Hippe PE 1000 Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer Erhard Hippe KG
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hippe PE 1000 Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Tough, flexible and stiff, depending on the crystalline structure (density). Resinous surface. Excellent dielectric properties, Good resistance against solvents, acids and alkalis. Physiologically safe. Low water absorption, not aromatic-resistant. Manifold usable. Easily machinable.Excellent sliding properties. PE 1000 with high molecular weight can be used to -260°C. The abrasion is very low.Information provided by Hippe.
Physical Properties Metric English Comments
Specific Gravity 0.930 g/cc
0.930 g/cc
DIN 53 479
Moisture Absorption at Equilibrium <= 0.050 %
<= 0.050 %
Absorption of humidity in standard operating environment; DIN 53 715
Water Absorption at Saturation <= 0.050 %
<= 0.050 %
DIN 53 495
Mechanical Properties Metric English Comments
Ball Indentation Hardness 38.0 MPa

@Time 30.0 sec
5510 psi

@Time 0.00833 hour
DIN 53 456
Tensile Strength 20.0 MPa
2900 psi
DIN 53 455
Elongation at Break >= 350 %
>= 350 %
DIN 53 455
Tensile Modulus 0.600 GPa
87.0 ksi
DIN 53 457
Flexural Modulus 0.800 GPa
116 ksi
from bending test; DIN 53 457
Charpy Impact, Notched NB
NB
DIN 53 453
Coefficient of Friction, Dynamic 0.29
0.29
Against steel, p=0.05 N/mm², v=0.6 m/s, hardened and ground
Tear Strength Test 40
40
in MPa; DIN 53 455
Thermal Properties Metric English Comments
CTE, linear 170 µm/m-°C
94.4 µin/in-°F
Specific Heat Capacity 1.84 J/g-°C
0.440 BTU/lb-°F
Thermal Conductivity 0.410 W/m-K
2.85 BTU-in/hr-ft²-°F
Melting Point 130 - 135 °C
266 - 275 °F
DIN 53 736
Maximum Service Temperature, Air 100 °C
212 °F
Continuous use
125 °C
257 °F
Short Periods
Deflection Temperature at 0.46 MPa (66 psi) 70.0 °C
158 °F
ISO-R 75 Method B
Deflection Temperature at 1.8 MPa (264 psi) 42.0 °C
108 °F
ISO-R 75 Method A
Glass Transition Temp, Tg -95.0 °C
-139 °F
dynamic; DIN 53 736
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
DIN 53 482, VDE 0303, Part 3
Surface Resistance 1.00e+11 ohm
1.00e+11 ohm
DIN 53 482
Dielectric Constant 3.0

@Frequency 1.00e+6 Hz
3.0

@Frequency 1.00e+6 Hz
DIN 53 483, IEC-250
Dielectric Strength 45.0 kV/mm
1140 kV/in
Breakdown; DIN 53 481, IEC-243, VDE 0303 Part 1
Descriptive Properties Value Comments
Color natural/green, black
Creep Resistance Grade KA 3c, KB >600, KC >600
DIN 53 480, IEC-112, VDE 0303 Part 1
Resistance to hot water, suds resistant