SABIC Innovative Plastics NORYL PX5558 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PX5558 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% glass reinforced, high flow PPO.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0020 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 19.6 g/10 min @Load 5.00 kg, Temperature 280 °C |
19.6 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 7.75 GPa | 1120 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 162 MPa | 23500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 7.17 GPa | 1040 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 8.34 GPa | 1210 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.61 J/cm | 4.89 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 14.0 J @Temperature 23.0 °C |
10.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
11.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 66.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C @Thickness 3.20 mm |
264 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 130 °C | 266 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 4504 PPC
- Johnson Matthey Mattiflux 100 Brazing Flux Paste
- Kostat ICP-STAT ICD-1001 PET Sheet
- SABIC Innovative Plastics LNP Thermocomp AF0029 ABS (Europe-Africa-Middle East)
- Stir SpA SPI 78 ATC (PVC)
- Styron DL 242NA Functionalized SB
- Axion Polymers Axpoly® PS02 1000 General Purpose Polystyrene
- Arlon 55579R055 0.054" (1.37 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- A.D. Compound Adene NCTA Homopolymer 50% CaCO3 Filled Polypropylene
Copyright © lookpolymers.com All Rights Reserved