Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 3.20 - 8.30 GPa | 464 - 1200 ksi | Average value: 5.57 GPa Grade Count:3 |
Overview of materials for Polystyrene, Wood Filled This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Wood Filled". Each property range of values reported is minimum and maximum values of appro.. |
|||
Flexural Modulus | 1.91 - 8.27 GPa | 277 - 1200 ksi | Average value: 2.54 GPa Grade Count:66 |
Overview of materials for Polycarbonate, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Impact Modified". Each property range of values reported is minimum and maximum values of.. |
|||
Flexural Modulus | 1.69 - 8.27 GPa | 245 - 1200 ksi | Average value: 3.45 GPa Grade Count:43 |
Overview of materials for Nylon 66, MoS2 Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, MoS2 Filled". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Flexural Modulus | 0.621 - 8.27 GPa | 90.0 - 1200 ksi | Average value: 3.90 GPa Grade Count:47 |
Overview of materials for Nylon 66, Aramid Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Aramid Fiber Filled". Each property range of values reported is minimum and maximum values of .. |
|||
Flexural Modulus | 6.21 - 8.28 GPa | 900 - 1200 ksi | Average value: 7.58 GPa Grade Count:5 |
Overview of materials for Nylon 12, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. .. |
|||
Flexural Modulus | 6.89 - 8.27 GPa | 1000 - 1200 ksi | |
Bulk Molding Compounds BMC A30 General Purpose Molding Compound BMC A30 is a general purpose molding compound with good dimensional stability. Due to the excellent flow and controlled reactivity, BMC A30 is well suited for injection, transfer or compression mol.. |
|||
Flexural Modulus | 6.89 - 8.27 GPa | 1000 - 1200 ksi | |
Bulk Molding Compounds BMC A30-3021 General Purpose Molding Compound BMC A30-3021 is a low shrink, general purpose molding compound formulated for the lighting industry. A30-3021 is temperature stabilized for use in elevated temp. lighting applications. Due to the .. |
|||
Flexural Modulus | 1.70 - 8.27 GPa | 247 - 1200 ksi | Average value: 2.96 GPa Grade Count:30 |
Overview of materials for Nylon 6, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, PTFE Filled". Each property range of values reported is minimum and maximum values of appropria.. |
|||
Flexural Modulus | 4.83 - 8.27 GPa | 700 - 1200 ksi | Average value: 7.02 GPa Grade Count:18 |
Overview of materials for Polyphenylene Ether, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 30% Glass Filled". Specific grades with glass content between 25% and 34% are inclu.. |
|||
Flexural Modulus | 6.89 - 8.27 GPa | 1000 - 1200 ksi | |
Bulk Molding Compounds BMC T40(18) Die Casting Replacement Grade Molding Compound BMC T40(18) was formulated as a direct replacement for aluminum die casting applications. T40(18) is UL recognized. Excellent mechanical properties and dimensional control allow molded parts to ma.. |