Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.800 GPa | 116 ksi | STN EN ISO 178 |
Plastcom PLASTALEN® EQ 18 N Polyethylene Impact modified PE for extrusion. Delivered in black color.Information Provided by Plastcom spol. s r.o. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | |
Plastcom SLOVAMID 66 SHI PA66, improved strength Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.0.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
Quadrant EPP TIVAR® 1000 UV Stabilized UHMW, Black (ASTM Product Data Sheet) |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
Quadrant EPP TIVAR® 1000 UV Stabilized UHMW-PE, Natural & Colored Except Black (ASTM Product Data Sheet) |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
SABIC M300054 High Density Polyethylene for Injection Molding Product Description: M300054 is a high density polyethylene grade with a narrow molecular weight distribution suitable for injection molding applications. It has been designed to provide good flow.. |
|||
Flexural Modulus | 0.800 GPa @Temperature 90.0 °C |
116 ksi @Temperature 194 °F |
ASTM D790 |
Nilit Polynil® P50L Externally Lubricated Nylon 66 Description: Polynil P50L is a general purpose injection molding grade that is widely used for gears, bearings, fasteners, clips. It is also suited for monofilament extrusion.Key characteristics: Ex.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | 1% secant; ASTM D790A |
Reliance Industries Repol D120MA Polypropylene REPOL Polypropylene D120MA is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly.. |
|||
Flexural Modulus | 0.800 - 2.70 GPa | 116 - 392 ksi | Average value: 1.65 GPa Grade Count:83 |
Overview of materials for Polypropylene with 20% Calcium Carbonate (CaCO3) Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Calcium Carbonate (CaCO3) Filler". Each property range of values reported is mini.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D760-66 |
Micropol Microlin ML25 Linear Polyethylene Rotational Molding Powder Information provided by Micropol Limited |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | GB/T94341 |
Lushan DE-1 Polyethylene Sintered Powder PE sintered powder Lushan DE-1 is combined with more than 10 years practice and experience on the area of oil & gas pipeline anti-corrosion. PE sintered powder Lushan DE-1 is used on anti-corrosion .. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ISO 178 |
Solvay TECHNYL® C 230 PA6, Conditioned Description: Unreinforced polyamide PA6, with improved impact resistance, for injection molding.Available in: EuropeProduct Applications: This grade has improved impact strength and higher flexibili.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ISO 178 |
Borealis BorPURE™ RD266CF Polypropylene Random Copolymer BorPure™ RD266CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications: BorPure™ RD266CF is recommended for
food packaging.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | 2mm/min; ISO 178 |
Borealis RA130E-1498 Polypropylene Random Copolymer RA130E-1498 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is white colored. Applications: RA130E-1498 is recommended for the production of PP-R p.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ISO 178 |
Borealis Steripeel™ WD165CF PO Compound for Sterilizable Peelable Film Applications Steripeel WD165CF is a non-formulated film resin, specially developed for the manufacturing of unoriented peelable cast films on chill roll process.Steripeel WD165CF is suitable for various peelable.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ISO 178 |
Borealis Steripeel™ WD170CF PO Compound for Sterilizable Peelable Film Applications Steripeel WD170CF is a non-formulated film resin, specially developed for the manufacturing of unoriented peelable cast films on chill roll process.Steripeel WD170CF is suitable for various peelable.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ISO 178 |
Unipetrol PE HD LITEN® VL 10 HDPE Extrusion and pipe applications.Information provided by Unipetrol RPA |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D 790 |
Total 3802 B HDPE, cable, sheet, pipe, injection molding FINATHENE® 3802 B is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low-pressure slurry polymerization process. FINATHENE® 3802 B is a black polyethylene.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | 2mm/min; ISO 178 |
Borealis RA130E-2492 Polypropylene Random Copolymer RA130E-2492 is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is dark blue colored. Applications: domestic water, heating, relining, plumbing, and in.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
Ecomass® 4703ZD95 Tungsten Filled Polyurethane Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applicationsHigh Specific GravityTungsten Powder Filled Polyurethane (TPU)FlexibleInformation provided by Technical Po.. |
|||
Flexural Modulus | 0.800 GPa @Temperature 120 °C |
116 ksi @Temperature 248 °F |
ISO 178 |
DSM Stanyl® TW341-B PA46 Heat Stabilized, Lubricated |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | from bending test; DIN 53 457 |
Hippe PE 1000 Polyethylene Tough, flexible and stiff, depending on the crystalline structure (density). Resinous surface. Excellent dielectric properties, Good resistance against solvents, acids and alkalis. Physiologicall.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ISO R178 |
Arkema Group ORGASOL® 3502 D Nat 1 Copolyamide 6/12 Information provided by Arkema Group |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
Aclo Accutech Polypropylene Copolymer CP0437C20L1 Calcium Reinforced |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM-D790 |
Braskem Symbios 3102 Polypropylene Terpolymer Braskem Symbios 3102 is a medium melt flow rate terpolymer with a heat seal temperature below 110ºC on its non-treated face. It is designed for use as a heat sealing layer for cast film coextrusion.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
Buckeye Polymers BP Flex D7030 UC85 TPO Bumpers, Air damsTPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment. These resins have excellent UV resi.. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
A. Schulman POLYFORT™ PP 1329 UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1329HU is a high flow UV stabilized, medium impact copolymer polypropylene. Information provided by A. Schulman. |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ISO 178 |
Cathay PA56 Renewable Engineering Polyamide, 50% RH Cathay engineering polyamides contain 26-100% renewably sourced material. Advantages: Operates at similar conditions to PA66; Suitable for injection, compounding and extrusion; Stable mechanical pr.. |
|||
Flexural Modulus | 0.800 GPa @Temperature 120 °C |
116 ksi @Temperature 248 °F |
ISO 178 |
DSM Stanyl® TE300 PA46 Heat Stabilized |
|||
Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
A. Schulman POLYFORT™ PP 1329 UV Stabilized, Medium Impact Copolymer Polypropylene DescriptionPolyfort® PP 1329HU is a high flow UV stabilized, medium impact copolymer polypropylene. Information provided by A. Schulman. |