Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | ASTM D638-61T |
Rotuba 856, Slow Burning Ethyl Cellulose Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | 4.0 mm thick, 10.0 mm wide molded rod; ISO 527 |
Premix Thermoplastics PRE-ELEC® ESD 7100 PRE-ELEC ESD 7100 is a static dissipative thermoplastic compound based on ABS. The dissipative property is permanent and built into the polymer chain. PRE-ELEC ESD 7100 has been developed for inject.. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | ASTM D638 |
North Wood Plastics Polypropylene with 40% Wood Fiber, Extrusion Grade Data provided by North Wood Plastics, Inc. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | ASTM D638 |
Rotuba MSS Cellulose Acetate Property values at 50% RH.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | ASTM D638 |
NCMT NanoPAC™ HG602 High Performance Polypropylene Nanocomposite Applications: Household Industry Electrical AppliancesInformation provided by Nano Composite Materials Technology Limited |
|||
Tensile Strength, Ultimate | 27.0 MPa @Temperature 90.0 °C |
3920 psi @Temperature 194 °F |
ISO 527 |
LATI LATAN 13 Medium Viscosity Polyoxymethylene Copolymer (POM)
(Unverified Data**) Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea.. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | ASTM D638 |
Solvay Specialty Polymers Algoflon® 15GL+3Mos PTFE; Glass Fiber/Molybdenum Disulphide Filled
(discontinued ** Data provided by the manufacturer.15 wt.% Glass Fiber + 3 wt.% MoS2. Suspension polymer powder grade recommended for compression molding. Pure PTFE possesses high inertness, excellent dielectric pro.. |
|||
Tensile Strength, Ultimate | 27.0 - 33.0 MPa | 3920 - 4790 psi | Average value: 29.0 MPa Grade Count:3 |
Overview of materials for Nylon 612, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Impact Modified". Each property range of values reported is minimum and maximum values of app.. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | |
Freudenberg Simrit Superiorâ„¢ F850 Fluoroelastomer Cost-effective, high performance compound for semiconductor applications. Superior F850 offers outstanding plasma resistance and low particulation in a wide range of plasma environments. |
|||
Tensile Strength, Ultimate | 27.0 MPa @Temperature 22.0 °C |
3920 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® BMC 0410 Unsaturated Polyester UP BMC 0410 is a low profile BMC with zero shrinkage and low coefficient of thermal expansion. It is especially suited for precision mouldings in office and communication equipment. The combination of .. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | |
Ineos Styrenics Avantra® 597N Polystyrene (NAFTA) High-impact grade of polystyrene with improved impact strength and heat resistance, developed for injection molding and extrusion/thermoforming applications.Information provided by BASF.Ineos Styren.. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | ASTM D638 |
LyondellBasell Hifaxâ„¢ ETA-3131EUV Thermoplastic Olefin Resin Key Features: fractional melt flow, medium modulus, UV-stabilized, extrusion grade thermoplastic olefin resin, excellent impact and stiffness balance, good practical impact, good processability, exc.. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1377 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1377 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | ISO 527-1, 2 |
Polyplastics Duracon® TD-35 Acetal Co-polymer (POM), High impact, Flexible DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1377 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1377 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | DIN 53504 |
Lubrizol ESTANE® 58565 Ester Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | ISO 527-1 |
Chengdu Polyster H4543 Thermoplastic Polyether-ester Elastomer (TPEE) Low modulus molding and injection grade. Contains improved color- stable antioxidants. Applications requiring high original color retention. Molded and injected products for consumer use, such as se.. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | ISO 527 |
Eastman Eastar GN071 Natural PETG Copolyester EASTAR GN071 Copolyester is used for injection molding applications. It is sparkling clear, tough, chemical resistant, odor free, versatile, easy to work with and affordable. Cleaning solutions wi.. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | ASTM D638 |
A. Schulman ComAlloy Voloy® 100 Polypropylene, Mineral Reinforced, Flame Retardant, UL, CSA Data provided by the manufacturer, ComAlloy International Company.15% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 27.0 - 35.0 MPa | 3920 - 5080 psi | ISO 527 |
BASF Ecovio® C2224 F Blend Biodegradable Polyester Description: Ecovio® F Blend C2224 is our biodegradable film product containing renewable resources. It is basically a compound of our biodegradable copolyester Ecoflex® F Blend and polylactic aci.. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | ASTM D638 |
Toyobo E3070A Thermoplastic Polyurethane Elastomer, Extrusion Grade Polyether type, featuring excellent resistance to hot water and fungus. Various grades of Toyobo polyurethane TPEs are used in auto parts, hoses, tubes, sporting goods, shoe soles, etc.Information .. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1107 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | at max load; ASTM D638 |
A. Schulman POLYPUR™ FPU 1377 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 27.0 - 63.0 MPa | 3920 - 9140 psi | Average value: 39.5 MPa Grade Count:20 |
Overview of materials for Acetal Copolymer, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Impact Modified". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Ultimate | 27.0 MPa | 3920 psi | ASTM D412 |
KKPC KOSYN KTR 601 Thermoplastic Elastomer (TPE) Thermoplastic Elastomer (TPE)Characteristics: KOSYN KTR101 is linear block copolymer made by solution polymerization which polymerizes butadiene and styrene in organic solvent. It is thermoplastics .. |