Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.270 GPa | 39.2 ksi | 1.7 mm/min; DIN 53457 |
Advanced Elastomer Systems VistaFlex® 912-B Thermoplastic Rubber
(discontinued **) Description: A black super high-flow thermoplastic elastomer especially designed for injection molding applications. It replaces soft thermoplastics such as SBS, SEBS, and PVC blends. Supplied as .. |
|||
Flexural Modulus | 0.270 GPa | 39.2 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP YP003 POLYESTER ELASTOMER LNP LUBRICOMP* YP003 is a compound based on Polyester Elastomer resin containing 15% PTFE/Silicone. Added features of this material include: Wear Resistant. |
|||
Flexural Modulus | 0.270 GPa | 39.2 ksi | ISO 178 |
SABIC Innovative Plastics LNP Lubricomp YP003 TPEE LNP LUBRICOMP* YP003 is a compound based on TPEE resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas .. |
|||
Flexural Modulus | 0.270 GPa | 39.2 ksi | Tangent - 16:1 span:depth, 0.5 in/min; ASTM D-790 |
Chevron Phillips Marlex® C101 Polyethylene; Enhanced Metallocene linear low density polyethylene. This linear low density, hexene copolymer is tailored for blow molded containers that require: High glossGood clarityExcellent ESCR Applications: Typi.. |
|||
Flexural Modulus | 0.270 GPa | 39.2 ksi | Conditioned 15 days at 23°C - 50% RH; ISO 178 |
Arkema Group Pebax® MV 1041 SA 01 Polyether Block Amide (PEBA) Polyether block amide PEBAX® MV 1041 SA 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This hydrophilic grade when extruded into either a thin film or laminated on .. |
|||
Flexural Modulus | 0.270 GPa | 39.2 ksi | ASTM D790 |
C.O.I.M. LARIPUR® LPR5850 Modified Ester Polyurethane Description: The products of the LARIPUR® line are thermoplastic polyurethanes. These products combine the technology of thermoplastic products with the features of polyurethanes:Excellent abrasion.. |
|||
Flexural Modulus | 0.270 GPa @Temperature 65.0 °C |
39.2 ksi @Temperature 149 °F |
ASTM Test |
BASF Ultramid® 8350 HS PA6 (Dry) Ultramid 8350 HS is a heat stabilized, impact modified type 6 graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate.. |