Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 550 MPa @Temperature 200 °C |
79800 psi @Temperature 392 °F |
EN min.; EN 10002-5 |
Outokumpu 2205 Duplex Stainless Steel Duplex stainless combining high mechanical strength with good corrosion resistance.Applications: Pulp and paper industryDesalination plantsFlue-gas cleaningCargo tanks and pipe systems in chemical t.. |
|||
Tensile Strength, Ultimate | >= 550 MPa | >= 79800 psi | |
Kobe Steel KS85 Commercially Pure Titanium, ASTM Gr. 4, Annealed Nominal Composition: Ti-Fe-OApplications: Airplane Parts.Features: Relatively high strength, excellent corrosion resistance.Information provided by Kobe Steel |
|||
Tensile Strength, Ultimate | >= 550 MPa | >= 79800 psi | |
MetalTek MTEK 50-50Nb Cast UNS R20501 Heat Resistant Stainless Steel Information provided by MetalTek |
|||
Tensile Strength, Ultimate | >= 550 MPa | >= 79800 psi | |
MetalTek MTEK CX-2MW Cast UNS N26022 Severe Corrosion and Heat Resistant Alloy Information provided by MetalTek |
|||
Tensile Strength, Ultimate | >= 550 MPa | >= 79800 psi | |
MetalTek MTEK N155 UNS R30155 Severe Corrosion and Heat Resistant Alloy Information provided by MetalTek |
|||
Tensile Strength, Ultimate | >= 550 MPa | >= 79800 psi | |
MetalTek MTEK 6XN Cast UNS J94651 Super Austenitic Stainless Steel Corrosion resistance approaching nickel alloys, especially in chloride service.Applications: Process piping exposed to flue gas and solutions.Information provided by MetalTek |
|||
Tensile Strength, Ultimate | 550 MPa | 79800 psi | Annealed |
Special Metals MONEL® Alloy R-405 The free-machining version of MONEL alloy 400. A controlled amount of sulfur is added to the alloy to provide sulfide inclusions that act as chip breakers during machining. Other characteristics a.. |
|||
Tensile Strength, Ultimate | >= 550 MPa | >= 79800 psi | |
SSAB Tunnplat Domex® 490XP Extra High-strength Cold-forming Steel Extra High-strength Cold-forming Steel, HSLACharacteristics: Domex® is the brand name of hot rolled products from SSAB Tunnplat. Domex® cold-forming steels are modern structural steels. Gene.. |
|||
Tensile Strength, Ultimate | 550 MPa | 79800 psi | |
Wieland 1605 Wilaform Gold Red gold for all kinds of decoration manufacturing.Applications: casting, laminar decoration, pipes, tubingDental |
|||
Tensile Strength, Ultimate | 550 - 610 MPa | 79800 - 88500 psi | Wire |
CLAL-MSX ARCAP Anticorrosion AP1 H13 3/4 hard, Drawn Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
Tensile Strength, Ultimate | 550 - 600 MPa | 79800 - 87000 psi | Rod |
CLAL-MSX ARCAP Anticorrosion AP1C H13 3/4 hard, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
Tensile Strength, Ultimate | 550 - 600 MPa | 79800 - 87000 psi | Rod |
CLAL-MSX ARCAP Anticorrosion AP1 H14 4/4 hard, Drawn Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
Tensile Strength, Ultimate | 550 - 650 MPa | 79800 - 94300 psi | Wire |
CLAL-MSX ARCAP Anticorrosion AP1C H11 1/4 hard, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
Tensile Strength, Ultimate | 550 - 650 MPa | 79800 - 94300 psi | |
CLAL-MSX ARCAP Anticorrosion AP1D H14 4/4 hard, Drawn Copper Alloy, Wire and rod, 5 High Corrosion Resistance: ARCAP alloys are very corrosion resistant to the majority of chemical and physical environments. CLAL can provide data for the corrosion resistance of ARCAP alloys. In par.. |
|||
Tensile Strength, Ultimate | 550 - 600 MPa | 79800 - 87000 psi | Rod |
CLAL-MSX ARCAP Anticorrosion AP4 H12 1/2 hard, Drawn Copper Alloy Description: The AP4 grade is less easy to turn than the other grades of ARCAP. It can however be machined without more difficulty than the nickel chromium molybdenum steels.High Corrosion Resistanc.. |
|||
Tensile Strength, Ultimate | 550 - 650 MPa | 79800 - 94300 psi | |
CLAL-MSX ARCAP Anticorrosion AP4 H12 1/2 hard, Rolled Copper Alloy Description: The AP4 grade is less easy to turn than the other grades of ARCAP. It can however be machined without more difficulty than the nickel chromium molybdenum steels.High Corrosion Resistanc.. |
|||
Tensile Strength, Ultimate | 550 MPa | 79800 psi | |
Ametek P434L P/M Stainless Steel, Sintered from 7.0 g/cc Green Density >Powder apparent bulk density 2.8 g/cc; powder flow 30 sec/50g.Compacting properties measured on powders with 1% lithium stearite. Sintering was done in dissociated ammonia at 1121°C (2050°F) for.. |
|||
Tensile Strength, Ultimate | 550 - 650 MPa | 79800 - 94300 psi | |
ArcelorMittal HSLA 460 High strength low alloy steel for cold forming, Hot Rolled Available in the following: S460MCDescription: Steels in the HSLA (High Strength Low Alloy) range are hardened by a combination of precipitation and grain size refining, resulting in high strength w.. |