Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 8.34 GPa | 1210 ksi | ASTM D790 |
Samyang Tripet® 2550GN45 Polyethylene Terephthalate, 45% Glass Fiber Reinforced, Flame Retardant
(discontinue TRIPET® has excellent heat resistance, good surface, chemical resistance and high electrical performance.Applications:Coil BobbinConnectorMotor HousingLamp HousingRelay BaseIron bodyAll information.. |
|||
Flexural Modulus | 8.34 GPa | 1210 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DFL36XXP PC LNP* Lubricomp* DFL36XXP is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 8.34 GPa @Thickness 3.20 mm |
1210 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID GP2251BF PA66+GF25%, Flame Retardant Feature: Injection Molding, PA66+GF25%, Flame RetardantApplication: IT/OA (Micro Switch)CAS No. 32131-17-2, 65997-17-3, 88497-56-7, 1309-64-4 and 138265-88-0Information provided by LG Chemical |
|||
Flexural Modulus | 8.34 GPa @Thickness 6.40 mm |
1210 ksi @Thickness 0.252 in |
3mm/min; ASTM D790 |
LG Chemical LUMID GP2300A(W) PA6+GF30%, General Purpose Feature: Injection Molding, PA6+GF30%, General PurposeApplication: Automotive (Side Mirror Base Plate)CAS No. 25038-54-4 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Modulus | 8.34 GPa @Thickness 3.20 mm |
1210 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID SG2300B(W) PA66+GF30%, General Purpose, Good Surface Feature: Injection Molding, PA66+GF30%, General Purpose, Good SurfaceApplication: Automotive PartsCAS No. 32131-17-2, 13983-17-0 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Modulus | 8.34 GPa | 1210 ksi | DIN 53452; ASTM D790 |
Kolon KOPA® KN332G30VO G/F Reinforced & Flame Retardant Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin.. |
|||
Flexural Modulus | 8.34 GPa | 1210 ksi | DIN 53452; ASTM D790 |
Kolon KOPET® KP133G30 FR-PET Resin KOPET® is the FR-PET which realizes the good properties and surface of injection molding with good mold process of short cooling time in low molding temperature.Good mold release, good surface of.. |
|||
Flexural Modulus | 8.34 GPa | 1210 ksi | DIN 53452; ASTM D790 |
Kolon SPESIN® KP213G30 Flame Retardant PBT Resin SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High.. |
|||
Flexural Modulus | 8.35 GPa | 1210 ksi | DIN 53452; ASTM D790 |
Kolon SPESIN® KP513G30WBL Multi Reinforced PBT Resin SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High.. |
|||
Flexural Modulus | 8.34 GPa @Thickness 3.20 mm |
1210 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical Lupox® GP2306FI PBT+GF30% Description: Injection Molding, PBT+GF30%, Flame Retardant, High Impact Application: IT/OA, E&E (Connector)CAS No. 68928-70-1, 65997-17-3, 24968-12-5 and 1309-64-4Information provided by LG Chemical.. |
|||
Flexural Modulus | 8.34 GPa | 1210 ksi | ASTM D790 |
Gromax PBT 3030-201 30% Glass Fiber Filled Product Description: A glass fiber 30% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature Excellent .. |
|||
Flexural Modulus | 8.34 GPa | 1210 ksi | ASTM D790 |
Gromax PBT 4130-104D 30% Glass Fiber Filled Product Description: A glass fiber 30% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature Excellent .. |
|||
Flexural Modulus | 8.34 GPa | 1210 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL PX5558 PPE+PS 30% glass reinforced, high flow PPO. |
|||
Flexural Modulus | 8.33 GPa | 1210 ksi | ASTM D790 |
SABIC Innovative Plastics Valox® VIC4350 PBT (Asia Pacific) |
|||
Flexural Modulus | 8.35 GPa | 1210 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DF006HL PC LNP THERMOCOMP* DF006HL is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Low Extractible, Healthcare. |
|||
Flexural Modulus | 8.34 GPa | 1210 ksi | ASTM D790 |
Techmer ES Plaslube® J-4/30/TF/13/SI/2 NAT PA6/12 |
|||
Flexural Modulus | 8.34 GPa | 1210 ksi | ASTM D790 |
Techmer ES Plaslube® J-4/35/TF/15 NAT PA6/12 |
|||
Flexural Modulus | 8.31 GPa | 1210 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP ZF006 PPE+PS LNP* THERMOCOMP* ZF006 is a compound based on PPE+PS resin containing 30% Glass Fiber. |
|||
Flexural Modulus | 8.31 GPa | 1210 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL PPX PPX640 PPE+PP 40% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited). |
|||
Flexural Modulus | 8.31 GPa | 1210 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL PPX PPX640 PPE+PP (Asia Pacific) 40% GR PPE+PP. High elongation. high stiffness. NSF Standard 61 Compliant (color limited). |
|||
Flexural Modulus | 8.33 GPa | 1210 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP WH0245A PBT LNP THERMOCOMP* WH0245A is a compound based on Polybutylene Terephalate resin. Added features of this material include: High Specific Gravity. |
|||
Flexural Modulus | 8.32 GPa | 1210 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp WH0270FX_WH5A289 PBT 2.7 specific gravity PBTThis data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 8.34 GPa | 1210 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL EM7430 PPE+PS 30% glass reinforced, high flow PPO. Automotive. Energy management material. |
|||
Flexural Modulus | 8.34 GPa | 1210 ksi | ASTM D790 |
Techmer Lehvoss Compounds Luvotech™ J-4/30 BK PA6/12
(discontinued **) Techmer Lehvoss Compounds, a JV between Techmer ES and Lehmann&Voss&Co. has been terminated. |
|||
Flexural Modulus | 8.34 GPa | 1210 ksi | ASTM D790 |
Techmer Lehvoss Compounds Luvotech™ J-4/30/V0 BK2989 PA6/12
(discontinued **) Techmer Lehvoss Compounds, a JV between Techmer ES and Lehmann&Voss&Co. has been terminated. |
|||
Flexural Modulus | 8.34 GPa | 1210 ksi | ASTM D790 |
Techmer Lehvoss Compounds Luvotech™ J-4/35 BK223 PA6/12
(discontinued **) Techmer Lehvoss Compounds, a JV between Techmer ES and Lehmann&Voss&Co. has been terminated. |
|||
Flexural Modulus | 8.35 GPa | 1210 ksi | ASTM D790 |
Adell WL-38 40% Glass and Mineral Reinforced PET |