Polymer Property : Flexural Modulus = 2.90 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	2.90 GPa	421 ksi	ASTM D790
PolyOne Geon™ Vinyl Rigid Extrusion 87549 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
Flexural Modulus	2.90 GPa	420 ksi	Tangent; ASTM D790
RheTech Products T30P100-01 30% Talc Reinforced Polypropylene, Black Applications: BracketsAir ductsConsolesWire troughInjection molding conditions reported in table.Information provided by RheTech Products.
Flexural Modulus	2.90 GPa	421 ksi	ASTM D790
PolyOne Geon™ Vinyl Fittings 87322 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne
Flexural Modulus	2.90 GPa	421 ksi	ASTM D790
LG Chemical LupoxÂ® GP-1001F General Purpose PBT, Unreinforced, Flame Retardant LUPOX semi-crystalline thermoplastic PBT resins exhibit properties including high strength, rigidity and good resistance to fatigue and creep at elevated temperatures. Furthermore, LUPOX resins sho..
Flexural Modulus	2.90 GPa	421 ksi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP RL003 PA 66 LNP* LUBRICOMP* RL003 is a compound based on Nylon 66 resin containing 15% PTFE. Added features of this material include: Wear Resistant.
Flexural Modulus	2.90 GPa	421 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM UF5011S PEI Enhanced flow, Specialty filtered Polyetherimide (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.
Flexural Modulus	2.90 GPa	421 ksi	ASTM D 790
SABIC Innovative Plastics LNP Stat-kon DX92440 PC LNP STAT-KON* DX92440 is a compound based on Polycarbonate resin containing Flame Retardant, Stainless Steel. Added features of this material include: Electrically Conductive.This data was supplied..
Flexural Modulus	2.90 GPa	421 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics XenoyÂ® X4830 PBT+PC Xenoy X4830 is a hydrostable, high modulus, low temperature ductile PC/PBT blend. Furthermore, this resin provides high chemical resistance, very low creep, low CTE, excellent fatique and high heat ..
Flexural Modulus	2.90 GPa	421 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics XenoyÂ® X4830 PBT+PC (Europe-Africa-Middle East) Xenoy X4830 is a hydrostable, high modulus, low temperature ductile PC/PBT blend. Furthermore, this resin provides high chemical resistance, very low creep, low CTE, excellent fatique and high heat ..
Flexural Modulus	2.90 GPa	420 ksi	ASTM D790
Techmer ES PlaslubeÂ® NY-1/TF/12 Nylon 66, 12% PTFE Plaslube polytetrafluoroethylene (PTFE) lubricated nylon 66 grades offer the best wear and friction properties of any unreinforced, lubricated nylon compounds, making them ideal materials for bearin..
Flexural Modulus	2.90 GPa	421 ksi	ISO 178
Solvay TECHNYLÂ® A 208F PA66, DRY Description: Unreinforced polyamide PA66, heat stabilized, high fluidity, fast cycling grade, for injection molding.Available in: EuropeProduct Applications: TECHNYL A 208F offers three main advanta..
Flexural Modulus	2.90 GPa	421 ksi	ISO 178
SABIC Innovative Plastics LNP STAT-KON DD0009PC PC LNP STAT-KON* DD0009PC is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant.
Flexural Modulus	2.90 GPa	421 ksi	ISO 178
Solvay TechnylÂ® A 205F Nylon 66, EH0 Unreinforced polyamide 66, high fluidity, fast cycling grade, for injection molding.Technyl A 205F offers two main advantages: excellent filling qualities and UL 94 V2 under 0.4 mm. It is particula..
Flexural Modulus	2.90 GPa	420 ksi	ASTM D790
Westlake Plastics Polyethersulfone High resistance to heat and combustibility, low smoke emission, and transparency are the combination of properties possessed by stock shapes extruded from PES. These, coupled with light weight, good..
Flexural Modulus	2.90 GPa	421 ksi	ISO 178
Total PSC 1540(EU) Crystal Polystyrene 1540 is an easy flowing crystal polystyrene designed for extrusion or injection applications. In extrusion, it improves extruder output and thermoforming cycle times when mixed with a high impact p..
Flexural Modulus	2.90 GPa	421 ksi	ASTM D790
A. Schulman POLYFORT™ FPP 1285U Glass Filled, UV Stable Impact Copolymer Polypropylene DescriptionPolyfort® FPP 1285U is a 20% glass filled UV stable impact copolymer polypropylene product. Information provided by A. Schulman.
Flexural Modulus	2.90 GPa	420 ksi	ASTM D790
Chesterton ARC 5 Paste grade Rapid Cure Abrasion Control Description: ARC 5 is an advanced composite formulated for emergency repair and patching of metal components subject to light abrasive and corrosive conditions. It can be used to seal leaks and patc..
Flexural Modulus	2.90 GPa	420 ksi	ASTM D790
Ensinger Delrin® 150 Homopolymer Acetal (POM) Ensinger's Delrin® 150 stock shapes are a homopolymer acetal manufactured using DuPont Delrin 150 Resin. It is a crystalline plastic which offers an excellent balance of properties to bridge the g..
Flexural Modulus	2.90 GPa	421 ksi	ISO 178
DuPont Performance Polymers Delrin® 500CL NC010 Acetal (POM) (Unverified Data**) Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction Delrin 500CL is a medium viscosity acetal homopolymer resin containing a chemical lubricant designed for low wear and fr..
Flexural Modulus	2.90 GPa	421 ksi	2 mm/min; ISO 178
Eurostar Staramide RX06027 PA66, 30% Glass Filled, Injection Molded Staramide RX06027 is a 30% Glass Fiber Reinforced Polyamide 66 Injection Molding Resin (also known as Staramide 66 30K S34/8)Information provided by Eurostar.
Flexural Modulus	2.90 GPa	420 ksi	ASTM D790
Clariant Renol PA101L Nylon 66, General Purpose, Lubricated Data provided by Clariant Masterbatches
Flexural Modulus	2.90 GPa	420 ksi	ASTM D790
Clariant Renol PA101LRD-190 Nylon 66, General Purpose, Lubricated Data provided by Clariant Masterbatches
Flexural Modulus	2.90 GPa	421 ksi	ASTM Test
BASF Ultramid® 1003-2 NF2002 PA66 (Dry) Ultramid 1003-2 NF2002 is a general purpose, heat stabilized nylon 6/6.
Flexural Modulus	2.90 GPa	421 ksi	ASTM D790
A. Schulman ComAlloy Comtuf® 524 Polycarbonate/Styrenic Alloy Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc..
Flexural Modulus	2.90 - 19.3 GPa	420 - 2800 ksi	Average value: 8.67 GPa Grade Count:46
Overview of materials for Nylon 46, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum values ..
Flexural Modulus	2.90 GPa	421 ksi	ASTM Data
BASF Capron® 8332G Impact Modified, 25% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron 8332G is a 25% glass reinforced, impact modified polyamide 6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance of ..
Flexural Modulus	2.90 GPa	421 ksi	ISO 178-93
Wellman Wellamid® 22L-NBK1/WE-1434 Nylon 66, Engineering Grade All information provided by Wellman Engineered Resins.
Flexural Modulus	2.90 GPa	420 ksi	ASTM D790
Quantum Acetal-Homopolymer Information provided by Quantum Advanced Engineering Plastics
Flexural Modulus	2.90 GPa	420 ksi	ASTM D790
Techmer ES Electrablend® PC SS15 15% Stainless Steel Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Stainless Steel Fiber, 15% Filler by WeightFeatures: Electromagnetic Shielding (EMI)Information provided by TP Composites, Inc.