3M Scotch-Weld™ 2214 Hi-Temp New Formula Epoxy Adhesive

Category	Polymer , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ 2214 Hi-Temp New Formula Epoxy Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M™ Scotch-Weld™ Adhesive 2214 Hi-Temp Formula is an aluminum filled, deaerated products fro use where higher strengths are required between 82-177°C. One part 250°F (121°C) curing 100% solids, 3M™ Scotch-Weld™ Epoxy Adhesive 2214 is a paste consistency epoxy adhesive designed for bonding metals and many high temperature plastics such as fiberglass reinforced plastic, polyester, and phenolicsInformation provided by 3M

Physical Properties	Metric	English	Comments
Viscosity	100 - 250 cP	100 - 250 cP

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	>= 85	>= 85
Elongation at Break	1.0 %	1.0 %
Shear Strength	8.27 MPa @Temperature 177 °C	1200 psi @Temperature 351 °F	Aluminum Overlap
	13.8 MPa @Temperature 149 °C	2000 psi @Temperature 300 °F	Aluminum Overlap
	17.2 MPa @Temperature 121 °C	2500 psi @Temperature 250 °F	Aluminum Overlap
	19.3 MPa @Temperature -53.0 °C	2800 psi @Temperature -63.4 °F	Aluminum Overlap
	19.3 MPa @Temperature 24.0 °C	2800 psi @Temperature 75.2 °F	Aluminum Overlap
	19.3 MPa @Temperature 82.0 °C	2800 psi @Temperature 180 °F	Aluminum Overlap

Thermal Properties	Metric	English	Comments
CTE, linear	44.0 µm/m-°C @Temperature -60.0 - 80.0 °C	24.4 µin/in-°F @Temperature -76.0 - 176 °F
Thermal Conductivity	0.429 W/m-K	2.98 BTU-in/hr-ft²-°F

Electrical Properties	Metric	English	Comments
Dielectric Constant	4.61 @Temperature 23.0 °C	4.61 @Temperature 73.4 °F	ASTM D150
	4.96 @Temperature 60.0 °C	4.96 @Temperature 140 °F	ASTM D150
Dissipation Factor	0.0135 @Temperature 23.0 °C	0.0135 @Temperature 73.4 °F
	0.018 @Temperature 60.0 °C	0.018 @Temperature 140 °F

Descriptive Properties	Value	Comments
Appearance	Gray