity	30000 cP <br>@Temperature 23.9 °C	30000 cP <br>@Temperature 75.0 °F

Mechanical Properties	Metric	English	Comments
Shear Strength	1.03 MPa <br>@Temperature 121 °C	149 psi <br>@Temperature 250 °F	ASTM D1002-64
	2.10 MPa <br>@Temperature 82.0 °C	305 psi <br>@Temperature 180 °F	ASTM D1002-64
	13.8 MPa <br>@Temperature 24.0 °C	2000 psi <br>@Temperature 75.2 °F	ASTM D1002-64
	17.2 MPa <br>@Temperature -55.0 °C	2490 psi <br>@Temperature -67.0 °F	ASTM D1002-64

Processing Properties	Metric	English	Comments
Processing Temperature	>= 20.0 °C	>= 68.0 °F
Pot Life	3.00 min <br>@Temperature 23.9 °C	3.00 min <br>@Temperature 75.0 °F

Users viewing this material also viewed the following:

3M Scotch-Weld™ 3535 B/A Off-white Two-Part Urethane Adhesive 3535 B/A Off-white &nbsp;(discontinued **)

3M Scotch-Weld™ 3535 B/A Off-white Two-Part Urethane Adhesive 3535 B/A Off-white (discontinued **)