3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive

Category Polymer , Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ 3532 B/A Two-Part Structural Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Urethane Adhesives are two-component, polyurethane adhesives which cure at room temperature or with heat to form tough, impact-resistant structural bonds. Their adhesion properties are identical and they vary only in work life, cure time and color. They provide excellent adhesion to many primed or painted metal and plastic substrates and are designed to develop sag resistance approximately 30 second after mixing.Information provided by 3M
Physical Properties Metric English Comments
Viscosity 30000 cP
30000 cP
Brookfield Viscosity 15000 - 40000 cP
15000 - 40000 cP
Accelerator, RVF #5 sp @ 20 rpm
10000 - 55000 cP
10000 - 55000 cP
Base, RVF #6 sp @ 20 rpm
Mechanical Properties Metric English Comments
Tensile Strength at Break 20.7 MPa
3000 psi
ASTM D738
Elongation at Break 96 %
96 %
ASTM D738
Shear Strength 0.138 MPa

@Temperature 82.0 °C
 20.0 psi

@Temperature 180 °F
 Overlap, Solvent Wiped Steel
0.276 MPa

@Temperature 82.0 °C
 40.0 psi

@Temperature 180 °F
 Overlap, Nylon
0.483 MPa

@Temperature 82.0 °C
 70.0 psi

@Temperature 180 °F
 Overlap, Plexiglass
0.689 MPa

@Temperature 82.0 °C
 100 psi

@Temperature 180 °F
 Overlap, Solvent Wiped Al
0.689 MPa

@Temperature 82.0 °C
 100 psi

@Temperature 180 °F
 Overlap, Abraded and Solvent Wiped Steel
0.758 MPa

@Temperature 82.0 °C
 110 psi

@Temperature 180 °F
 Overlap, Rigid PVC
0.758 MPa

@Temperature 82.0 °C
 110 psi

@Temperature 180 °F
 Overlap, Polystyrene
0.862 MPa

@Temperature 82.0 °C
 125 psi

@Temperature 180 °F
 Overlap, Lexan
1.24 MPa

@Temperature 82.0 °C
 180 psi

@Temperature 180 °F
 Overlap, FRP
1.65 MPa

@Temperature -40.0 °C
 240 psi

@Temperature -40.0 °F
 Overlap, Nylon
2.07 MPa

@Temperature 82.0 °C
 300 psi

@Temperature 180 °F
 Overlap
2.07 MPa

@Temperature 82.0 °C
 300 psi

@Temperature 180 °F
 Overlap, Etched Aluminum
2.07 MPa

@Temperature 82.0 °C
 300 psi

@Temperature 180 °F
 Overlap, Abraded and Solvent Wiped Al
2.07 MPa

@Temperature 82.0 °C
 300 psi

@Temperature 180 °F
 Overlap, ABS
2.28 MPa

@Temperature -40.0 °C
 330 psi

@Temperature -40.0 °F
 Overlap, Polystyrene
2.55 MPa

@Temperature -40.0 °C
 370 psi

@Temperature -40.0 °F
 Overlap, Rigid PVC
3.03 MPa

@Temperature -40.0 °C
 440 psi

@Temperature -40.0 °F
 Overlap, ABS, Substrate Failure
3.65 MPa

@Temperature 24.0 °C
 530 psi

@Temperature 75.2 °F
 Overlap, Polystyrene
4.00 MPa

@Temperature 24.0 °C
 580 psi

@Temperature 75.2 °F
 Overlap, Nylon
4.27 MPa

@Temperature -40.0 °C
 620 psi

@Temperature -40.0 °F
 Overlap, Plexiglass
4.83 MPa

@Temperature 24.0 °C
 700 psi

@Temperature 75.2 °F
 Overlap, Solvent Wiped Steel
5.58 MPa

@Temperature 24.0 °C
 810 psi

@Temperature 75.2 °F
 Overlap, ABS
6.62 MPa

@Temperature 24.0 °C
 960 psi

@Temperature 75.2 °F
 Overlap, Rigid PVC
6.89 MPa

@Temperature -40.0 °C
 1000 psi

@Temperature -40.0 °F
 Overlap, Solvent Wiped Al
6.89 MPa

@Temperature -40.0 °C
 1000 psi

@Temperature -40.0 °F
 Overlap, Solvent Wiped Steel
6.89 MPa

@Temperature 24.0 °C
 1000 psi

@Temperature 75.2 °F
 Overlap, Solvent Wiped Al
7.93 MPa

@Temperature 24.0 °C
 1150 psi

@Temperature 75.2 °F
 Overlap, FRP, Substrate Failure
8.27 MPa

@Temperature 24.0 °C
 1200 psi

@Temperature 75.2 °F
 Overlap, Abraded and Solvent Wiped Steel
8.55 MPa

@Temperature -40.0 °C
 1240 psi

@Temperature -40.0 °F
 Overlap, Lexan, Substrate Failure
8.96 MPa

@Temperature 24.0 °C
 1300 psi

@Temperature 75.2 °F
 Overlap, Plexiglass
11.4 MPa

@Temperature -40.0 °C
 1660 psi

@Temperature -40.0 °F
 Overlap, FRP, Substrate Failure
12.7 MPa

@Temperature 24.0 °C
 1840 psi

@Temperature 75.2 °F
 Overlap, Lexan, Substrate Failure
13.8 MPa

@Temperature -40.0 °C
 2000 psi

@Temperature -40.0 °F
 Overlap, Abraded and Solvent Wiped Steel
13.8 MPa

@Temperature 24.0 °C
 2000 psi

@Temperature 75.2 °F
 Overlap
13.8 MPa

@Temperature 24.0 °C
 2000 psi

@Temperature 75.2 °F
 Overlap, Etched Aluminum
13.8 MPa

@Temperature 24.0 °C
 2000 psi

@Temperature 75.2 °F
 Overlap, Abraded and Solvent Wiped Al
13.8 MPa

@Temperature -40.0 °C
 2000 psi

@Temperature -40.0 °F
 Overlap, Abraded and Solvent Wiped Al
17.2 MPa

@Temperature -40.0 °C
 2500 psi

@Temperature -40.0 °F
 Overlap, Etched Aluminum
17.2 MPa

@Temperature -55.0 °C
 2500 psi

@Temperature -67.0 °F
 Overlap
Peel Strength 4.38 kN/m
25.0 pli
T-Peel
Processing Properties Metric English Comments
Cure Time 90.0 min
1.50 hour
1440 min
24.0 hour
Full Cure
Descriptive Properties Value Comments
Appearance Brown
Accelerator
Off-White
Base