Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | >= 8.27 MPa | >= 1200 psi | |
Parker Chomerics CHO-BOND 584-29 Conductive Adhesive Two-component, highly conductive adhesive system that combines the good adhesive characteristics of epoxy with the superior conductivity of silver. In addition to being available in bulk form, the m.. |
|||
Shear Strength | >= 8.27 MPa | >= 1200 psi | Lap; ASTM D1022 |
Parker Chomerics CHO-BOND® 584-29 SYRINGE-PAK™ Silver Filled Conductive Epoxy and Hardener Description: Chomerics CHO-BOND 584-29 is a two-component, highly conductive adhesive system that combines the strong adhesive characteristics of epoxy with the superior conductivity of pure silver... |
|||
Shear Strength | >= 8.27 MPa | >= 1200 psi | Al/Al, bond |
Master Bond EP21SC-1 Two Component Epoxy Resin System Product Description: Master Bond Polymer System EP21SC-1 is a two component epoxy system featuring abrasion resistance. This high performance compound utilizes silicon carbide as a filler material a.. |
|||
Shear Strength | >= 8.27 MPa @Temperature 23.9 °C |
>= 1200 psi @Temperature 75.0 °F |
Al/Al, Tensile lap |
Master Bond EP21TDC-2ND Two component, highly flexibilized, non-drip epoxy resin compound Product Description: Master Bond EP21TDC-2ND is a two component highly flexible epoxy resin system for high performance bonding, sealing and coating with a non-drip consistency. It has a forgiving o.. |
|||
Shear Strength | >= 8.27 MPa | >= 1200 psi | Tensile, Al to Al |
Master Bond EP30AOHT Dimensionally Stable, Two Component Epoxy Description: Master Bond Polymer System EP30AOHT is a two component epoxy resin system for high performance bonding, potting, sealing and coating, formulated to cure at room temperature or more rapi.. |
|||
Shear Strength | >= 8.27 MPa | >= 1200 psi | Bond, After 30 days water immersion, Al to Al |
Master Bond EP76M-1R Nickel Conductive Epoxy Adhesive Description: Master Bond Polymer System EP76M-1R is a two component, nickel filled, electrically conductive adhesive for high performance bonding formulated to cure at room temperature or more rapid.. |
|||
Shear Strength | >= 8.27 MPa | >= 1200 psi | Tensile lap, Al to Al |
Master Bond EP42HT-2AO-1 Two Part, Cryogenically Serviceable Epoxy Description: Master Bond EP42HT-2AO-1 Black is a room temperature curable, two component epoxy adhesive, sealant, coating and casting material that meets NASA low outgassing specifications. It featu.. |
|||
Shear Strength | >= 8.27 MPa | >= 1200 psi | Tensile, aluminum |
Master Bond Supreme 10HTFS Silver Conductive Microelectronic Epoxy Description: Master Bond Polymer System Supreme 10HTFS “snap cure” epoxy is a formulated system featuring a combination of high performance properties including high shear and peel strength, outst.. |
|||
Shear Strength | 8.27 MPa | 1200 psi | Long Beam Shear, W Direction |
Hexcel® HexWeb® HDC-G-327 - 3/16 - 15.0 (R2) Heavy Density Core Designation: Material-Cell Size (inches)-DensityHexWeb® HDC is a fabric reinforced honeycomb, typically made from either fiberglass or carbon prepreg. A thermosetting node adhesive is used with eit.. |
|||
Shear Strength | 8.27 MPa | 1200 psi | Overlap, Etched Aluminum, 3 days, 71°C, 100% RH |
3M Scotch-Weld™ DP110 Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M |
|||
Shear Strength | 8.27 MPa | 1200 psi | Overlap, DCT 5002X Top Coat CRS/HDPE (non-abraded CRS), Top Coat Failure |
3M Scotch-Weld™ DP8010 Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8010 is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of Polypropyl.. |
|||
Shear Strength | 8.27 MPa | 1200 psi | Overlap, 304 Stainless Steel (1/32" thick), Adhesive Failure |
3M Scotch-Weld™ DP8010NS Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8010NS is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of Polyprop.. |
|||
Shear Strength | 8.27 MPa | 1200 psi | Overlap, Acrylic |
3M Scotch-Weld™ DP805 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP805 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability .. |
|||
Shear Strength | 8.27 MPa @Temperature -55.0 °C |
1200 psi @Temperature -67.0 °F |
Overlap |
3M Scotch-Weld™ DP810 Black Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 8.27 MPa @Temperature -55.0 °C |
1200 psi @Temperature -67.0 °F |
Overlap |
3M Scotch-Weld™ DP810NS Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 8.27 MPa | 1200 psi | Overlap, Acrylic, Substrate Failure |
3M Scotch-Weld™ DP8405NS Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP8405NS is a high performance, two-part acrylic adhesives that offer excellent shear, peel and impact performance. These toughened adhesives provide improved adh.. |
|||
Shear Strength | 8.27 MPa | 1200 psi | ASTM D1002-94 |
Aremco Aremco-Bond™ 820 High Performance Epoxide Clear, 1:1, 45-Minute Cure System with Good Flexibility |
|||
Shear Strength | 8.27 MPa @Temperature 66.0 °C |
1200 psi @Temperature 151 °F |
Overlap, Plywood, Substrate Failure |
3M Scotch-Weld™ Thin Instant Wood Adhesives and Surface Activator 3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in t.. |
|||
Shear Strength | 8.27 MPa @Temperature -55.0 °C |
1200 psi @Temperature -67.0 °F |
Overlap |
3M Scotch-Weld™ DP810 Tan Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 8.27 MPa | 1200 psi | Overlap, Galvanized Steel |
3M Scotch-Weld™ DP820 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP820 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability .. |
|||
Shear Strength | 8.27 MPa | 1200 psi | Overlap, Fir Wood |
3M Scotch-Weld™ DP820 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP820 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability .. |
|||
Shear Strength | 8.27 MPa @Temperature 82.0 °C, Time 900 sec |
1200 psi @Temperature 180 °F, Time 0.250 hour |
Aluminum, etched, Overlap, Adhesive Failure |
3M Scotch-Weld™ LSB60 Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60 is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of f.. |
|||
Shear Strength | 8.27 MPa @Temperature 120 °C |
1200 psi @Temperature 248 °F |
Overlap; ASTM D1002 |
3M Scotch-Weld™ 2290 Epoxy Adhesive/Coating 3M™ Scotch-Weld™ Epoxy Adhesive/Coating 2290 is an amber tinted thermo-setting adhesive/coating for metal to metal bonding and coating. It can be used to assemble laminated steel cores for electri.. |
|||
Shear Strength | 8.27 MPa | 1200 psi | Overlap, Etched Aluminum, 3 days, 71°C, 100% RH |
3M Scotch-Weld™ DP110 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M |
|||
Shear Strength | 8.27 MPa | 1200 psi | Overlap, Fiberglass |
3M Scotch-Weld™ DP125 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP125 Translucent is a faster curing version of 3M Scotch-Weld Epoxy Adhesive 2216 Translucent B/A. The worklife and cure time has been reduced from hours and days .. |
|||
Shear Strength | 8.27 MPa @Temperature 21.0 °C |
1200 psi @Temperature 69.8 °F |
Overlap |
3M Scotch-Weld™ DP190 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP190 Translucent is a 1:1 mix ratio similar to Scotch-Weld™ Epoxy Adhesive 2216 B/A Translucent but faster curing.Information provided by 3M |
|||
Shear Strength | >= 8.27 MPa | >= 1200 psi | Tensile, Al to Al |
Master Bond Supreme 3AN One Component, Heat Curing Epoxy Adhesive Description: Master Bond Polymer System SUPREME 3AN is a one component, heat cured epoxy adhesive and sealant, featuring high peel and shear strength along with excellent thermal conductivity and co.. |
|||
Shear Strength | >= 8.27 MPa | >= 1200 psi | Tensile, Al to Al |
Master Bond Supreme 3ANHT Epoxy Adhesives for Bonding Stainless Steel Description: Master Bond Polymer System Supreme 3ANHT is a one component, heat cured epoxy adhesive and sealant, featuring high peel and shear strength along with good thermal conductivity and conve.. |